Preparation method of light-shielding tape for wireless charger
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of wireless chargers and light-shielding tapes, applied in applications, adhesives, household appliances, etc., can solve the problems of affecting appearance, film performance, and lack of anti-fingerprint performance, so as to enhance dirt resistance, reduce adhesion, The effect of reducing the difficulty of cleaning
Active Publication Date: 2022-02-11
ZHEJIANG OUREN NEW MATERIALS CO LTD
View PDF4 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] At present, this kind of tape does not have anti-fingerprint performance. After repeated use, the residual fingerprint marks not only affect the appearance, but also have a certain impact on the performance of the film material.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1～4
[0022] Embodiments 1 to 4: A method for preparing a light-shielding adhesive tape for a wireless charger, comprising a black ink layer 1, a substrate layer 2, and an adhesive layer 3, and the black ink layer 1 and the adhesive layer 3 are respectively Located on the upper surface and the lower surface of the substrate layer 2, the side of the adhesive layer 3 opposite to the substrate layer 2 is provided with a release layer 4;
[0023] The black ink layer 1 is obtained by drying the black ink, and the black ink is obtained through the following steps:
[0024] S1. Mix 60-80 parts of water-based polyurethane, 15-25 parts of deionized water, 1-5 parts of 1,1',1"-methine tris(4-isocyanate)benzene, and 0.1-0.3 parts of tripolyphosphoric acid Sodium is added to the high-speed stirring dispersant for stirring, the speed is 300-500r / min, and the mixture is uniform;
[0025] S2. Add 1-5 parts of carbon black, 1-1.5 parts of sodium silicate, 1-5 parts of polyethyleneimine, 0.5-2 part...
Embodiment 1
[0031] In embodiment 1, light absorbing agent is selected from nanometer Al / Al 2 o 3 For the core-shell material, the above-mentioned coupling agent is selected from coupling agent KH-580, the above-mentioned substrate layer 2 is a PET layer with a thickness of 2 μm, and the thickness of the above-mentioned black ink layer 1 is 1 μm.
Embodiment 2
[0032] In Example 2, the light absorbing agent is selected from nano-nickel powder, the above-mentioned coupling agent is selected from coupling agent KBM403, the above-mentioned substrate layer 2 is a PET layer with a thickness of 2.5 μm, and the thickness of the above-mentioned black ink layer 1 is 1.3 μm.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
thickness
aaaaa
aaaaa
thickness
aaaaa
aaaaa
thickness
aaaaa
aaaaa
Login to View More
Abstract
The invention discloses a method for preparing a light-shielding tape for a wireless charger, comprising a black ink layer, a substrate layer and an adhesive layer, wherein the black ink layer and the adhesive layer are respectively located on the upper surface of the substrate layer and the lower surface, the side of the adhesive layer opposite to the base material layer is provided with a release layer; the black ink layer is obtained by drying the black ink, and the black ink is prepared by the following steps: S1. 60~80 parts of water-based polyurethane, 15~25 parts of deionized water, 1~5 parts of 1,1',1"-methylenetris(4-isocyanato)benzene, 0.01~0.03 parts of sodium tripolyphosphate added at high speed Stir in the dispersing agent, the speed is 300~500r / min, and the mixing is uniform; S2, add 1~5 parts of carbon black, 1~1.5 parts of sodium silicate, 1~5 parts of polyethyleneimine, 0.5~2 parts of eighteen Alkyl dimethyl benzyl ammonium chloride and 0.5~1.5 parts of coupling agent, the rotating speed is adjusted to 500~600r / min, and the dispersion and stirring are uniform. The invention has anti-fingerprint performance, and will not remain after repeated use in various environments Fingerprint marks can avoid the corrosion of the tape caused by fingerprints and sweat stains.
Description
technical field [0001] The invention belongs to the technical field of adhesive tapes, and in particular relates to a preparation method of a light-shielding adhesive tape used for a wireless charger. Background technique [0002] Wireless charging technology, also known as inductive charging and non-contact charging, is a new charging technology derived from wireless power transmission technology. Wireless charging technology has developed rapidly in recent years, but it has also encountered many technical difficulties, such as improving charging efficiency, reducing costs, and the effective charging distance is too short. In order to obtain higher charging efficiency and reduce or eliminate the influence of the electromagnetic field on the mobile phone during charging, it is necessary to use an electromagnetic shielding film for shielding. The function of the electromagnetic shielding film is to isolate the influence of the electromagnetic field on the mobile phone, and p...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 