Neutron shielding material with flame-retardant and heat-insulating properties and preparation method thereof

A shielding material and neutron technology, which are applied in the field of neutron shielding materials and their preparation, can solve the problems of weak neutron shielding ability, poor flexibility, and no flame retardancy, and achieve good thermal neutron shielding performance and high thermal stability. effect of sub-absorption cross section, high mechanical strength

Active Publication Date: 2017-07-11
NANJING UNIV OF AERONAUTICS & ASTRONAUTICS
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The traditional neutron radiation protective clothing uses multi-layer neutron protective fiber cloth as the main material, which is heavy, poor in flexibility, weak in neutron shielding ability, and does not have flame retardancy and heat insulation performance. Fire protection requirements; traditional hard polymer shielding materials cannot change randomly with the size of the environment and the shape of the equipment, and do not have flame retardant performance, which brings certain difficulties and risks to the protection of nuclear equipment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The formula of the neutron shielding material with flame-retardant and heat-insulating properties is: 100g of methyl vinyl silica gel with a hardness of 5HA, B 4 C powder 90g, SiO 2 8.2g of hollow microspheres, 48g of zinc borate powder, 0.5g of bis-pentasulfurizing agent, and 1g of KH-540 coupling agent. where B 4 C powder particle size 50um, SiO 2 The particle size of hollow microbeads is 25um, and the particle size of zinc borate powder is 2.5um.

[0021] The steps of the preparation method of the neutron shielding material with flame-retardant and heat-insulating properties are as follows:

[0022] (1) Plastic refining of methyl vinyl silica gel matrix material: adjust the distance between the double rollers of the open mill to 2mm, and the rotation speed to 45r / min. Put it into the double roller room for masticating, and the masticating time is 3 minutes. Add 1g of vulcanizing agent Shuang25 to the above-mentioned methyl vinyl silica gel and continue masticati...

Embodiment 2

[0032] The formula of the neutron shielding material with flame-retardant and heat-insulating properties is: 100g of methyl vinyl silica gel with a hardness of 5HA, B 4 C powder 53.5g, TiO 2 4.8g of hollow microspheres, 28.3g of zinc borate powder, 2g of bis-pentasulfurizing agent, and 3g of KH-550 coupling agent. where B 4 C powder particle size 50um, TiO 2 The particle size of hollow microbeads is 20um, and the particle size of zinc borate powder is 2.5um.

[0033] The steps of the preparation method of the neutron shielding material with flame-retardant and heat-insulating properties are as follows:

[0034] (1) Plastic refining of methyl vinyl silica gel matrix material: adjust the distance between the double rollers of the open mill to 2mm, and the speed of 45r / min. Carry out masticating between two rollers, the masticating time is 4 minutes. Add a certain amount of vulcanizing agent 225 to the methyl vinyl silica gel and continue masticating for 14 minutes, during w...

Embodiment 3

[0044] The formula of the neutron shielding material with flame-retardant and heat-insulating properties is: 100g of methyl vinyl silica gel with a hardness of 5HA, B 4 C powder 30g, Al 2 o 3 2.7g of hollow microspheres, 15.8g of zinc borate powder, 3g of bis-pentasulfurizing agent, and 5g of aminopropyltrimethoxysilane. where B 4 C powder particle size 50um, Al 2 o 3 The particle size of hollow microbeads is 30um, and the particle size of zinc borate powder is 2.5um.

[0045] The steps of the preparation method of the neutron shielding material with flame-retardant and heat-insulating properties are as follows:

[0046](1) Plastic refining of methyl vinyl silica gel matrix material: adjust the distance between the double rollers of the open mill to 2mm, and the speed of 45r / min. Carry out mastication between the double rollers, and the mastication time is 5 minutes. Add a certain amount of vulcanizing agent bis-2-5 into the methyl vinyl silica gel and continue masticat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
oxygen indexaaaaaaaaaa
oxygen indexaaaaaaaaaa
oxygen indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a neutron shielding material with flame-retardant and heat-insulating properties and a preparation method thereof. It is composed of Wuhe powder surface modifier; its preparation method is to add methyl vinyl silica gel and vulcanizing agent Shuangerwu into the open mill for mastication, and then mix it with neutron absorber material, flame retardant functional filler, heat insulation The mixture of functional fillers and powder surface modifiers is commonly added to the vacuum mixer for banburying, and finally the banburying product is added to the flat vulcanizer to obtain a neutron shielding material with flame-retardant and heat-insulating properties; the material has thermal Materials with neutron shielding performance have good flexibility, flame retardancy, heat insulation performance, and mechanical strength. They can not only meet the peripheral protection of nuclear instruments and equipment with complex shapes, but also are good core materials for neutron protective clothing.

Description

technical field [0001] The invention relates to a neutron shielding material with flame-retardant and heat-insulating properties and a preparation method thereof, belonging to the field of nuclear radiation protection and the technical field of preparation of nuclear radiation shielding materials. [0002] technical background [0003] As the application of nuclear technology plays an increasingly important role in energy conservation and environmental protection, resource exploration, radiation processing, medical diagnosis, and national defense and military affairs, the number of radioactive practitioners has also increased. But while bringing convenience and enjoyment to people, various rays also bring harm to human beings to some extent. Therefore, it is necessary to reduce the occupational exposure level of practitioners in various radioactive activities and ensure the life and health of radiation practitioners. extremely important. [0004] The traditional neutron radi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L83/07C08K13/06C08K9/06C08K7/24C08K7/26C08K7/28C08K3/22C08K3/16C08K3/38C08K3/02G21F1/10
Inventor 汤晓斌柴浩倪敏轩陈飞达陈达
Owner NANJING UNIV OF AERONAUTICS & ASTRONAUTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap