Formula of cast stone slab

A slab and cast stone technology, which is applied in the formulation field of cast stone slabs, can solve problems such as inability to bear large loads and general strength, and achieve the effects of increasing service life, increasing load-bearing capacity, and increasing strength

Inactive Publication Date: 2017-08-25
SHAANXI SCI TECH UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The selection of existing cast stone raw materials is relatively traditional, resulting in its average strength and unable to bear large loads

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] The formula of the cast stone plate includes the following raw materials in parts by weight: 26 parts of granite, 18 parts of calcite, 25 parts of gneiss, 5 parts of sandstone, 12 parts of obsidian, 3 parts of hornblende, 6 parts of dolomite, 16 parts of blue Gold stone, 7 parts iron gallstone, 7 parts yellow wax stone, 13 parts chromite, all raw materials must be homogeneous, fine-grained unweathered raw rock, and ground into powder.

Embodiment 2

[0012] The formula of this cast stone plate comprises the raw material of following parts by weight: 29 parts of granite, 15 parts of calcite, 23 parts of gneiss, 8 parts of sandstone, 14 parts of obsidian, 5 parts of hornblende, 8 parts of dolomite, 14 parts of blue Gold stone, 5 parts iron gallstone, 5 parts yellow wax stone, 10 parts chromite, all raw materials must be homogeneous, fine-grained unweathered raw rock, and ground into powder.

Embodiment 3

[0014] The formula of this cast stone plate comprises the raw material of following parts by weight: 32 parts of granite, 12 parts of calcite, 20 parts of gneiss, 12 parts of sandstone, 15 parts of obsidian, 7 parts of hornblende, 10 parts of dolomite, 12 parts of bluestone Gold stone, 3 parts iron gallstone, 3 parts yellow wax stone, 8 parts chromite, all raw materials must be homogeneous, fine-grained unweathered raw rock, and ground into powder.

[0015] The formula of the cast stone plate adopts granite, calcite, and gneiss as the main materials, and sandstone, obsidian, hornblende, dolomite, lapis lazuli, iron gallstone, yellow wax stone, and chromite are used as the proportioning raw materials. The strength of the cast stone is improved to ensure that the load-bearing capacity of the cast stone plate is enhanced and its service life is improved.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a formula of a cast stone slab, and relates to the field of building materials. According to the formula of the cast stone slab, granite, calcite and gneiss are used as the main materials, sandstone, obsidian, hornblende, dolomite, lapis lazuli, iron gallbladder stone, chrismatite and chromite are used as matching raw materials, the strength of cast stone is sufficiently improved, the increase of the bearing capacity of the cast stone slab is ensured, and the service life of the cast stone slab is prolonged.

Description

technical field [0001] The invention relates to the field of building materials, more specifically, the invention relates to a formula of cast stone plates. Background technique [0002] Cast stone is a processed silicate crystalline material, which uses natural rock or industrial waste as the main raw material, and is made of regular crystal arrangement, hard texture and delicate non-metallic material through batching, melting, pouring, heat treatment and other processes. industrial materials. The selection of existing cast stone raw materials is relatively traditional, resulting in its general strength and unable to bear large loads. Contents of the invention [0003] The problem to be solved by the present invention is to provide a formula of cast stone plate with high strength and strong load-bearing capacity. [0004] In order to achieve the above object, the technical solution adopted by the present invention is: a formula for cast stone slabs, characterized in tha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C10/04C03C6/04
CPCC03C1/00C03C10/00
Inventor 黄文华田海宁黄研李根
Owner SHAANXI SCI TECH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com