A technology of alloy fiber and polymer, applied in the direction of conjugated synthetic polymer rayon, fiber treatment, single-component polyolefin rayon, etc., which can solve the problems of reduced wear resistance, reduced mechanical properties, and compatibility Achieves excellent wear resistance, suppression of uneven dyeing, and suppression of fiber diameter deviation

Active Publication Date: 2022-05-10
TORAY IND INC
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the compatibility of the composite polymers is low, not only the improvement effect of the polymer alloy cannot be obtained, but also problems such as a decrease in mechanical properties and a decrease in wear resistance are caused.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polymer alloy fiber and fiber structure containing same
  • Polymer alloy fiber and fiber structure containing same
  • Polymer alloy fiber and fiber structure containing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0117] Add 70 parts by weight of polypropylene (PP) ("Novatec" (registered trademark) MA2 manufactured by Japan Polypropylene Corporation), 28 parts by weight of polyethylene terephthalate (PET) (T701T manufactured by Toray), 2 parts by weight Parts of styrene-ethylene-butylene-styrene copolymer (C) (25 parts by weight of styrene block, ethylene block / butylene block=0.25), using a twin-screw extruder, at a mixing temperature of 280 °C for mixing. After the strands discharged from the twin-screw extruder were cooled with water, they were cut into about 5 mm in length using a pelletizer to obtain pellets. After the obtained pellets were vacuum-dried at 150° C. for 12 hours, they were supplied to an extruder-type melt spinning machine to be melted, and the spinning temperature was 285° C., and the discharge amount was 31.5 g / min. 0.18mm, the length of the discharge hole is 0.23mm, the number of holes is 36, and the circular hole) is discharged to obtain the spun yarn. The spun ...

Embodiment 2～6

[0119] A stretched yarn was produced in the same manner as in Example 1 except that the functional group of the styrene-ethylene-butylene-styrene copolymer (C) was changed as shown in Table 1. Table 1 shows the evaluation results of fiber properties and fabric properties of the obtained fibers.

Embodiment 7～11

[0121] A stretched yarn was produced in the same manner as in Example 5 except that the content of the styrene block (C1) in the styrene-ethylene-butylene-styrene copolymer (C) was changed as shown in Table 2. Table 2 shows the evaluation results of fiber properties and fabric properties of the obtained fibers.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
temperatureaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The polymer alloy fiber is characterized in that it comprises polyolefin (A), polyester (B), styrene-ethylene-butylene-styrene copolymer (C), the fiber diameter CV% is 0.1-2.5%, and the fiber transverse The dispersion diameter of the island component in the cross section is 1 to 1000 nm. The present invention provides the following polymer alloy fiber, which has both the properties of polyolefin and polyester, has suppressed variation in fiber diameter between single yarns, has excellent mechanical properties and wear resistance, and has suppressed uneven dyeing, and can be used as The form of a fibrous structure is suitably used.

Description

technical field [0001] This invention relates to polymer alloy fibers. More specifically, it relates to a polymer alloy fiber that combines the characteristics of polyolefin and polyester, has suppressed variation in fiber diameter between single yarns, has excellent mechanical properties and abrasion resistance, and has suppressed uneven dyeing , can be suitably used in the form of a fiber structure. Background technique [0002] Polyolefins are excellent in lightness, abrasion resistance, heat retention, and water resistance, and polyesters are excellent in heat resistance, mechanical properties, dyeability, and chemical resistance. Therefore, polyolefins and polyesters are used as fibers, films, etc. The raw materials of molded products such as are widely used. [0003] Composite polymer alloys based on heterogeneous polymers can make use of the advantages of each polymer and compensate for their disadvantages, and thus are an effective method for developing new materia...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F8/06D01F8/10D01F8/14
CPCD01F6/46D01F8/06D01F8/10D01F8/14D01D5/34C08L23/12C08L23/20C08L67/02C08L2203/12C08L2205/03
Inventor 鹿野秀和长尾优志望月克彦
Owner TORAY IND INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap