Steel material for crude oil tank with excellent corrosion resistance, and crude oil tank

A corrosion-resistant, crude oil tank technology, applied in the field of crude oil tank steel and crude oil tank, can solve the problems of promoting corrosion, large coating area, and high inspection cost.

Active Publication Date: 2018-08-03
JFE STEEL CORP
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the coating work of crude oil tanks not only requires a large coating area, but also requires recoating every 10 years due to the deterioration of the coating film. Therefore, huge costs are incurred in inspection and coating.
Furthermore, it is pointed out that the damaged part of the repainted coating film will actually promote corrosion in the corrosive environment of crude oil tanks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel material for crude oil tank with excellent corrosion resistance, and crude oil tank
  • Steel material for crude oil tank with excellent corrosion resistance, and crude oil tank
  • Steel material for crude oil tank with excellent corrosion resistance, and crude oil tank

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0141]The steels with various compositions shown in Table 3 No. 1 to 37 are melted in a vacuum melting furnace to make steel ingots, or melted in a converter and made into billets by continuous casting, and they are reheated to 1150°C After that, hot rolling was performed at the finishing temperature shown in Table 4 to form a thick steel plate with a thickness of 25 mm, and then cooled to the cooling stop temperature shown in Table 4 at a water cooling rate of 10° C. / s.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

This steel material has a component composition comprising, in mass%, C: 0.03-0.18%, Si: 0.03-1.50%, Mn: 0.1-2.0%, P: 0.025% or less, S: 0.010% or less, Al: 0.015-0.049%, N: 0.008% or less, W: 0.005-0.5%, and Nd: 0.0001-0.010%, with the remainder being Fe and unavoidable impurities, wherein the dislocation density alpha of the steel material is set to within a range that satisfies formula (1), thereby obtaining a steel material for a crude oil tank that has excellent general corrosion resistance in the upper plate of a crude oil tank such as a tanker oil tank unit and that also has excellent local corrosion resistance in the bottom plate of the crude oil tank. Formula (1): alpha( / m2)<={1020*[%W]*[%Nd]} / {5*([%Al]-0.01)}, where [%M] is the content (mass%) of an element M in the steel material.

Description

technical field [0001] The present invention relates to an oil tank of a crude oil tanker formed by welding steel materials, and a tank for transporting or storing crude oil (hereinafter collectively referred to as "crude tank"). Steel materials for crude oil tanks that can prevent full surface corrosion at the bottom of the crude oil tank and localized corrosion at the bottom of the crude oil tank, and crude oil tanks made of the steel. [0002] It should be noted that the steel material for crude oil tanks of the present invention includes thick steel plates, thin steel plates and section steels. Background technique [0003] It is known that steel materials used on the inner surface of crude oil tanks of oil tankers, especially the back of the upper deck and the upper part of the side walls, are corroded over the entire surface. The following reasons etc. are mentioned as a cause which causes this whole surface corrosion. [0004] (1) Repeated occurrences of dew condens...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/00B65D90/02B65D90/22C22C38/12C22C38/60C21D8/02
CPCB65D90/02B65D90/22C21D8/02C22C38/00C22C38/12C22C38/60C22C38/001C22C38/02C22C38/04C22C38/06
Inventor 钓之郎村濑正次
Owner JFE STEEL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com