Preparation of nano SiO2 enhanced toughened PET composite material for plastic-steel baling belt
A technology of plastic-steel packing belt and composite material, which is applied in the field of preparation of nano-material modified polyethylene terephthalate, can solve the problems of poor dispersion and inconspicuous modification effect, achieve simple process and solve relative problems. Capacitive issues, effects of small particle size
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0027] Take 750g of dried PET pellets, stir them in a molten state, turn on the ultrasonic wave, add 7.5g of coupling agent KH550, mix for 10 minutes, then add 90g of gas phase SiO 2 Mix for 30 minutes, then add 80g gas phase SiO in two times 2 , every 30 minutes. Continue to sonicate and stir for 1 hour, and the material is cooled and granulated to obtain a modified masterbatch, wherein SiO 2 The content is 25% (referred to as PET-25)
Embodiment 2
[0029] Take 700g of dried PET pellets, stir them in a molten state, turn on the ultrasonic wave, add 9.0g of coupling agent KH550, mix for 10 minutes, then add 100g of gas phase SiO 2 Mix for 30 minutes, then add 100g gas phase SiO in two times 2 , every 30 minutes. Continue to sonicate and stir for 1 hour, and the material is cooled and granulated to obtain a modified masterbatch, wherein SiO 2 The content is 30% (referred to as PET-30)
Embodiment 3
[0031] Take 650g of dried PET pellets, stir them in a molten state, turn on the ultrasonic wave, add 10.5g of coupling agent KH550, mix for 10 minutes, then add 130g of gas phase SiO 2 Mix for 30 minutes, then add 110g gas phase SiO in two times 2 , every 30 minutes. Continue to sonicate and stir for 1 hour, and the material is cooled and granulated to obtain a modified masterbatch, wherein SiO 2 The content is 35% (referred to as PET-35)
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
melting point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com