Computer-to-plate flexible plate and production method thereof

A technology of computer and flexographic plate, which is applied in the field of flexible photosensitive resin plate and its preparation, can solve the problems of slow ablation speed, shorten plate making time, troublesome ablation residue treatment, etc., and achieve good adhesion effect

Active Publication Date: 2015-06-24
LUCKY HUAGUANG GRAPHICS
View PDF16 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The advantage of this kind of plate is that it does not need to be dried and rinsed, which saves a lot of cost; because it does not need to dry the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Computer-to-plate flexible plate and production method thereof
  • Computer-to-plate flexible plate and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The support (1) can be selected from polyhexylene naphthalene-2,6-dicarbonate, polyethylene terephthalate, polybutylene terephthalate, etc., with a thickness of 50-300 μm. In this embodiment, polyethylene terephthalate is used as a support body with a thickness of 100 μm, produced by Lucky Company.

[0036] Preparation of the photosensitive elastomer layer (2): 700 g of thermoplastic elastomer SIS1107 (Kraton Company), 200 g of plasticizer polybutadiene NissoPB-P2000 (NipponSoda, Japan), 1-hydroxycyclohexyl phenyl ketone (Zhangjiagang) Free Trade Zone Tianjie International Trade Co., Ltd.) 32g, 2,6-ditert-butyl-p-cresol (Nanjing Jiulong Chemical Co., Ltd.) 12g, trimethylolpropane triacrylate 40g (Tianjin Tianjiao Chemical Co., Ltd.), 1,9 - 15.8g of nonanediol diacrylate (Tianjin Tianjiao Chemical Co., Ltd.), 0.2g of dye RED335 (BASF company), 0.2g of styrylbenzimidazole dye, join in the twin-screw extruder, and mix at 150°C for 2 minutes, extrude a photosensitive elast...

Embodiment 2

[0043] The support (1) can be selected from polyhexylene naphthalene-2,6-dicarbonate, polyethylene terephthalate, polybutylene terephthalate, etc., with a thickness of 50-300 μm. In this embodiment, polyethylene terephthalate is used as a support body with a thickness of 125 μm, produced by Lucky Company.

[0044] Preparation of the photosensitive elastomer layer (2): 700 g of thermoplastic elastomer SISD1160ES (Kraton Company), 200 g of plasticizer polybutadiene NissoPB-P2000 (NipponSoda, Japan), 1-hydroxycyclohexyl phenyl ketone (Zhangjiagang) Free Trade Zone Tianjie International Trade Co., Ltd.) 32g, 2,6-ditert-butyl-p-cresol (Nanjing Jiulong Chemical Co., Ltd.) 12g, trimethylolpropane triacrylate 40g (Tianjin Tianjiao Chemical Co., Ltd.), 1,9 - 15.8g of nonanediol diacrylate (Tianjin Tianjiao Chemical Co., Ltd.), 0.2g of dye RED335 (BASF Company), 0.2g of pyridinium cyanine dye, added to the twin-screw extruder, mixed for 2 minutes at 140°C, and extruded A photosensitive...

Embodiment 3

[0049] The selection of the support (1) is the same as in Example 2.

[0050] Preparation of the photosensitive elastomer layer (2): 750 g of thermoplastic elastomer SIS1107 (Kraton Company), 150 g of plasticizer polybutadiene NissoPB-P2000 (NipponSoda, Japan), 1-hydroxycyclohexyl phenyl ketone (Zhangjiagang) Free Trade Zone Tianjie International Trade Co., Ltd.) 32g, 2,6-ditert-butyl-p-cresol (Nanjing Jiulong Chemical Co., Ltd.) 12g, trimethylolpropane triacrylate 30g (Tianjin Tianjiao Chemical Co., Ltd.), 1,9 - 25.8g of nonanediol diacrylate (Tianjin Tianjiao Chemical Co., Ltd.), 0.2g of dye RED335 (BASF Company), 0.2g of copper phthalocyanine, added to the twin-screw extruder, mixed for 2 minutes at 140°C, and extruded A photosensitive elastomer layer (2) with a thickness of 2.70mm, set aside.

[0051] The anti-adhesive layer (3) was prepared the same as in Example 1.

[0052] The protective film (4) is selected from the same embodiment 1.

[0053] The lower surface of t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Coating thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a computer-to-plate flexible plate and a production method thereof. The flexible plate comprises a supporting body, a photosensitive elastomer layer, an anti-adhering layer and a protection film, a plate material is directly scanned through a computer and then cleaned with water or a solution prior to being dried in hot wind to be made into a printing plate of the flexible plate, scanning of the computer is performed before stripping of the protecting film or after stripping of the protecting film, the photosensitive elastomer layer is highly sensitive to purple light and ultra violet and can be sufficiently cross-linked and solidified; the protecting film is a transparent thin film. Dynamic integration of rapid laser plate production and fine network reduction is realized, and adhesive strength of the photosensitive elastomer layer of the flexible plate is good.

Description

technical field [0001] The invention relates to a computer-to-plate flexible plate and a preparation method thereof, in particular to a computer-directly imageable flexible photosensitive resin plate and a preparation method thereof. Background technique [0002] At present, flexographic printing is widely used in the printing of cartons, flexible packaging, labels and other easily deformed or soft substrates. [0003] Usually, a film with patterns or characters is placed on an unexposed flexographic plate, exposed to ultraviolet light, and the transparent part of the film passes through ultraviolet light, and the photosensitive elastomer undergoes cross-linking and curing. The area that does not pass through the ultraviolet rays cannot undergo cross-linking reaction, and the difference in solubility in the developer is used to develop a relief image containing text patterns. The developed plate is dried, debonded, and post-exposed. The prepared plate is fixed on the cylin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B41N1/12B41C1/00G03F7/20
CPCG03F7/11G03F7/202
Inventor 王国才高英新张刚李志勇高峰赵军权
Owner LUCKY HUAGUANG GRAPHICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap