Chromium-based high-nitrogen alloy cushion block for silicon steel high-temperature heating furnace and preparation method thereof

A high-temperature heating and high-nitrogen alloy technology, which is applied in heat treatment furnaces, heat treatment equipment, metal processing equipment, etc., can solve the problem of reducing limited resources and achieve the effects of improving adhesion, creep resistance, and strength

Active Publication Date: 2022-04-29
烟台新钢联冶金科技有限公司
View PDF29 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the disclosed alloy contains tungsten, and as we all know, tungsten, as a non-renewable resource, is facing a rapid reduction of limited resources due to a large number of unreasonable mining over the years; for the sustainable development of this field, it is urgent to find alternative products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chromium-based high-nitrogen alloy cushion block for silicon steel high-temperature heating furnace and preparation method thereof
  • Chromium-based high-nitrogen alloy cushion block for silicon steel high-temperature heating furnace and preparation method thereof
  • Chromium-based high-nitrogen alloy cushion block for silicon steel high-temperature heating furnace and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] Below in conjunction with embodiment further illustrate the present invention.

[0027] The eight embodiments of the present invention correspond to the preparation of heat-resistant pads from sample 1 to sample 8 in Table 1, respectively, and are casted according to the specific alloy composition in Table 1.

[0028] Table 1 Sample chemical composition (mass %)

[0029]

[0030]

[0031] Among them, the difference between sample 2, sample 3 and sample 4 and sample 1 is mainly reflected in the change of Mo content, and the difference between sample 5, sample 6 and sample 7 and sample 1 is mainly reflected in the content of N The content changes, and the difference between sample 8 and sample 1 is mainly reflected in whether rare earth elements (La and Ce) are added.

[0032] The above-mentioned chromium-based high-nitrogen alloy heat-resistant pads for silicon steel high-temperature heating furnaces are all prepared by hot-melt method, and the preparation steps a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
heat deflection temperatureaaaaaaaaaa
service temperatureaaaaaaaaaa
Login to view more

Abstract

The invention discloses a chromium-based high-nitrogen alloy cushion block for a silicon steel high-temperature heating furnace and a preparation method thereof. The alloy cushion block contains Cr, Mo, N, La, Ce and Fe, and does not contain tungsten; the alloy cushion block In terms of high temperature oxidation resistance and high temperature creep resistance, it is superior to the ferrochrome alloy of the prior art; the present invention can optimize the replacement of the existing ferrochrome alloy block for the high temperature heating furnace of silicon steel to meet the heating requirements of the silicon steel in the heating furnace, Large-scale factory production has extremely high use value and broad application market.

Description

technical field [0001] The invention relates to a chromium-based alloy pad, in particular to a chromium-based high-nitrogen alloy pad with high temperature resistance, oxidation resistance, corrosion resistance and creep resistance for a silicon steel high-temperature heating furnace. The invention also relates to a preparation method of the chromium-based high-nitrogen alloy pad. Background technique [0002] Walking beam heating furnace is the mainstream heating equipment for steel billet heating before rolling in steel rolling mills, and heat-resistant pads are key components for heating furnace. The heat-resistant block needs to work under the extremely high temperature of 1200 ℃ ~ 1350 ℃ and the harsh conditions of strong oxidation and vulcanization, and plays the role of supporting and transferring the heated billet. [0003] The temperature in the silicon steel high-temperature heating furnace can reach 1400°C. At this temperature, the heat-resistant block made of tr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C27/06C22C1/02B22C9/04B22C9/22C21D9/70
CPCC22C27/06C22C1/02B22C9/04B22C9/22C21D9/0006C21D9/70
Inventor 王楠马志军林毓云成华
Owner 烟台新钢联冶金科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap