A kind of positive lead paste of lead-acid storage battery

A lead-acid battery, positive lead paste technology, applied in lead-acid batteries, battery electrodes, circuits and other directions, can solve the problems of complex steps, inability to significantly improve performance, increase battery costs, etc., to improve utilization, improve life, improve The effect of service life

What is AI technical title?
AI technical title is built by PatSnap AI team. It summarizes the technical point description of the patent document.
A lead-acid battery, positive lead paste technology, applied in lead-acid batteries, battery electrodes, circuits and other directions, can solve the problems of complex steps, inability to significantly improve performance, increase battery costs, etc., to improve utilization, improve life, improve The effect of service life

CN108400304BActive Publication Date: 2021-01-19HENAN CHILWEE GENSHORE POWER

13 Cites 0 Cited by

Image

Smart Image Click on the blue labels to locate them in the text.

Viewing Examples

Smart Image

Examples

Experimental program

Comparison scheme

Effect test

Embodiment 1

[0038] A positive lead paste for a lead-acid storage battery. The raw materials are composed of 90 parts of lead powder, 10 parts of sulfuric acid, 12 parts of water, 0.1 part of short fiber, 0.05 part of xanthan gum and 0.3 part of graphite in parts by weight. Wherein, the particle size of the xanthan gum is 20-200 mesh; the density of the sulfuric acid is 1.4±0.001g / cm 3 (25° C.); the short fibers are polyester fibers with a length of 2-6 mm.

Embodiment 2

[0040] A positive lead paste for a lead-acid storage battery. The raw materials are composed of 70 parts of lead powder, 6 parts of sulfuric acid, 10 parts of water, 0.5 part of short fiber, 0.5 part of xanthan gum and 0.2 part of graphite in parts by weight. Wherein, the particle size of the xanthan gum is 20-200 mesh; the density of the sulfuric acid is 1.4±0.001g / cm 3 (25° C.); the short fibers are polyester fibers with a length of 2-6 mm.

Embodiment 3

[0042] A positive lead paste for a lead-acid storage battery. The raw materials are composed of 90 parts of lead powder, 8 parts of sulfuric acid, 5 parts of water, 0.05 part of short fiber, 0.3 part of xanthan gum and 0.1 part of graphite in parts by weight. Wherein, the particle size of the xanthan gum is 20-200 mesh; the density of the sulfuric acid is 1.4±0.001g / cm 3 (25° C.); the short fibers are polyester fibers with a length of 2-6 mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine

Login to View More

PUM

Property	Measurement	Unit
particle size	aaaaa	aaaaa
density	aaaaa	aaaaa
length	aaaaa	aaaaa

Login to View More

Abstract

The invention discloses a lead-acid storage battery positive lead paste. The lead-acid storage battery positive lead paste is prepared from the following raw materials in parts by weight: 70-90 partsof lead powder, 3-15 parts of sulfuric acid, 5-20 parts of water, 0.05-1 part of short fiber, 0.05-0.5 part of graphite and 0.05-0.5 part of xanthan gum. A lead-acid storage battery prepared by usingthe positive lead paste is high in initial capacity, slow in attenuation and long in cycle life, has strong large current discharge and low temperature charge and discharge performance, and ensures that the combination performance of the lead paste and a grid is significantly improved; and the problems of low initial capacity, short cycle life, easy falling off of active materials and the like inexisting lead-acid storage batteries can be effectively solved.

Description

technical field [0001] The invention belongs to the technical field of lead-acid storage battery manufacturing, and in particular relates to a lead-acid storage battery anode lead paste. Background technique [0002] Compared with the existing nickel-metal hydride batteries and lithium-ion batteries, lead-acid batteries have the advantages of low cost, safety and reliability, mature production technology, long service life, easy recycling and stable electrical performance, etc. The best choice for commercial applications in the field of communication energy storage. However, due to the weakness of lead-acid batteries in terms of weight ratio, energy and cycle use, its wide application is limited. One of the main reasons for the low weight-to-energy ratio is that the weight of the positive plate of the lead-acid battery cannot be reduced due to the low utilization rate of the positive active material, especially in high-power and power applications. It is seriously challeng...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine

Login to View More

Application Information

Patent Timeline

19 Jan 2021

Publication

CN108400304B

IPC: H01M4/36; H01M4/57; H01M4/62; H01M10/06

CPC: H01M4/364; H01M4/57; H01M4/62; H01M4/622; H01M4/625; H01M10/06; Y02E60/10

Inventors: 李芹坡; 程志明