A metal surface treatment method

A metal surface treatment and metal surface technology, applied in the field of metal surface treatment, can solve the problems of incompleteness, poor surface polishing effect, difficult removal, etc., and achieve the effect of enhancing surface hardness

Active Publication Date: 2021-04-13
泽涵电气(内蒙古)有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, in actual use, it still has some shortcomings. It is difficult to take out when the metal surface shell is relatively strong, it is difficult to clean the rust or debris in the dead corner, and the effect of surface polishing is poor and not comprehensive.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A metal surface treatment method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The present invention provides such figure 1 Shown a kind of metal surface treatment method, specifically comprises the following steps:

[0024] Step 1. Fixing the metal as a whole: First, fix the metal to be processed by the clamping manipulator, then tilt the metal to be processed to an angle of 30° through the clamping manipulator, and then fix a protective shell on the outside of the metal to prevent post-processing. spills of waste;

[0025] Step 2. Metal surface shell removal: After that, the high-frequency vibrator is fixed on the metal surface, and the high-frequency vibrator performs high-frequency vibration to separate the shell and waste that need to be separated from the metal. At the same time, a blower is used to blow off the waste, which is unstable The metal breaks after being vibrated by a high-frequency vibrator, and then the precision of the metal as a whole can be detected to prevent the breakage of the later use. After that, the remaining stains o...

Embodiment 2

[0034] Further, in the above-mentioned embodiment 1, a metal surface treatment method specifically includes the following steps:

[0035] Step 1. Fixing the metal as a whole: First, fix the metal to be processed by the clamping manipulator, then tilt the metal to be processed to an angle of 45° through the clamping manipulator, and then fix a protective shell on the outside of the metal to prevent post-processing. spills of waste;

[0036]Step 2. Metal surface shell removal: After that, the high-frequency vibrator is fixed on the metal surface, and the high-frequency vibrator performs high-frequency vibration to separate the shell and waste that need to be separated from the metal. At the same time, a blower is used to blow off the waste, which is unstable The metal breaks after being vibrated by a high-frequency vibrator, and then the precision of the metal as a whole can be detected to prevent the breakage of the later use. After that, the remaining stains on the surface are...

Embodiment 3

[0045] The present invention provides such as figure 1 Shown a kind of metal surface treatment method, specifically comprises the following steps:

[0046] Step 1. Fixing the metal as a whole: First, fix the metal to be processed by the clamping manipulator, then tilt the metal to be processed to an angle of 60° through the clamping manipulator, and then fix a protective shell on the outside of the metal to prevent post-processing. waste spilled;

[0047] Step 2. Metal surface shell removal: After that, the high-frequency vibrator is fixed on the metal surface, and the high-frequency vibrator performs high-frequency vibration to separate the shell and waste that need to be separated from the metal. At the same time, a blower is used to blow off the waste, which is unstable The metal breaks after being vibrated by a high-frequency vibrator, and then the precision of the metal as a whole can be detected to prevent the breakage of the later use. After that, the remaining stains ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for metal surface treatment, which specifically includes the following steps: Step 1. Fixing the metal as a whole: first, fix the metal to be treated by a clamping manipulator, and then tilt the metal to be treated to 30° by the clamping manipulator ‑60° angle, and then fix a protective shell on the outside of the metal to prevent the waste generated by post-processing from splashing out. In the actual use of the present invention, the metal surface shell is removed by setting, and then the high-frequency vibrator is fixed on the metal surface, and the high-frequency vibrator performs high-frequency vibration to separate the shell and the waste that need to be separated from the metal, and simultaneously uses a blower to remove the waste. Blow off, the unstable metal breaks after being vibrated by a high-frequency vibrator, and then the precision of the metal as a whole can be detected to prevent the breakage in later use, and then the remaining stains on the surface are removed with a high-pressure water spray gun.

Description

technical field [0001] The invention relates to the technical field of metal surface treatment technology, in particular to a metal surface treatment method. Background technique [0002] The invention patent of the patent application publication number CN102218389A discloses a metal surface treatment method, which includes the following steps: (1) metal surface rust removal and paint removal treatment; (2) metal surface rust prevention treatment; (3) metal surface Protective treatment, that is, to get the treated metal. Compared with the existing technology, the present invention can completely transform the rust into a film. The water-based system does not contain harmful substances and can be applied without solvents. The base material can be applied with rust and rust-proof The effect is good, spraying various paints and epoxy asphalt, the mechanical bite force of the joint surface is large, no bubbles, no hanging marks, no need to spray multiple times, no need to add th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23P9/00
CPCB23P9/00
Inventor 孙金龙陈华余雪荣孙凯
Owner 泽涵电气(内蒙古)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com