An adhesive, high temperature resistant technology, applied in the direction of adhesives, non-polymer adhesive additives, adhesive types, etc. The effect of contact
Inactive Publication Date: 2018-08-31
闫洪銮 +3
View PDF1 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] However, due to the low elongation of epoxy resin, high brittleness, and fatigue resistance of adhesive parts, if no modification tre
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0013] A high-temperature-resistant modified adhesive, each component by weight, 100 parts of epoxy resin, 50 parts of maleimide resin, 20 parts of alkylene glycidyl ether, 0.8 parts of ethylenediamine, methyl tetrahydro 2 parts of phthalic anhydride, 1 part of diphenylthiourea.
Embodiment 2
[0015] A high temperature resistant modified adhesive, the components are calculated by weight parts, 100 parts of epoxy resin, 30 parts of maleimide resin, 25 parts of alkylene glycidyl ether, 0.5 parts of ethylenediamine, methyl tetrahydro 1 part of phthalic anhydride, 0.5 part of diphenylthiourea.
Embodiment 3
[0017] A high-temperature-resistant modified adhesive, each component by weight, 100 parts of epoxy resin, 60 parts of maleimide resin, 15 parts of alkylene glycidyl ether, 1 part of ethylenediamine, methyl tetrahydro 3 parts of phthalic anhydride, 1.5 parts of diphenylthiourea.
[0018] A preparation process of a high-temperature-resistant modified adhesive, comprising the following steps:
[0019] Step 1. Add epoxy resin, maleimide resin, and ethylenediamine to the reaction kettle, and stir for one hour at 120 °;
[0020] Step 2. Cool to below 90°, add alkylene glycidyl ether, and continue to stir for half an hour;
[0021] Step 3. Add methyl tetrahydrophthalic anhydride and diphenylthiourea, and mix well to obtain a high-temperature-resistant modified adhesive.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a high-temperature-resistant modified adhesive. The adhesive comprises the following components in parts by weight: 100 parts of epoxy resin, 30-60 parts of maleimide resin, 15-25 parts of alkylidene glycidyl ether, 0.5-1 part of ethylenediamine, 1-3 parts of methyl tetrahydrophthalic anhydride, and 0.5-2 parts of thiocarbanilide. The high-temperature-resistant modified adhesive provided by the invention is an epoxy adhesive, but the high-temperature-resistant modified adhesive breaks through the disadvantage that an epoxy adhesive is not resistant to high temperature,and the high-temperature-resistant modified adhesive has excellent adhesion at the high temperature.
Description
technical field [0001] The invention relates to an adhesive, in particular to a high temperature resistant modified adhesive. Background technique [0002] Epoxy resin is an adhesive with many excellent properties. Its composition structure is relatively complex, including many hydroxyl groups, ether bonds and epoxy groups. It has high stability, good adhesion performance, good electrical insulation performance, blending The advantages of good performance. [0003] However, due to the low elongation of epoxy resin, high brittleness, and fatigue resistance of adhesive parts, if no modification treatment is carried out, the adhesive generally cannot withstand high temperature and has brittle defects, so the application field is limited. Contents of the invention [0004] (1) Technical problems to be solved [0005] In order to overcome the defects of the prior art, the invention provides a high temperature resistant modified adhesive. [0006] (2) Technical solution [0...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more