HRB400E ordinary-speed hot-rolled ribbed steel bar with tensile strength of 700 Mpa or above

A hot-rolled ribbed steel bar, tensile strength technology, applied in the direction of metal rolling, temperature control, etc., can solve the problems of low tensile strength, low strength-to-yield ratio, etc., and achieve the effect of excellent seismic performance

Active Publication Date: 2022-07-08
GUANGXI LIUGANG HUACHUANG TECH R & D CO LTD +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention provides a HRB400E ordinary-speed hot-rolled ribbed steel bar with a tensile strength above 700Mpa to solve the problems of the existing ordinary-speed (non-high-bar) HRB400E seismic steel bar with low tensile strength and low yield ratio

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • HRB400E ordinary-speed hot-rolled ribbed steel bar with tensile strength of 700 Mpa or above
  • HRB400E ordinary-speed hot-rolled ribbed steel bar with tensile strength of 700 Mpa or above
  • HRB400E ordinary-speed hot-rolled ribbed steel bar with tensile strength of 700 Mpa or above

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] In order to have a clearer understanding of the technical features, objects and effects of the present invention, the present invention will now be described.

[0022] This application is suitable for ordinary bars, and the finish rolling speed is relatively slow. According to different specifications, the finish rolling speed (the exit speed of the finishing mill in hot tandem rolling) is only 1 / 3 to 1 / 2 of that of high-speed bars. At the same time, due to different production lines, more alloys need to be added to achieve the same performance, and more specifications are produced than high-speed bars.

[0023] (1) Composition design: increase the content of Si and Mn in the steel and add V element to combine with N in the steel to increase the strength, control the N element in the steel within a reasonable range, so that most of the N is combined with V to reduce the free N in the steel . When B element is added, since most of N in steel combines with V to produce c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
strength to yield ratioaaaaaaaaaa
Login to View More

Abstract

The invention provides an HRB400E ordinary speed hot rolling ribbed steel bar with the tensile strength of 700 Mpa or above. The HRB400E ordinary speed hot rolling ribbed steel bar comprises the following components in percentage by weight: 0.19%-0.25% of C, 0.60%-0.80% of Si, 1.45%-1.60% of Mn, less than or equal to 0.040% of P, less than or equal to 0.035% of S, 0.065%-0.10% of V, 0.010%-0.022% of Nb, 0.008%-0.020% of N and 0.0020%-0.0050% of B. By means of the method, the tensile strength of the HRB400E straight hot-rolled ribbed steel bar with the specification of phi 10-40 mm can be improved to 700 Mpa or above, the yield ratio R degree m / R degree eL is larger than or equal to 1.45, and a hot-rolled ribbed steel bar product with the anti-seismic property better than that of the conventional HRB400E is obtained.

Description

[0001] The present invention is: application date: June 10, 2021, application number: 2021106484836, name of invention: HRB400E general-speed hot-rolled ribbed steel bar with tensile strength above 700Mpa and its production method, a divisional application. technical field [0002] The invention belongs to the field of steel production and manufacture, and relates to a common HRB400E hot-rolled ribbed steel bar with a tensile strength of over 700 Mpa or a normal-speed HRB400E hot-rolled ribbed steel bar with a tensile strength of over 700 Mpa. Background technique [0003] HRB400E seismic steel bars are widely used due to their high strength and good seismic performance. GB / T 1499.2-2018 "Steel for Reinforced Concrete Part 2: Hot-Rolled Ribbed Steel Bars" has plastic indexes for HRB400E seismic steel bars (such as: maximum total force Elongation A gt , strong bending ratio R° m / R° eL , R° eL / R eL and other indicators) have clear requirements. The tensile strength of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/12C22C33/04C21D8/08B21B1/16B21B37/74
CPCC22C38/02C22C38/04C22C38/12C22C38/001C22C38/002C22C33/04C21D8/065C21D8/08B21B37/74C21D2211/002B21B1/163
Inventor 钱学海李宗强陈学良李西德文震何维肖娟蒙曰睿赵贤平廖耀俊温小园
Owner GUANGXI LIUGANG HUACHUANG TECH R & D CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com