Preparation method of shock-absorbing foam

A technology of foam and substrate, applied in the field of preparation of shock-absorbing foam, can solve problems such as burning

Active Publication Date: 2017-10-13
EVA GLORY INDAL
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the above-mentioned method is used to prepare the shock-absorbing foam whose distance between the side of the protrusion 2 away from the base 1 and the base 1 is greater than 2mm, the surface of the protrusion 2 will be scorched.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of shock-absorbing foam
  • Preparation method of shock-absorbing foam
  • Preparation method of shock-absorbing foam

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] Prepare shock-absorbing foam

[0058] Step (1): Select the required ingredients and their contents according to Table 1, mix and stir the ingredients evenly to prepare a mixture.

[0059] Table 1

[0060]

[0061] Step (2): knead the mixture obtained in step (1) at 130° C. for 10 minutes, and then extrude to obtain an embryonic body (a thin sheet with a thickness ranging from 1 to 8 mm).

[0062] Step (3): The primary body obtained in step (2) is subjected to micro-processing such as pulverization, granulation or granulation to form a plurality of fragments or granules with a particle size ranging from 3 to 6 mm and a volume range of 27~196mm 3 embryo body.

[0063] Step (4): Put the embryo body obtained in step (3) into a mold and place it on a hot press table for molding and foaming (temperature is 170°C, pressure is 150kg / cm 2 ), after 12 minutes, a shock-absorbing foam was obtained.

[0064]

[0065] refer to figure 2 , the shock-absorbing foam prepared ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

A method for preparing a shock-absorbing foam, comprising the following steps: (1) preparing a mixture, the mixture including a base material component, a foaming agent, and a bridging agent, the base material component having a main base material and a secondary base (2) kneading and extruding the mixture to obtain a primordial body; (3) subjecting the primordial body to micro-processing to form a plurality of embryonic bodies with a particle size ranging from 1 to 20 mm; and ( 4) Forming and foaming the embryo body to prepare a shock-absorbing foam. When the method of the present invention is used to prepare the shock-absorbing foam comprising at least one protrusion with a protrusion length greater than 2 mm, the surface of the protrusion will not be scorched.

Description

technical field [0001] The invention relates to a preparation method of foam, in particular to a preparation method of shock-absorbing foam. Background technique [0002] Plastic products have become one of the indispensable products in modern people's life, especially the foam which is formed by plastic foam and has material properties such as light weight, wear resistance, insulation, impact resistance, etc., is very suitable as a shock-absorbing material, so It is often used in body protective equipment, sports equipment protective equipment or packaging materials for precision instruments and equipment. [0003] China Taiwan Patent Publication No. 200842154 discloses a method for preparing a shock-absorbing foam, which is to knead and extrude a mixture to form a primordial body, and then directly foam the primordial body to obtain a shock-absorbing foam. Wherein, the mixture includes a main substrate containing ethylene-vinyl acetate copolymer (ethylene-vinyl acetate co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B29C44/02B29K31/00
Inventor 李文生
Owner EVA GLORY INDAL