Photochromic gravure water-based ink and preparation method thereof

A technology of photochromic and water-based inks, applied in inks, household utensils, applications, etc., can solve problems such as single function, water-based inks without antibacterial properties, and inability to meet multiple needs

Inactive Publication Date: 2016-12-14
佛山市高明区尚润盈科技有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Gravure printing water-based ink is a new type of ink with low toxicity, no irritating smell, non-flammable, energy-saving and environmental protection, but ordinary water-based ink does not have antibacterial properties. The high-performance gravure water-based ink can endow the printed products printed with antibacterial water-based inks with high antibacterial properties. People who touch these printed products will be protected from the above germs, effectively cutting off the transmission of germs and protecting people's health.
At the same time, the function of traditional ink is single, which can no longer meet the diverse needs of people.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Photochromic gravure water-based ink and preparation method thereof
  • Photochromic gravure water-based ink and preparation method thereof
  • Photochromic gravure water-based ink and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A kind of preparation method of porous graphene silver-loaded antibacterial composite material, it comprises the following steps:

[0046] (1) Preparation of graphene quantum dot suspension: weigh 0.5g of C60 powder, measure 50ml of concentrated sulfuric acid with a mass fraction of 98%, mix C60 powder and concentrated sulfuric acid in a beaker, place the beaker in an ice-water bath, and simultaneously Stir at a speed of 500rpm to obtain a mixed solution; weigh 0.5g of potassium permanganate powder, and slowly add it to the above mixed solution; remove the ice-water bath and replace it with a water bath, keep the temperature of the water bath at 30~40°C, and react for 8 hours; quickly add 200ml Pure water, filtered, and then dialyzed for 3 days with a dialysis bag with a molecular weight cut-off of 1000, to obtain a suspension of graphene quantum dots; the suspension of graphene quantum dots was stirred at a speed of 100 rpm, while laser irradiation was performed for 30 ...

Embodiment 2

[0052] A kind of preparation method of porous graphene silver-loaded antibacterial composite material, it comprises the following steps:

[0053] (1) Preparation of graphene quantum dot suspension: Weigh 0.6g of C60 powder, measure 80ml of concentrated sulfuric acid with a mass fraction of 98%, mix C60 powder and concentrated sulfuric acid in a beaker, put the beaker in an ice-water bath, and simultaneously Stir at a speed of 500rpm to obtain a mixed solution; weigh 1g of potassium permanganate powder, and slowly add it to the above mixed solution; remove the ice-water bath and replace it with a water bath, keep the temperature of the water bath at 30~40°C, and react for 6 hours; quickly add 200ml of pure Water, filtered, and then dialyzed for 3 days with a dialysis bag with a molecular weight cut-off of 1000 to obtain a suspension of graphene quantum dots; the suspension of graphene quantum dots was stirred at a speed of 100 rpm, while laser irradiation was performed for 40 mi...

Embodiment 3

[0059] A kind of preparation method of porous graphene silver-loaded antibacterial composite material, it comprises the following steps:

[0060] (1) Preparation of graphene quantum dot suspension: Weigh 0.8g of C60 powder, measure 100ml of concentrated sulfuric acid with a mass fraction of 98%, mix C60 powder and concentrated sulfuric acid in a beaker, put the beaker in an ice-water bath, and simultaneously Stir at a speed of 500rpm to obtain a mixed solution; weigh 3g of potassium permanganate powder, and slowly add it to the above mixed solution; remove the ice-water bath and replace it with a water bath, keep the temperature of the water bath at 30-40°C, and react for 5 hours; quickly add 100ml of pure Water, filtered, and then dialyzed for 3 days with a dialysis bag with a molecular weight cut-off of 1000 to obtain a suspension of graphene quantum dots; the suspension of graphene quantum dots was stirred at a speed of 100 rpm, while laser irradiation was performed for 30 m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses photochromic gravure water-based ink and a preparation method thereof. The photochromic gravure water-based ink is prepared from, by weight, 70%-75% of water soluble resin, 10%-15% of deionized water, 5%-10% of water-based organic pigment, 3%-6% of ethyl alcohol, 0.5%-1% of kieselguhr / antibacterial compound, 1%-2% of dispersing agent, 0%-1% of slow drying agent, 0.5%-1% of water-based flatting agent, 0.5%-1% of water-based wax emulsion, 0.5%-1% of kieselguhr / inorganic oxide, 0.5%-1% of organic amine, 0.5%-1% of antifoaming agent and 0.1%-2% of photochromic compound. The ink has excellent antibacterial, anti-formaldehyde and deodorization properties and photochromic properties and meets the need for multiple functions, and the application range of the ink is further widened.

Description

technical field [0001] The invention relates to the technical field of inks, in particular to a photochromic gravure water-based ink and a preparation method thereof. Background technique [0002] Ink is an important material for printing packaging materials. It expresses patterns and characters on the substrate through printing. The ink includes main components and auxiliary components. They are evenly mixed and rolled repeatedly to form a viscous colloidal fluid; It is composed of pigments, linking materials and additives; it is used in various printings such as books, periodicals, packaging and decoration, and architectural decoration. With the increase of social demand, the variety and output of ink have also expanded and increased accordingly. Gravure printing water-based ink is a new type of ink with low toxicity, no irritating smell, non-flammable, energy-saving and environmental protection, but ordinary water-based ink does not have antibacterial properties. The hi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D11/50C09D11/107C09D11/102C09D11/105C09D11/03
CPCC09D11/50C09D11/03C09D11/102C09D11/105C09D11/107
Inventor 陆庚
Owner 佛山市高明区尚润盈科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com