Negative oxygen ion carbon crystal and carbon fiber infrared heating wallpaper mural production method

A technology of negative oxygen ions and carbon fibers, applied in the field of negative oxygen ion carbon crystal and carbon fiber infrared heating and heating paper heating, can solve the problems of inconvenient use, uneven heating, large power consumption, etc., and achieves easy promotion and low cost. , the effect of low power consumption

Active Publication Date: 2017-09-29
深圳市长奇节能环保科技有限公司
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In terms of indoor heating, industrial and agricultural heating, medical heating, etc., as far as the heating methods of heating wallpaper and murals are concerned, there are no relatively mature products on the market at present. It is made of wallpaper and murals. Its shortcomings, defects and disadvantages are high cost, inconvenient use, large power consumption, uneven heat generation, and the heat transfer method is heat conduction and slow heat transfer.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Negative oxygen ion carbon crystal and carbon fiber infrared heating wallpaper mural production method
  • Negative oxygen ion carbon crystal and carbon fiber infrared heating wallpaper mural production method

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0034] The present invention will be described in detail below in conjunction with the accompanying drawings. As shown in the accompanying drawings:

[0035] A negative oxygen ion carbon crystal and carbon fiber infrared heating wallpaper mural, which is composed of a wallpaper layer 1, a heating carbon crystal layer 2, an insulating and heat insulating layer 3, a mural layer 4, and a wire 5;

[0036]The negative oxygen ion carbon crystal and the carbon fiber infrared heating wallpaper mural, the mural layer 4, the wallpaper layer 1, the heating carbon crystal layer 2, and the insulating and heat insulating layer 3 are all connected in sequence by bonding, and the heating carbon crystal layer 2 Both sides of each are electrically connected to the wire 5 respectively.

[0037] The negative oxygen ion carbon crystal and the carbon fiber infrared heating wallpaper mural, the wallpaper layer 1, the heating carbon crystal layer 2, the insulation and heat insulation layer 3, and th...

specific Embodiment approach 2

[0046] Carry out according to specific embodiment 1, just: a kind of negative oxygen ion carbon crystal and carbon fiber infrared heating wallpaper mural, be made of wallpaper layer 1, heating carbon crystal layer 2, insulation and heat insulation layer 3, mural layer 4, wire 5;

[0047] The negative oxygen ion carbon crystal and the carbon fiber infrared heating wallpaper mural, the mural layer 4, the wallpaper layer 1, the heating carbon crystal layer 2, and the insulating and heat insulating layer 3 are all connected in sequence by bonding, and the heating carbon crystal layer 2 Both sides of each are electrically connected to the wire 5 respectively.

[0048] The negative oxygen ion carbon crystal and the carbon fiber infrared heating wallpaper mural, the wallpaper layer 1, the heating carbon crystal layer 2, the insulation and heat insulation layer 3, and the mural layer 4 are all flake structures, and the wire 5 is a linear structure .

[0049] Received the expected goo...

specific Embodiment approach 3

[0050] Carry out by specific embodiment one, just: to described nano-carbon crystal powder with 1 weight part, carbon fiber chopped strand, with 1 weight part, graphene with 1 weight part, tourmaline with 1 weight part, flame retardant epoxy 20 parts by weight of resin, 1 part by weight of dicyandiamide, 50 parts by weight of acetone, and 5 parts by weight of nitrile rubber were implemented; the expected good effect was obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for making a negative oxygen ion carbon crystal and a carbon fiber infrared heating wallpaper mural, which relates to the technical field of heating paper (film) heating. With the key technology of "setting a heating carbon crystal layer", negative oxygen ion carbon crystals and carbon fiber infrared heating wallpaper murals are the mural layer, wallpaper layer, heating carbon crystal layer, and insulation layer. Electrical connection; the method is to combine 1-30 parts by weight of nano-carbon crystal powder, 1-15 parts by weight of carbon fiber chopped strands, 1-5 parts by weight of graphene, 1-20 parts by weight of tourmaline, and 20-40 parts by weight of flame retardant epoxy resin The heat-generating carbon crystal glue prepared in parts by weight, 1-2 parts by weight of dicyandiamide, 50-100 parts by weight of acetone, and 5-20 parts by weight of nitrile nitrile rubber is back-coated, baked, wired, and then covered with an insulating heat-shielding film. For indoor heating and decoration. The process is simple, the effect is good, the cost is low, and the promotion is favorable.

Description

technical field [0001] The method for making negative oxygen ion carbon crystals and carbon fiber infrared heating wallpaper murals of the present invention relates to the technical field of negative oxygen ion carbon crystals and carbon fiber infrared heating; in particular to the technical field of heating paper (film) heating; in particular to negative oxygen ion carbon crystals and carbon fiber infrared heating The technical field relates to a method for making heat-generating wallpaper murals. Background technique [0002] In terms of indoor heating, industrial and agricultural heating, medical heating, etc., as far as the heating methods of heating wallpaper and murals are concerned, there are no relatively mature products on the market at present. Made of wallpaper and murals, its shortcomings, defects and disadvantages are high cost, inconvenient use, large power consumption, uneven heat generation, and the heat transfer method is heat conduction and slow heat transf...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): F24D13/00H05B3/10B44C5/04
Inventor 郭长奇郭凯华
Owner 深圳市长奇节能环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap