Chromatic bituminous cement and preparation method and application thereof

Abstract

The invention discloses a coloured asphalt cement, preparing method and application, which is characterized by the following: including 1-5% FT ceresin wax; introducing little FT ceresin wax to decrease the processing temperature; decreasing the odor of cementing agent; making the coloured asphalt cement with better high temperature stability.

Description

technical field

[0001] The invention relates to an asphalt binder, in particular to a binder for colored asphalt pavement. Background technique

[0002] Colored asphalt pavement has been widely used in highways, bicycle lanes, sidewalks, bus lanes, pedestrian areas, squares and home driveways.

[0003] The mechanical properties and rheological properties of colored asphalt binder are the same as those of general road heavy traffic asphalt. The main principle of colored asphalt binder pavement is to use colored asphalt binder and add various pigments to make it have various required colors. At the same time, by using colored stones or light-colored stones, it can have a longer-lasting color effect. A good colored asphalt binder should meet the following requirements:

[0004] Colored asphalt binder has good performance and should try to meet the requirements of heavy traffic asphalt or even modified asphalt; good high temperature stability; good water damage resistance; good...

Examples

Embodiment 1～6

[0026] Raw materials used:

[0027] A lubricating oil refined extraction oil, viscosity at 40°C: 3.5Pa.S, flash point: 235°C, aromatic content: 68wt%, density at 15°C: 0.98g / cm3

[0028] B Petroleum Resin, produced by Korea Kolon Company, the brand is P-140, the softening point is 145°C, and the average molecular weight (GPC method) is 2200

[0029] CFT paraffin, produced by Schumann Sasol, Germany, trade name: Sasobit

[0030] D styrene butadiene triblock copolymer (SBS), produced by Baling Petrochemical, trade name: YH-791H, styrene / butadiene ratio 30 / 70, linear structure

[0031] E ethylene vinyl acetate resin (EVA), produced by Sumitomo Chemical Co., Ltd., Japan, trade name: EVATATER-5011, VA content: 41wt%, MI: 60g / 10min

[0032] Heat the extracted lubricating oil to 175°C, then add petroleum resin, SBS, EVA and FT paraffin, and stir with a stirrer at a speed of 200 rpm for 60 minutes to prepare the finished colored asphalt binder. The specific composition ratio (perce...

Embodiment 7

[0037] Weight percentage (%) of ore materials passing through the following sieve size (mm)

[0038] composition ratio

[0039] It can be seen from the above table that the porosity of the mixture formed under the same conditions by adding FT paraffin to the colored asphalt binder decreases, indicating that its construction performance is improved. At the same time, the dynamic stability of the colored asphalt mixture also increases with the increase of FT paraffin Gradually increasing, indicating that its high temperature stability has been improved.

technical field

[0001] The invention relates to an asphalt binder, in particular to a binder for colored asphalt pavement. Background technique

[0002] Colored asphalt pavement has been widely used in highways, bicycle lanes, sidewalks, bus lanes, pedestrian areas, squares and home driveways.

[0003] The mechanical properties and rheological properties of colored asphalt binder are the same as those of general road heavy traffic asphalt. The main principle of colored asphalt binder pavement is to use colored asphalt binder and add various pigments to make it have various required colors. At the same time, by using colored stones or light-colored stones, it can have a longer-lasting color effect. A good colored asphalt binder should meet the following requirements:

[0004] Colored asphalt binder has good performance and should try to meet the requirements of heavy traffic asphalt or even modified asphalt; good high temperature stability; good water damage resistance; good...

Examples

Embodiment 1～6

[0026] Raw materials used:

[0027] A lubricating oil refined extraction oil, viscosity at 40°C: 3.5Pa.S, flash point: 235°C, aromatic content: 68wt%, density at 15°C: 0.98g / cm3

[0028] B Petroleum Resin, produced by Korea Kolon Company, the brand is P-140, the softening point is 145°C, and the average molecular weight (GPC method) is 2200

[0029] CFT paraffin, produced by Schumann Sasol, Germany, trade name: Sasobit

[0030] D styrene butadiene triblock copolymer (SBS), produced by Baling Petrochemical, trade name: YH-791H, styrene / butadiene ratio 30 / 70, linear structure

[0031] E ethylene vinyl acetate resin (EVA), produced by Sumitomo Chemical Co., Ltd., Japan, trade name: EVATATER-5011, VA content: 41wt%, MI: 60g / 10min

[0032] Heat the extracted lubricating oil to 175°C, then add petroleum resin, SBS, EVA and FT paraffin, and stir with a stirrer at a speed of 200 rpm for 60 minutes to prepare the finished colored asphalt binder. The specific composition ratio (perce...

Embodiment 7

[0037] Weight percentage (%) of ore materials passing through the following sieve size (mm)

[0038] composition ratio

[0039] It can be seen from the above table that the porosity of the mixture formed under the same conditions by adding FT paraffin to the colored asphalt binder decreases, indicating that its construction performance is improved. At the same time, the dynamic stability of the colored asphalt mixture also increases with the increase of FT paraffin Gradually increasing, indicating that its high temperature stability has been improved.