A kind of modified hydroxypropyl methylcellulose for reinforced tile adhesive and its preparation method and application

A technology of hydroxypropyl methylcellulose and tile adhesive, which is applied in the direction of cellulose adhesives, adhesives, adhesive types, etc., can solve the problems of small production capacity, low labor intensity, low pressure, etc., and achieve improvement and maintenance Moisture capacity, improvement of tensile bond strength, effect of improving tensile bond strength

Active Publication Date: 2021-06-15
SHANDONG YITENG NEW MATERIAL CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The internal pressure of the liquid-phase method equipment is small, the requirements for the pressure-bearing capacity of the equipment are low, and the risk is small. After the cellulose is soaked in the lye, it will be fully swollen and alkalized evenly. Well, products with relatively uniform substitution and viscosity can be obtained, and the variety is easy to replace, but the reactor should not be too large (generally within 15m 3 Below), the production capacity is relatively small, and if the output is to be increased, multiple reactors must be added, and the reaction process requires a large amount of organic solvent as a carrier, and the reaction time is also long (generally more than 10 hours), which increases solvent distillation recovery and time cost
The gas-phase method has compact equipment, high single-batch yield, and the reaction is carried out in a horizontal autoclave. The time (generally 5-8 hours) is shorter than that of the liquid-phase method, and does not require a complicated solvent recovery system. After the reaction is completed, the excess methyl chloride And the by-product dimethyl ether enters the recovery system in the form of gas, and is recycled and reused separately. The labor cost is low, the labor intensity is low, and the production cost is lower than that of the liquid phase method, but the investment in equipment and automatic control is large, and the technical content is high. Expensive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of modified hydroxypropyl methylcellulose for reinforced tile adhesive and its preparation method and application
  • A kind of modified hydroxypropyl methylcellulose for reinforced tile adhesive and its preparation method and application
  • A kind of modified hydroxypropyl methylcellulose for reinforced tile adhesive and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] Modified hydroxypropyl methylcellulose for reinforced tile adhesive, made from raw materials of the following quality: 74kg of hydroxypropylmethylcellulose, hydroxypropyl starch (19.5% hydroxypropoxy content, 5% type B LVT viscosity 1950cp, ash content 7.5%, produced by Shandong Yiteng New Material Co., Ltd.) 20kg, anionic polyacrylamide 3kg and guar gum 3kg;

[0052] Among them, hydroxypropyl methylcellulose is made of cotton cellulose powder (average degree of polymerization is 2663, particle diameter is 0.230mm, bulk density is 175g / L) 100kg, granular sodium hydroxide (particle diameter is 0.7mm) 27kg, hydrogen Sodium oxide aqueous solution (mass concentration: 50%) 63kg, methyl chloride 74kg and propylene oxide 16kg are prepared.

[0053] The preparation method specifically comprises the following steps:

[0054] (1) Take each raw material by the above-mentioned quality;

[0055] (2) Add cotton cellulose powder, granular sodium hydroxide and aqueous sodium hydroxi...

Embodiment 2

[0058] Modified hydroxypropyl methylcellulose for reinforced tile adhesive, made from the following quality raw materials: hydroxypropyl methylcellulose 66kg, hydroxypropyl starch (hydroxypropoxy content is 19.5%, 5% type B LVT viscosity 1950cp, ash content 7.5%, produced by Shandong Yiteng New Material Co., Ltd.) 30kg, nonionic polyacrylamide 2kg and gum arabic 2kg;

[0059] Among them, hydroxypropyl methylcellulose consists of 100kg of wood cellulose powder (average degree of polymerization is 2880, particle size is 0.230mm, bulk density is 175g / L), granular sodium hydroxide (particle size is 0.7mm) 34kg, hydrogen Prepared from 51kg of sodium oxide aqueous solution (50% mass concentration), 79kg of methyl chloride and 12kg of propylene oxide.

[0060] The preparation method specifically comprises the following steps:

[0061] (1) Take each raw material by the above-mentioned quality;

[0062] (2) Add wood cellulose powder, granular sodium hydroxide and aqueous sodium hydro...

Embodiment 3

[0065] Modified hydroxypropyl methylcellulose for reinforced tile adhesive, made from raw materials of the following quality: 71 kg of hydroxypropyl methylcellulose, hydroxypropyl starch (19.5% hydroxypropoxy content, 5% type B LVT viscosity 1950cp, ash content 7.5%, produced by Shandong Yiteng New Material Co., Ltd.) 25kg, polyvinyl alcohol 2kg and carrageenan 2kg;

[0066] Wherein, hydroxypropyl methylcellulose is made of bamboo cellulose powder (average degree of polymerization is 1060, particle diameter is 0.18mm, bulk density is 150g / L) 20kg, wood cellulose powder (average degree of polymerization is 2530, particle diameter is 0.18mm, bulk density 150g / L) 60kg, cotton cellulose powder (average degree of polymerization 5010, particle size 0.18mm, bulk density 150g / L) 20kg, granular potassium hydroxide (particle size 0.3mm) 65kg , Potassium hydroxide aqueous solution (mass concentration is 40%) 100kg, methyl chloride 167kg and propylene oxide 65kg make.

[0067] The prepar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a modified hydroxypropyl methylcellulose for reinforced tile adhesive, which is prepared from the following raw materials in mass percentage: 54%-94% of hydroxypropylmethylcellulose, 5%-40% of starch ether , dispersant 0.5%-3% and rheological agent 0.5%-3%; wherein, hydroxypropyl methylcellulose is made from cellulose powder, granular alkali, liquid alkali, methyl chloride and propylene oxide; the preparation method is (1) Weigh each raw material; (2) Mix cellulose powder, granular alkali, liquid alkali, methyl chloride and propylene oxide, carry out etherification reaction, and then carry out neutralization, washing, centrifugation, drying and pulverization in sequence , to obtain hydroxypropyl methyl cellulose; (3) mixing and stirring hydroxypropyl methyl cellulose, starch ether, dispersant and rheological agent to obtain final product. The product obtained by the invention has stable quality, has the function of improving the tensile bonding strength of the tile adhesive, is applied to modern tiles with large size and high quality, and can significantly improve the safety of the tiles in use.

Description

technical field [0001] The invention relates to the technical field of building materials, and more specifically relates to a modified hydroxypropyl methylcellulose for reinforced tile adhesives and a preparation method and application thereof. Background technique [0002] As a decorative material, ceramic tiles have a vast market, but with the continuous improvement of the specialization of the ceramic tile market, more and more consumers are pursuing the seamless effect of wall decoration, making large-scale ceramic tiles more and more popular. At the same time, large-area The increasing popularity of residential buildings has also promoted the popularity of large-size tiles. As the size and quality of ceramic tiles are getting bigger and bigger, the requirements for safety are getting higher and higher. Traditional tile adhesives have been difficult to meet the requirements, so new tile adhesives have been developed rapidly. [0003] Usually, the main reasons for the ti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J101/28C09J103/08C09J11/08C08B11/193
CPCC09J101/284C09J11/08C08B11/193C08L2205/035C08L3/08C08L33/26C08L5/00C08L29/04C08L71/02
Inventor 滕鲲赵明滕波李青华姜爱梅赵建玉孟兆武
Owner SHANDONG YITENG NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products