Preparation method of heat-resistant polyphenylene sulfide fiber

A polyphenylene sulfide fiber, polyphenylene sulfide technology, applied in the direction of fiber type, fiber treatment, fiber chemical characteristics, etc., can solve the problems of filter bag strength loss, fiber oxidation, reduction of dust removal effect and service life, etc. Reasonable, accurate and detailed results

Inactive Publication Date: 2011-10-19
TAIYUAN UNIV OF TECH
View PDF4 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, it is found in use that due to the macromolecular structure of PPS fibers, the use temperature is higher than 180°C, and the oxidation of the fibers is serious, resulting in

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of heat-resistant polyphenylene sulfide fiber
  • Preparation method of heat-resistant polyphenylene sulfide fiber
  • Preparation method of heat-resistant polyphenylene sulfide fiber

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0079] The present invention will be further explained below in conjunction with the drawings:

[0080] figure 1 Shown is the working state diagram of the twin-screw extruder. The positions of each part should be correct, proportioning according to the quantity, and operation in order.

[0081] The amount of chemical materials used in the preparation is determined according to a preset range, with grams, milliliters, and centimeters as the unit of measurement.

[0082] The preparation of silica + polyphenylene sulfide masterbatch is carried out on a twin-screw extruder, which is completed under heating, electric metering feeding, twin-screw extrusion, water cooling, and pelletizing by a pelletizer; The twin screw 15 is placed on the upper part of the base 25 of the extruder 26. The twin screw 15 is engaged with left and right, and the two screws are engaged with the right rotation. On the left of the twin screw 15 is the screw motor 14; Main feed box 10 and side feed box 11, main fe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Fiber denieraaaaaaaaaa
Breaking strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of heat-resistant polyphenylene sulfide fiber, comprising the following steps: aiming at the demand on high-performance industrial fabric, adding silica to a polyphenylene sulfide material, preparing masterbatch, extruding by double screws to form strips, dicing, drying in vacuum, extruding and spinning by a single screw, cooling, applying oil to an oil roller, thermally sizing, and winding to form a wire barrel to finally obtain heat-resistant silica and polyphenylene sulfide fiber, namely, SiO2/PPS fiber, wherein the fiber is white long silk, the fineness is 400dtex, the breaking strength is 3.75 cN/dtex, the heat resistance temperature is 230 DEG C, and the silk has stable chemical and physical performances; the fiber can be used for manufacturing heat-resistant, corrosion-resisting dedusting filter bags and the like, which has high demand on the breaking strength; the preparation method has advanced and remarkable technology and accurate and detailed quantity parameters, and is capable of performing large-scale industrial production; and the preparation method is a very ideal preparation method of the heat-resistant polyphenylene sulfide fiber.

Description

technical field [0001] The invention relates to a preparation method of heat-resistant polyphenylene sulfide fiber, belonging to the technical field of high-performance chemical fiber manufacture and application. technical background [0002] Polyphenylene sulfide fiber, referred to as PPS fiber, is a chemical fiber with excellent performance. It has good chemical corrosion resistance, flame retardancy, insulation, temperature resistance, dimensional stability and textile processability, and is widely used. In metallurgy, building materials, electric power, chemical industry and other industries, it is the preferred textile material for steel mills, cement plants, thermal power plants, waste incineration stations, and high-temperature dust removal filter bags. [0003] However, it is found in use that due to the macromolecular structure of PPS fibers, the use temperature is higher than 180°C, and the oxidation of the fibers is serious, resulting in a loss of 30%-55% of the s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01F6/94D01D1/04D01D5/088D01D5/12D01D10/02D01D10/06D06M15/53D06M13/256D06M13/224D06M101/30
Inventor 张蕊萍牛梅盛向前戴晋明杨晗高立斌李世焕
Owner TAIYUAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap