A kind of high temperature and anti-scratch pi battery label material and preparation method thereof

A label material and high temperature resistant technology, applied in the field of film materials, can solve the problems of non-printability and non-scratch-resistant surface, achieve good temperature resistance and improve the effect of scratch resistance

Active Publication Date: 2021-07-27
SHENZHEN LICHANGSHI ADHESIVE PROD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is necessary for a product to have more prominent advantages at the same time, and most products in the PI product market currently have problems such as non-scratch-resistant surfaces and non-printable surfaces.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high temperature and anti-scratch pi battery label material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A method for preparing a high temperature and scratch-resistant PI battery label material, characterized in that it comprises the following steps:

[0023] (1) Synthesis of modified polyurethane resin, the first stage is to add reactive acrylamide, 2,6-dicarboxynaphthalene, acetic anhydride, and conduct chemical crosslinking reaction with polyurethane resin at 120 ° C; the second stage is the internal addition stage , the temperature is 200°C, the stirring speed is 120 rpm, until no acid is distilled out; the high temperature resistant glue is a commercially available epoxy resin high temperature resistant glue. The mass ratio of reactive acrylamide, 2,6-dicarboxynaphthalene, acetic anhydride, and polyurethane resin is 5:5-5.5:8-10:200. In the internal addition stage, the temperature is 200° C., and the stirring speed is 120 rpm.

[0024] (2) Use a stirring device to add the isocyanate hardener into the modified polyurethane resin and stir evenly, and the proportioning...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a high-temperature-resistant and scratch-resistant PI battery label material and a preparation method thereof, which comprise from top to bottom: a scratch-resistant and scratch-resistant resin coating, a PI polyimide film, a high-temperature-resistant glue, and a release film; The anti-scratch resin coating comprises: modified polyurethane resin, isocyanate, ethyl acetate, anhydrous toluene; The preparation method of described modified polyurethane resin is: first stage by adding reactive acrylamide, 2,6-dicarboxynaphthalene , acetic anhydride, and polyurethane resin for chemical cross-linking reaction; the second stage is the internal addition stage, and the acid is stirred out at high temperature.

Description

technical field [0001] The invention belongs to the field of film materials, and in particular relates to a high-temperature-resistant and scratch-resistant PI battery label material and a preparation method thereof. Background technique [0002] As the market develops faster and faster, everyone's demand and requirements for products are getting higher and higher. It is necessary for a product to have more prominent advantages at the same time, but most of the products in the PI product market currently have problems such as non-scratch-resistant surfaces and non-printable surfaces. Therefore, in order to make the battery label simpler and more convenient, this product is specially developed. Contents of the invention [0003] The invention provides a PI battery label material with impact resistance, high temperature resistance and scratch resistance and a preparation method thereof, by modifying the surface coating (oily polyurethane) (introducing acrylamide functional ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G09F3/02C09D175/04C09D7/63C08J7/046C08J3/24C08L79/08
CPCC08J3/24C08J2375/04C08J2379/08C08J2475/04C09D175/04C09D7/63G09F3/02G09F2003/0232C08K5/29
Inventor 唐贤坤王益刚司徒灼铝
Owner SHENZHEN LICHANGSHI ADHESIVE PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com