A kind of preparation method of injectable L-lactic acid microparticles

A technology of L-polylactic acid and microparticles, which is applied in the field of medical cosmetic materials, can solve the problems of severe inflammatory reaction, poor dispersion effect, and long duration, and achieve good reconstitution and dispersion, good application effect, reduction degree and duration Effect

Active Publication Date: 2021-12-14
普丽妍(南京)医疗科技有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Purpose of the invention: In view of the problems that the L-polylactic acid particles prepared by the existing method are all microspheres, the dispersion effect is not good, and the inflammatory reaction in the body after the degradation of the microspheres is severe and the duration is long, the present invention provides an injectable poly-L-lactic acid particle The preparation method, the method can be prepared to obtain sheet-like L-polylactic acid microparticles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of injectable L-lactic acid microparticles
  • A kind of preparation method of injectable L-lactic acid microparticles
  • A kind of preparation method of injectable L-lactic acid microparticles

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Disperse L-polylactic acid microspheres with an intrinsic viscosity of 3.8dL / g and a particle size of 60 microns in a mixed aqueous solution of sodium carboxymethylcellulose and mannitol, freeze-dry, heat the sample to 90 degrees, and apply 8 kg / cm2 pressure, after holding the pressure for 4 hours, the compressed sample was dissolved in water to form a solution, and after freeze-drying, injectable L-lactic acid microparticles could be obtained, the SEM image of which is as follows figure 1 , it can be seen that the resulting product is in the form of thin flakes.

Embodiment 2

[0024] Disperse L-polylactic acid microspheres with an intrinsic viscosity of 2.0dL / g and a particle size of 100 microns in a mixed aqueous solution of sodium carboxymethylcellulose and mannitol, freeze-dry, heat the sample to 60 degrees, and apply 1 kg / cm2 pressure, after holding the pressure for 0.5 hours, the compressed sample was dissolved in water to make a solution, and after freeze-drying, injectable L-lactic acid microparticles could be obtained, and its surface morphology was similar to that in Example 1. Also in thin flake form.

Embodiment 3

[0026] Disperse L-polylactic acid microspheres with an intrinsic viscosity of 5.0dL / g and a particle size of 10 microns in a mixed aqueous solution of sodium carboxymethylcellulose and mannitol, freeze-dry, heat the sample to 100 degrees, and apply 10 kg / cm2 pressure, after holding the pressure for 5 hours, the compressed sample is dissolved in water to make a solution, and after freeze-drying, injectable L-lactic acid particles can be obtained. Appearance is similar to that in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of injectable L-lactic acid microspheres, comprising the following steps: (1) dispersing the L-polylactic acid microspheres into a mixed aqueous solution of carboxymethyl cellulose and mannitol, and freeze-drying; (2) The freeze-dried sample is pressurized and compressed, and the compressed sample is dissolved in water to form a solution, and freeze-dried again to obtain sheet-like injectable L-lactic acid microparticles. The L-polylactic acid particles prepared by the present invention exist in the form of flake particles, and compared with the existing L-lactic acid microspheres, it is more conducive to the dispersion in viscous solutions, so that its application effect is better; and, the present invention The inventive method does not need to use organic solvents, and compared with the conventional emulsification method, the preparation process is green and environmentally friendly; in addition, the method has a simple process, and compared with the existing emulsification method for preparing L-polylactic acid microspheres, the preparation efficiency of the product is high, and the yield Large, suitable for industrial large-scale preparation.

Description

technical field [0001] The invention relates to a preparation method of injectable L-lactic acid microparticles, belonging to the field of medical cosmetic materials. Background technique [0002] Poly-L-lactic acid has good biocompatibility and degradation performance, and has been widely used in absorbable medical devices, tissue engineering, drug controlled release and medical cosmetic products. Injectable L-polylactic acid microspheres can be used as a beauty product. After being injected into the body, it can stimulate cells to produce a large amount of extracellular matrix, which plays a role in beauty and wrinkle removal (Clinics in Dermatology 2009, 27, S3-S12; Dermatol Surg 2005, 31, 1511-1518). [0003] The micronization of L-lactic acid is usually prepared into microspheres by emulsification method, and it is kept in a stable dispersion state in water by adding surfactants such as PVA, sodium dodecylsulfonate, Tween, and Span. The Chinese invention patent (publi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): A61L27/18A61L27/58A61L27/50
CPCA61L27/18A61L27/58A61L27/50A61L2400/06C08L67/04
Inventor何斌赵楠蒲雨吉朱虹成磊张译心
Owner普丽妍(南京)医疗科技有限公司