Method for manufacturing gold-inlaid relief sculpture artistic porcelain

Abstract

The invention provides a method for manufacturing gold-inlaid relief sculpture artistic porcelain. The method sequentially comprises the following steps of: 1) designing and drawing decorating patterns; 2) manufacturing a corrosion-resistance mask; 3) repasting the corrosion-resistance mask; 4) performing abrasion treatment; 5) applying gold; and 6) burning, wherein the step of performing the abrasion treatment is to abrade porcelain adhered with an abrasion mask with relief sculpture decorating patterns on an abrader; the step of applying gold is to apply 12 percent of gold paste to a corresponding region of the cleaned and dried porcelain which is subjected to the abrasion treatment by using a writing brush, and the gold-inlaid relief sculpture porcelain decorating patterns are predesigned in the region; and the step of burning is to flat place the porcelain in a roller table type continuous operation high-temperature rapid decoration firing kiln for firing. According to the manufacturing method provided by the invention, body health of operators and ecological environment are prevented from damages, a relief sculpture layer is over 100microns thick and has a remarkable stereoscopic and spatial impression. Furthermore, the profile of the relief sculpture texture patterns is bright, clean, fine and smooth, the edges of the patterns are sharp and steep without burrs, and gold is inlaid in the relief sculpture to show a sumptuous and elegant impression.

Description

technical field [0001] The invention relates to porcelain making, in particular to a method for making gold-embossed relief art porcelain. Background technique [0002] The decorative flower surface of gold-inlaid embossed art porcelain is magnificent, with a sense of three-dimensional space and strong artistic expression, and has high practical, ornamental and collection values. The existing method of utilizing the "subtractive relief" process to make gold-inlaid relief art porcelain is the hydrofluoric acid corrosion method. This method has the following steps in turn: 1) designing and drawing decorative patterns; The negative text of the decorative pattern, that is, the pattern is concave on the printing surface, and the resist mask is made: 3) the resist mask is transferred to the surface of the porcelain to be processed; The porcelain surface of the etching mask corrodes a surface layer and sinks, forming a relief-like convex-concave pattern with the porcelain surface ...

AI Technical Summary

Problems solved by technology

The defect of this method is: 1) hydrofluoric acid has poisonous effect to human body, affects the health of operator, and corrodes waste water and pollutes ecological environment; The depth of the convex-concave pattern is at most 30 microns, the sense of three-dimensionality and space is not strong, and the edge of the pattern is not too steep and sharp, forming rough edges, which requires subsequent processing and affects the improvement of production efficiency