Floor used indoors and outdoors and manufacturing method thereof

An indoor and outdoor flooring technology, applied in the direction of architecture, building structure, floor, etc., can solve the problems of poor floor texture, poor anti-skid performance, etc., and achieve the effect of solving poor texture

Inactive Publication Date: 2019-11-26
南京金铭新型装饰材料有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Purpose of the invention: The purpose of the present invention is to provide a general indoor and outdoor floor and its preparation method, which can solve the problems of poor texture and poor anti-skid performance of the existing indoor and outdoor general floor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Embodiment 1: The indoor and outdoor universal floor of this embodiment includes 20 parts of PVC resin powder, 15 parts of PVC regenerated resin powder, 6 parts of orthoclase, 5 parts of 100 mesh alumina, 3 parts of sodium methyl silicate, 5 parts of phytosterol 10 parts of calcium stearate, 4 parts of saturated octadecylamide, 7 parts of barium ferrite, 3 parts of neodymium oxide, and 2 parts of ethyl methacrylate. According to the ratio of raw materials during preparation, PVC resin powder, PVC recycled resin powder, orthoclase, 100 mesh alumina, sodium methyl silicate, phytosterol, calcium stearate, saturated octadecylamide, barium ferrite , neodymium oxide, and ethyl methacrylate are added to the mixer and mixed at a speed of 1500 rpm, the time is 25-35 minutes, and the temperature is 100°C to obtain the mixture for later use; the obtained mixture is added to the granulator at a temperature of 125°C Carry out granulation, and cool the obtained pellets to obtain a PV...

Embodiment 2

[0017] Embodiment 2: the indoor and outdoor universal floor of the present embodiment comprises 25 parts of PVC resin powder, 18 parts of PVC recycled resin powder, 10 parts of orthoclase, 8 parts of 100 mesh bauxite, 9 parts of sodium methyl silicate, 10 parts of phytosterol 15 parts of calcium stearate, 8 parts of saturated octadecylamide, 12 parts of barium ferrite, 5 parts of neodymium oxide, and 4 parts of ethyl methacrylate. During preparation, according to the ratio of raw materials, PVC resin powder, PVC recycled resin powder, orthoclase, 100 mesh alumina, sodium methyl silicate, phytosterol, calcium stearate, saturated octadecylamide, ferrous acid Add barium, neodymium oxide, and ethyl methacrylate into the mixer and mix, the speed is 1500 rpm, the time is 25-35 minutes, the temperature is 100°C, and the mixture is obtained for later use; the obtained mixture is added to the granulator at a temperature of 125°C granulation, and after cooling the obtained pellets, a PV...

Embodiment 3

[0018] Embodiment 3: The indoor and outdoor universal floor of this embodiment includes 22 parts of PVC resin powder, 17 parts of PVC regenerated resin powder, 8 parts of orthoclase, 6.5 parts of 100 mesh alumina, 6 parts of sodium methyl silicate, 7 parts of phytosterol 13 parts of calcium stearate, 6 parts of saturated octadecylamide, 10 parts of barium ferrite, 4 parts of neodymium oxide, and 3 parts of ethyl methacrylate. During preparation, according to the ratio of raw materials, PVC resin powder, PVC recycled resin powder, orthoclase, 100 mesh alumina, sodium methyl silicate, phytosterol, calcium stearate, saturated octadecylamide, ferrous acid Add barium, neodymium oxide, and ethyl methacrylate into the mixer and mix, the speed is 1500 rpm, the time is 25-35 minutes, the temperature is 100°C, and the mixture is obtained for later use; the obtained mixture is added to the granulator at a temperature of 125°C granulation, and after cooling the obtained pellets, a PVC cal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a floor used indoors and outdoors. The floor comprises 25 to 35 parts of polyvinyl chloride (PVC) resin powder, 10 to 20 parts of PVC regenerated resin powder, 8 to 18 parts oforthoclase, 2 to 6 parts of methyl sodium silicate, 12 to 16 portions of calcium stearate, 3 to 9 parts of saturated stearamide and 1 to 5 parts of ethyl methacrylate. The invention discloses a manufacturing method of the floor used indoors and outdoors. Compared with the prior art, the floor used indoors and outdoors has the characteristics of high texture and good skid resistance.

Description

technical field [0001] The invention belongs to the field of decoration materials, in particular to an indoor and outdoor floor and a manufacturing method thereof. Background technique [0002] Indoor and outdoor universal floor, can be applied to both indoors and outdoors. The existing indoor and outdoor general-purpose floors have the problems of poor texture and poor anti-skid performance. [0003] Therefore, new technologies are urgently needed to improve the deficiencies of the prior art. Contents of the invention [0004] Purpose of the invention: The purpose of the present invention is to provide an indoor and outdoor universal floor and its preparation method, which can solve the problems of poor texture and poor anti-skid performance of the existing indoor and outdoor universal floor. [0005] Technical solution: a general indoor and outdoor floor, characterized in that it includes PVC resin powder, PVC recycled resin powder, orthoclase, sodium methyl silicate, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K13/02C08K3/34C08K5/098C08K5/20C08K3/24E04F15/10
CPCC08K2201/014C08L27/06C08L2205/025E04F15/105C08K13/02C08K3/34C08K5/098C08K5/20C08K3/24
Inventor 陈振华杨斌李光保赵春水张勇胡玉军
Owner 南京金铭新型装饰材料有限公司