Anti-sagging and anti-crystallizing wind power hand lay-up resin system and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
An anti-crystallization and anti-sag technology, used in the chemical and composite fields to achieve excellent heat resistance of cured products, eliminate sagging or dripping, and enhance tolerance.
Active Publication Date: 2015-06-24
上海康达新材料科技有限公司
View PDF5 Cites 11 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0006] One of the technical problems to be solved by the present invention is to provide an anti-sag and anti-crystallization wind power grade hand lay-up resin system to overcome the contradiction between anti-sag viscosity and fiber wetting ability, low-temperature
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0051] Epoxy resin component A raw material parts by weight:
[0052]
[0053]
[0054] Synthetic alicyclic amine raw material parts by weight:
[0055]
[0056] Curing agent component B raw material parts by weight:
[0057]
[0058] Preparation:
[0059] Preparation of epoxy resin component A:
[0060] According to the weight percentage of raw materials, add bisphenol A epoxy resin, heat-resistant novolac epoxy resin, flexible epoxy resin, and reactive diluent into the reactor in advance, raise the temperature to 60°C-70°C, and stir and mix at a constant temperature 2-4h; then cool down to below 40°C, add the non-reactive diluent into the reactor, and continue to stir and mix for 2-4h; then turn off the stirring to prepare epoxy resin component A, and store it in a sealable container at room temperature.
[0061] The preparation of synthetic cycloaliphatic amine:
[0062] According to the weight percentage of raw materials, add isophoronediamine, N-aminoethyl...
Embodiment 2
[0069] Epoxy resin component A raw material parts by weight:
[0070]
[0071] Synthetic alicyclic amine raw material parts by weight:
[0072]
[0073] Curing agent component B raw material parts by weight:
[0074]
[0075] The mixing weight ratio of epoxy resin component A and curing agent component B is 100:34.
Embodiment 3
[0077] Epoxy resin component A raw material parts by weight:
[0078]
[0079] Synthetic alicyclic amine raw material parts by weight:
[0080]
[0081] Curing agent component B raw material parts by weight:
[0082]
[0083] The mixing weight ratio of epoxy resin component A and curing agent component B is 100:36.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses an anti-sagging and anti-crystallizing wind power hand lay-up resin system and a preparation method thereof. The hand lay-up resin system is a mixture of a compounded epoxy resin component A and a denatured curing agent component B, wherein the compounded epoxy resin component A is prepared from epoxy resin, heat-resisting novolac epoxy resin, flexible epoxy resin, active diluent and a non-activated diluent; the denatured curing agent component B is prepared from synthetic alicyclic amine, acylamino amine, aliphatic amine, cashew nut shell oil modified phenolic aldehyde amine, an accelerant, a rheological agent and a dye. The anti-sagging and the anti-crystallizing properties are obviously enhanced, the fiber wettability for fibers is excellent, the influence from the working environment is low, the comprehensive performances such as the mechanical property, the toughness, the heat resistance and the water resistance of the curing product are excellent, the practical requirement of various compound materials for hand lay-up manufacture and repair can be met, and particularly the product is suitable for being used in the large-area high-strength compound materials such as a wind power blade.
Description
technical field [0001] The invention relates to the technical fields of chemical engineering and composite materials, in particular to a hand-lay-up resin system for composite material molding and repairing and a preparation method thereof, in particular to an anti-sag and anti-crystallization wind power-grade hand-lay-up resin system and a preparation method thereof . Background technique [0002] The hand lay-up process is one of the mainstream traditional methods for manufacturing composite materials. The principle of the process is to use the hand lay-up resin system to impregnate the fiber braiding layer, then lay the layers and press them together. After the impregnated resin system is cured, a composite is formed. Material matrix. Although it seems that the hand lay-up process is prone to process hidden dangers and quality problems, it is still widely used. Even in the preparation of large-scale advanced composite materials such as MW-level wind power blades, this pr...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.