A kind of screen printing protective ink composition and screen printing method

A technology for protecting inks and compositions, applied in the direction of inks, printing, printing devices, etc., can solve the problem of unstable size in the sandblasting step and achieve good corrosion resistance

Active Publication Date: 2016-08-17
LENS TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But this method still has the problem of dimensional instability in the blasting step

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of screen printing protective ink composition and screen printing method
  • A kind of screen printing protective ink composition and screen printing method
  • A kind of screen printing protective ink composition and screen printing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] First, prepare the screen printing protection ink composition in the present invention: first prepare the acid-resistant ink and the amine curing agent in proportion and stir evenly, then add superfine Stir the rubber powder and diluent (ketone solvent) evenly; the weight ratio is ink:curing agent:diluent:rubber powder=100:1:8:10. Among them, the acid-resistant ink is the acid-resistant ink of the model IP-505-03 produced by Matsui Chemical, the ultra-fine rubber powder is the ultra-fine rubber powder produced by Mingjintai Rubber and Plastic Products Company, and the curing agent is the model DA-043 produced by Matsui Chemical The amine solidifying agent, the diluent is the ketone-containing solvent of the model KJ001 that Matsui Chemical produces.

[0028] Preparation: Prepare the screen version (screen version of about 120T mesh), screen printing machine and such as figure 1 The shapes and dimensions shown in are all processed white glass.

[0029] Silk screen prin...

Embodiment 2

[0033] The weight ratio of the screen printing protective ink composition in this embodiment is ink:curing agent:diluent:rubber powder=100:0.8:8:8, and the rest of the conditions are the same as in Example 1. The obtained screen printing protective ink composition can play an ideal protective effect when used for screen printing.

Embodiment 3

[0035] The weight ratio of the screen printing protective ink composition in this embodiment is ink:curing agent:diluent:rubber powder=100:1.2:10:15, and the rest of the conditions are the same as in Example 1. The obtained screen printing protective ink composition can play an ideal protective effect when used for screen printing.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a screen printing protective ink composition. The ink composition comprises acid-resistant ink and ultrafine rubber powder, wherein the average particle diameter of the ultrafine rubber powder is less than or equal to 0.04mm and the mass of the ultrafine rubber powder accounts for 5-20% of mass of the acid-resistant ink. The invention also correspondingly provides a screen printing method. According to the technical scheme, a product of which a specific position on the surface of glass has a frosting effect is produced, the blocking of a fixture is not needed in the blasting process, the ink at a non-frosting region can resist blast and strike and meanwhile, after the etching process is completed and the plating layer is removed, the condition of poor appearance caused by corrosion on the surface of glass at the non-frosting region is caused.

Description

technical field [0001] The invention relates to a screen printing protection ink composition and a screen printing method. Background technique [0002] The frosting effect on the glass surface is popular in the market because of its fog and hand feeling. More and more industries are developing sandblasting and etching processes for preparing the frosting effect on the glass surface. To obtain the effect of frosting on the glass surface, in this field, the frosting area on the glass surface is generally determined first, and then the non-frosting area on the glass surface is covered with silk screen printing ink by accurately positioned silk screen; and then the entire surface of the glass surface is covered. Sandblasting and etching, the area covered with screen printing protection ink will not be affected by the impact and corrosion of sandblasting and etching steps; after that, the covered screen printing protection ink is deplated and cleaned, thus obtaining a frosting e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/02C09D11/03B41M1/12
CPCB41M1/12C09D11/02C09D11/03
Inventor 周群飞饶桥兵段毅
Owner LENS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap