Anti-hollowing paving process of vitrified tiles

A technology of vitrified tiles and paving, which is applied in covering/lining, construction, building construction, etc.
CN104947902AInactive Publication Date: 2015-09-30GOLD MANTIS FINE DECORATION TECH SUZHOU CO LTD
2 Cites 8 Cited by

Patent Information

Authority / Receiving Office
CN Β· China
Patent Type
Applications(China)
Current Assignee / Owner
GOLD MANTIS FINE DECORATION TECH SUZHOU CO LTD
Publication Date
2015-09-30
Estimated Expiration
Not applicable Β· inactive patent

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention discloses an anti-hollowing paving process of vitrified tiles. The process includes the steps of 1, treating the vitrified tiles, to be specific, cleaning the back of each vitrified tile, soaking the vitrified tiles to move dust and other impurities, brushing off industrial wax from the back of the vitrified tiles, and air-drying the vitrified tiles; 2, treating a base layer of a wall, to be specific, cleaning a bonding face of the wall with a cleaning tool before painting so as to keep the bonding face of the wall clean, spraying water to the wall for moisturizing, drying the surface of the wall in shade to make sure the surface has no evident water stain, and applying bonding agent to the bonding face of the wall with the thickness of the bonding agent ranging from 0.6 mm to 1.2 mm; 3, testing water absorption of the vitrified tiles, and selecting proper binder; 4, paving the vitrified tiles, to be specific, by means of double-side bonding, scrape-coating the base layer of the wall with a layer of binder, scrape-coating the back of each vitrified tile with a layer of binder, smearing the periphery of each vitrified tile into a beveled edge, and performing paving. By the use of the anti-hollowing paving process, the vitrified tiles and the base layer of the wall can be fully contacted and bonded, and hollowing or shedding rarely occurs.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to a brick paving process, in particular to a vitrified brick anti-aircraft drum paving process. Background technique

[0002] Traditionally, when laying vitrified tiles, due to the following reasons, it is very easy to cause hollowing or falling off: 1. The professionalism of the laying personnel is poor: the understanding of the laying site is low, and only the workload is required; 2. The glass The quality of the brick itself is poor, and the structure has disadvantages: the friction coefficient on the back of the vitrified brick is low and there are many impurities and dust on the back; 3. The environmental conditions for on-site paving are insufficient: the base is dry and the wetting is not enough; or the mortar loses water quickly, Decreased adhesion; or frost in winter, dry in summer, etc.; 4. Improper selection of paving tools; 5. There are problems in the paving method itself, causing hidden dangers. Contents of the in...

Claims