Preparation method of deodorizing fiberglass packaging box

A packaging box and fiberglass technology, applied in chemical instruments and methods, glass/slag layered products, lamination devices, etc., can solve problems such as single function and inability to meet people's multiple needs

Inactive Publication Date: 2017-02-01
佛山市高明区尚润盈科技有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the single function of the traditional deodorizing FRP packaging boxes can no longer meet the diverse needs of people.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of deodorizing fiberglass packaging box
  • Preparation method of deodorizing fiberglass packaging box
  • Preparation method of deodorizing fiberglass packaging box

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] A kind of preparation method of porous graphene silver-loaded antibacterial composite material, it comprises the following steps:

[0051] (1) Preparation of graphene quantum dot suspension: weigh 0.5g of C60 powder, measure 50ml of concentrated sulfuric acid with a mass fraction of 98%, mix C60 powder and concentrated sulfuric acid in a beaker, place the beaker in an ice-water bath, and simultaneously Stir at a speed of 500rpm to obtain a mixed solution; weigh 0.5g of potassium permanganate powder, and slowly add it to the above mixed solution; remove the ice-water bath and replace it with a water bath, keep the temperature of the water bath at 30~40°C, and react for 8 hours; quickly add 200ml Pure water, filtered, and then dialyzed for 3 days with a dialysis bag with a molecular weight cut-off of 1000, to obtain a suspension of graphene quantum dots; the suspension of graphene quantum dots was stirred at a speed of 100 rpm, while laser irradiation was performed for 30 ...

Embodiment 2

[0057] A kind of preparation method of porous graphene silver-loaded antibacterial composite material, it comprises the following steps:

[0058](1) Preparation of graphene quantum dot suspension: Weigh 0.6g of C60 powder, measure 80ml of concentrated sulfuric acid with a mass fraction of 98%, mix C60 powder and concentrated sulfuric acid in a beaker, put the beaker in an ice-water bath, and simultaneously Stir at a speed of 500rpm to obtain a mixed solution; weigh 1g of potassium permanganate powder, and slowly add it to the above mixed solution; remove the ice-water bath and replace it with a water bath, keep the temperature of the water bath at 30~40°C, and react for 6 hours; quickly add 200ml of pure Water, filtered, and then dialyzed for 3 days with a dialysis bag with a molecular weight cut-off of 1000 to obtain a suspension of graphene quantum dots; the suspension of graphene quantum dots was stirred at a speed of 100 rpm, while laser irradiation was performed for 40 min...

Embodiment 3

[0064] A kind of preparation method of porous graphene silver-loaded antibacterial composite material, it comprises the following steps:

[0065] (1) Preparation of graphene quantum dot suspension: Weigh 0.8g of C60 powder, measure 100ml of concentrated sulfuric acid with a mass fraction of 98%, mix C60 powder and concentrated sulfuric acid in a beaker, put the beaker in an ice-water bath, and simultaneously Stir at a speed of 500rpm to obtain a mixed solution; weigh 3g of potassium permanganate powder, and slowly add it to the above mixed solution; remove the ice-water bath and replace it with a water bath, keep the temperature of the water bath at 30-40°C, and react for 5 hours; quickly add 100ml of pure Water, filtered, and then dialyzed for 3 days with a dialysis bag with a molecular weight cut-off of 1000 to obtain a suspension of graphene quantum dots; the suspension of graphene quantum dots was stirred at a speed of 100 rpm, while laser irradiation was performed for 30 m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a deodorizing fiberglass packaging box. The preparation method comprises the following steps: (1) according to the size of the packaging box, manufacturing a mould; (2) compounding and fixing to form a fiber reinforced layer by using resin; (3) laying reinforcing ribs; (4) laying fiber cloth to form a first compound layer; (5) forming a second compound layer; (6) injecting antibacterial glue under vacuum; (7) curing; (8) demoulding to obtain the deodorizing fiberglass packaging box. Through reasonable matching of a diatomite / antibacterial composite material and diatomite / inorganic oxide, a synergistic effect between functional additives is achieved; then, epoxy resin used in the glue injecting step is injected and is modified into the antibacterial glue, so that after glue injection, the box body has the antibacterial performance from the inside to the outside, and thus the antibacterial performance and the antibacterial stability and persistence of the packaging box are improved; meanwhile, the packaging box has anti-formaldehyde and deodorant characteristics, meets multifunctional needs, and further widens application of the packaging box.

Description

technical field [0001] The invention relates to a preparation method of a deodorizing glass fiber reinforced plastic packing box. Background technique [0002] FRP has the characteristics of light weight, high specific strength, good fatigue resistance, good chemical corrosion resistance and good designability, and has been widely used in various fields. In recent years, the use of FRP materials to make various materials such as deodorized FRP packaging boxes has been used more and more in national defense and civilian use. But the function of the traditional deodorizing FRP packing box is single, which can no longer meet the diverse needs of people. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a method for preparing a deodorizing FRP packing box. [0004] The technical problem to be solved by the present invention is realized through the following technical solutions: [0005] A kind of preparation method ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B17/02B32B9/00B32B3/08B32B33/00B32B37/12B32B1/02C08L63/00C08L1/28C08K13/06C08K9/04C08K3/34C08K9/12C08K9/10C08K7/24C08K3/04C08K3/08B29C70/34
CPCC08L63/00B29C70/34B32B3/08B32B5/26B32B33/00B32B37/12B32B2439/62B32B2262/101B32B2262/106C08K2201/014B32B1/00C08L1/286C08K13/06C08K9/04C08K3/34C08K9/12C08K9/10C08K7/24C08K3/04C08K2003/0806
Inventor 陆庚
Owner 佛山市高明区尚润盈科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com