Transparent conductive thin film and placode and touch screen and making method thereof and display device

A technology of a transparent conductive film and a touch screen, applied in the fields of a touch screen and its manufacturing method, a transparent conductive film, a substrate, and a display device. Indium tin oxide high impedance and other problems, to improve the visual effect, improve the electrical effect, reduce the effect of reflectivity

Active Publication Date: 2017-05-17
BOE TECH GRP CO LTD +1
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the prior art, indium tin oxide is generally used to make the touch electrodes of the touch screen. Indium tin oxide has good optical and electrical comprehensive properties, but compared with metal materials, the impedance of indium tin oxide is still high, which leads to touch The electrical effect of the screen needs to be improved
[0003] And because th

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Transparent conductive thin film and placode and touch screen and making method thereof and display device
  • Transparent conductive thin film and placode and touch screen and making method thereof and display device
  • Transparent conductive thin film and placode and touch screen and making method thereof and display device

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] This embodiment provides a transparent conductive film, which includes a transparent inorganic insulating layer, a metal layer and a transparent metal oxide conductive layer stacked, wherein the refractive index of the transparent inorganic insulating layer is less than 1.5.

[0046] In this embodiment, the transparent conductive film is composed of a stacked transparent inorganic insulating layer, a metal layer and a transparent metal oxide conductive layer. Adopting this structure can make the transparent conductive film have a low reflectivity and the conductivity is not weaker than that of metal. The transparent conductive film is used as the touch electrode of the touch screen, which will not affect the transmittance, but also can reduce the resistivity of the touch electrode, improve the electrical effect of the touch screen, and can also reduce the reflectivity of the touch screen. Further, the visual effect of the display device adopting the touch screen is impro...

Embodiment 2

[0057] This embodiment provides a substrate, including a plurality of signal transmission lines formed on the base substrate, and the signal transmission lines are made of the above-mentioned transparent conductive film.

[0058] In this embodiment, the signal transmission line of the substrate is made of a transparent conductive film. The transparent conductive film is composed of a transparent inorganic insulating layer, a metal layer and a transparent metal oxide conductive layer, so that the transparent conductive film has a low reflectivity and is conductive. The performance is not weaker than that of metal. Using the transparent conductive film to make signal transmission lines can not only meet the requirements of resistivity, but also because of its transparency, it can save the need to set up a black matrix that blocks signal transmission lines.

Embodiment 3

[0060] This embodiment provides a touch screen, and the touch electrodes of the touch screen are made of the above-mentioned transparent conductive film.

[0061] In this embodiment, the transparent conductive film is composed of a stacked transparent inorganic insulating layer, a metal layer and a transparent metal oxide conductive layer, so that the reflectance of the transparent conductive film is low and the conductivity is not weaker than that of metal. The touch electrode of the touch screen will not affect the transmittance, but also can reduce the resistivity of the touch electrode, improve the electrical effect of the touch screen, and can also reduce the reflectivity of the touch screen, thereby improving the use of touch screen. The visual effect of the display device of the screen.

[0062] Furthermore, the touch electrode bridging and / or signal transmission lines of the touch screen can also be made of transparent conductive film, and the use of the transparent co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a transparent conductive thin film and a placode and a touch screen and a making method thereof and a display device and belongs to the technical field of display. The transparent conductive thin film comprises a stack-set transparent inorganic insulating layer, a metal layer and a transparent metal oxide conductive layer, wherein refractive index of the transparent inorganic insulating layer is less than 1.5. According to the technical scheme, reflectivity of the touch screen and resistance of a touch-sensitive electrode can be reduced, electricity effect can be increased, and visual effect of the display device can be improved.

Description

technical field [0001] The invention relates to the field of display technology, in particular to a transparent conductive film, a substrate, a touch screen, a manufacturing method thereof, and a display device. Background technique [0002] In the prior art, indium tin oxide is generally used to make the touch electrodes of the touch screen. Indium tin oxide has good optical and electrical comprehensive properties, but compared with metal materials, the impedance of indium tin oxide is still high, which leads to touch The electrical effect of the screen needs to be improved. [0003] And because the visible light reflectance of indium tin oxide is relatively high (about 11%), which is greater than the visible light reflectance of the glass substrate (about 4%), after the touch display device is formed by attaching an external touch screen on the display , the reflectivity of the touch display device will be relatively large, and the visual effect will be poor. Contents o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01B5/14G06F3/041G02F1/133G02F1/1333
CPCG02F1/133G02F1/1333G06F3/041H01B5/14
Inventor 徐佳伟李保然李必生张雷郭总杰王准王庆浦
Owner BOE TECH GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap