A kind of polyolefin encapsulation adhesive film for photovoltaic

Abstract

Provided is a photovoltaic polyolefin encapsulating adhesive film. A stabilizer is added to the encapsulating adhesive film. The encapsulating adhesive film comprises, by mass parts, 100 parts of olefin copolymer, 0.1-3 parts of crosslinking agent, 0.1-3 parts of auxiliary crosslinking agent, 0.05-2 parts of anti-aging agent, 0.05-2 parts of silane coupling agent, and 0.05-4 parts of stabilizer. According to the photovoltaic polyolefin encapsulating adhesive film, when an assembly is laminated, a long-chain alkane or a long-chain siloxane protective layer is formed at the interface between glass and the polyolefin encapsulating adhesive film, thereby improving the hydrophobicity of the glass; the chance of direct contact of moisture with the glass is significantly reduced, thereby reducingthe salting out of the glass in the assembly hygrothermal aging process, the pH of the interface between the glass and the polyolefin encapsulating adhesive film is maintained between 7 and 11, and the adhesion between the polyolefin encapsulating adhesive film and the glass is maintained.

Description

Technical field

[0001] The invention belongs to the field of photovoltaic new energy materials, and specifically relates to a polyolefin encapsulating film for photovoltaics. Background technique

[0002] The packaging material of solar cell modules can provide protection for solar cell modules. Currently, the widely used packaging material is ethylene-vinyl acetate copolymer (EVA). In a long-term high temperature and high humidity environment, the EVA film is easily hydrolyzed and releases acetic acid corrosion. The circuit causes the component resistance to increase and the power generation to decrease; at the same time, acetic acid is also one of the causes of snail patterns. Solar cell modules have been used in high-voltage environments for a long time. Due to the insufficient insulation of the EVA film, wet leakage current channels are easily generated between the EVA film, the back sheet, the glass and the frame, and a large amount of charge is accumulated on the surface of...

Examples

Embodiment 1

[0044] Ethylene-1-octene random copolymer (Dow Chemical ENGAGE 8137) 100g, in which 0.1g tert-butylperoxycarbonate-2-ethylhexyl was added as a crosslinking agent, 0.1g trimethylolpropane trimethyl Base acrylate as a crosslinking agent, 2g of anti-aging agent (containing 0.8g of 2,2'-dihydroxy-4-methoxybenzophenone as a UV absorber, 0.6g of Lowilite-62 and Lowilite- 94 weight ratio 1:1 mixture as light stabilizer, 0.2g of tetra[methyl-β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate]pentaerythritol ester and 0.1g of tri (2,4-Di-tert-butylphenyl) phosphite as an antioxidant, 0.2g of nano-magnesium hydroxide as an acid absorbent, 0.1gMgAl(CO 3 )(OH)·nH 2 O as a metal ion trapping agent), 0.05g γ-(methacryloxy)propyltrimethoxysilane as a silane coupling agent, 4g hydrogenated C5 petroleum resin (Puyang Kairuide Petroleum Resin Co., Ltd. BT100, softening point 90-100°C) as a stabilizer. The uniformly mixed materials are added to the melt-extrusion casting machine for extrusion, and ...

Embodiment 2

[0046] Propylene-ethylene random copolymer (Dow Chemical VERSIFY 3401) 100g, in which 2.5g tert-butylperoxycarbonate-2-ethylhexyl ester is added as a crosslinking agent, and 0.5g pentaerythritol tetramethacrylate is used as a crosslinking aid Coupling agent, 0.05g anti-aging agent (containing 0.05 parts of Lowilite-62 and Lowilite-94 weight ratio 1:1 mixture as light stabilizer), 10g silane grafted POE, 0.05 parts of γ-(methacryloyloxy) ) Propyl trimethoxy silane is used as a silane coupling agent, and 0.7 g of n-octyl triethoxy silane is used as a stabilizer. The uniformly mixed materials are added to the melt-extrusion casting machine for extrusion, and the temperature is controlled at 100°C. The extrudate is cast, cooled, drawn, and crimped to obtain a polyolefin encapsulating film with a thickness of 0.45 mm.

Embodiment 3

[0048] Propylene-ethylene random copolymer (ExxonMobil Vistamaxx 6202FL) 100g, in which 2g tetracosyl peroxydicarbonate was added as a crosslinking agent, 3g 1,3,5-triallyl-s-triazine- 2,4,6-triketone is used as a crosslinking agent, 1g of anti-aging agent (0.1g of Lowilite-62 and Lowilite-94 weight ratio 1:1 mixture as light stabilizer, 0.2g of tetra[methyl- A mixture of β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester and 0.1 g of tris(2,4-di-tert-butylphenyl) phosphite as an antioxidant , 0.3g of nano-magnesium hydroxide as acid absorbent, 0.3gMgAl(CO 3 )(OH)·nH 2 O is used as a metal ion trap), 1 g of vinyl ethoxysilane is used as a silane coupling agent, and 0.5 g of paraffin wax (Honeywell AC1702, softening point 90°C) is used as a stabilizer. The uniformly mixed materials are added to the melt extrusion casting machine for extrusion, the temperature is controlled at 100°C, and the extrudate is cast, cooled, hauled, and crimped to obtain a polyolefi...

Technical field

[0001] The invention belongs to the field of photovoltaic new energy materials, and specifically relates to a polyolefin encapsulating film for photovoltaics. Background technique

[0002] The packaging material of solar cell modules can provide protection for solar cell modules. Currently, the widely used packaging material is ethylene-vinyl acetate copolymer (EVA). In a long-term high temperature and high humidity environment, the EVA film is easily hydrolyzed and releases acetic acid corrosion. The circuit causes the component resistance to increase and the power generation to decrease; at the same time, acetic acid is also one of the causes of snail patterns. Solar cell modules have been used in high-voltage environments for a long time. Due to the insufficient insulation of the EVA film, wet leakage current channels are easily generated between the EVA film, the back sheet, the glass and the frame, and a large amount of charge is accumulated on the surface of...

Examples

Embodiment 1

[0044] Ethylene-1-octene random copolymer (Dow Chemical ENGAGE 8137) 100g, in which 0.1g tert-butylperoxycarbonate-2-ethylhexyl was added as a crosslinking agent, 0.1g trimethylolpropane trimethyl Base acrylate as a crosslinking agent, 2g of anti-aging agent (containing 0.8g of 2,2'-dihydroxy-4-methoxybenzophenone as a UV absorber, 0.6g of Lowilite-62 and Lowilite- 94 weight ratio 1:1 mixture as light stabilizer, 0.2g of tetra[methyl-β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate]pentaerythritol ester and 0.1g of tri (2,4-Di-tert-butylphenyl) phosphite as an antioxidant, 0.2g of nano-magnesium hydroxide as an acid absorbent, 0.1gMgAl(CO 3 )(OH)·nH 2 O as a metal ion trapping agent), 0.05g γ-(methacryloxy)propyltrimethoxysilane as a silane coupling agent, 4g hydrogenated C5 petroleum resin (Puyang Kairuide Petroleum Resin Co., Ltd. BT100, softening point 90-100°C) as a stabilizer. The uniformly mixed materials are added to the melt-extrusion casting machine for extrusion, and ...

Embodiment 2

[0046] Propylene-ethylene random copolymer (Dow Chemical VERSIFY 3401) 100g, in which 2.5g tert-butylperoxycarbonate-2-ethylhexyl ester is added as a crosslinking agent, and 0.5g pentaerythritol tetramethacrylate is used as a crosslinking aid Coupling agent, 0.05g anti-aging agent (containing 0.05 parts of Lowilite-62 and Lowilite-94 weight ratio 1:1 mixture as light stabilizer), 10g silane grafted POE, 0.05 parts of γ-(methacryloyloxy) ) Propyl trimethoxy silane is used as a silane coupling agent, and 0.7 g of n-octyl triethoxy silane is used as a stabilizer. The uniformly mixed materials are added to the melt-extrusion casting machine for extrusion, and the temperature is controlled at 100°C. The extrudate is cast, cooled, drawn, and crimped to obtain a polyolefin encapsulating film with a thickness of 0.45 mm.

Embodiment 3

[0048] Propylene-ethylene random copolymer (ExxonMobil Vistamaxx 6202FL) 100g, in which 2g tetracosyl peroxydicarbonate was added as a crosslinking agent, 3g 1,3,5-triallyl-s-triazine- 2,4,6-triketone is used as a crosslinking agent, 1g of anti-aging agent (0.1g of Lowilite-62 and Lowilite-94 weight ratio 1:1 mixture as light stabilizer, 0.2g of tetra[methyl- A mixture of β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester and 0.1 g of tris(2,4-di-tert-butylphenyl) phosphite as an antioxidant , 0.3g of nano-magnesium hydroxide as acid absorbent, 0.3gMgAl(CO 3 )(OH)·nH 2 O is used as a metal ion trap), 1 g of vinyl ethoxysilane is used as a silane coupling agent, and 0.5 g of paraffin wax (Honeywell AC1702, softening point 90°C) is used as a stabilizer. The uniformly mixed materials are added to the melt extrusion casting machine for extrusion, the temperature is controlled at 100°C, and the extrudate is cast, cooled, hauled, and crimped to obtain a polyolefi...

Images