Rare earth aluminum alloy conductor and preparation method thereof

An aluminum alloy wire, aluminum alloy technology, applied in metal/alloy conductors, cable/conductor manufacturing, electrical components, etc., can solve the problems of insufficient continuous development, easy overload and heat generation, and potential safety hazards, saving time and raw material costs. , Reduce the operation steps, the effect of easy removal of impurities

Active Publication Date: 2013-03-27
ANHUI PACIFIC CABLE CO LTD
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] (1) Poor mechanical strength and easy to break;
[0004] (2) It is easy to creep and needs to be tightened frequently;
[0005] (3) It is easy to overload and generate heat; there are potential safety hazards;
[0006] (4) The problem of copper-aluminum transition connection is not well solved
A large number of rese

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rare earth aluminum alloy conductor and preparation method thereof
  • Rare earth aluminum alloy conductor and preparation method thereof
  • Rare earth aluminum alloy conductor and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-7

[0107] Melting: According to the formula in Table 1, first melt aluminum and aluminum-iron alloy at 720-730°C, then heat up to 780-790°C and add zinc, antimony, tin, copper, strontium and tellurium in the form of master alloy; fully mix Finally, add light rare earth in the form of master alloy at 760-770°C; after fully mixing, add medium rare earth in the form of master alloy at 730-740°C; after fully mixing, add in the form of master alloy at 780-790°C Heavy rare earth; when the master alloy is added, it should be fed in different positions of the aluminum liquid as much as possible, so that the composition of the master alloy can be more quickly and evenly dispersed in the aluminum liquid; after being fully mixed, it is refined at 760-770°C refining agent, the components of the refining agent are: sodium nitrate 60wt%, graphite powder 10wt%, cryolite 30wt% (each component meets: sodium nitrate 50-70wt%, graphite powder 5-15wt%, cryolite 20wt% -40wt% can be used). The weight...

Embodiment 8

[0119] Prepare the rare earth aluminum alloy stranded conductor, the steps are as follows:

[0120] a) Stranding: using the aluminum alloy wire obtained in Example 3, twisting through a concentric layer stranding process;

[0121] b) annealing: performing annealing treatment on the aluminum alloy stranded wire obtained in step a;

[0122] The annealing method is a three-stage annealing, and the three-stage annealing specifically refers to placing the aluminum alloy twisted coil obtained in step 1 in an annealing furnace, and the annealing furnace is divided into upper, lower, Middle and lower temperature zones, the heating temperature range of the upper temperature zone is 340-360°C, the temperature range of the middle temperature zone is 350-370°C, and the temperature range of the lower temperature zone is 360-370°C, The annealing time is 4-10h.

[0123] The obtained stranded conductor fill factor is ≥92%. Visually observe the cross-section of the stranded conductor, the s...

Embodiment 9

[0125] The formula in Example 3 was used to prepare round monofilament wires respectively, and the round monofilament wires were extruded into special-shaped aluminum alloy monofilament wires through crimping holes. The cross-section of the special-shaped aluminum alloy monofilament wire is as follows figure 1 Shown is a special-shaped isosceles trapezoid, the long base of the special-shaped isosceles trapezoid is an arc 1, and the center of the circle coincides with the intersection point 2 of the extension line of the waist line of the special-shaped isosceles trapezoid. The four corners of the special-shaped isosceles trapezoid are all rounded.

[0126] In the special-shaped aluminum alloy stranded conductor, the number n of special-shaped aluminum alloy monofilament wires used in each layer is:

[0127]

[0128] The θ simultaneously satisfies the formula:

[0129] 57 h R ≤ θ ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Arc radiusaaaaaaaaaa
Diameteraaaaaaaaaa
Outer radiusaaaaaaaaaa
Login to view more

Abstract

The invention provides a rare earth aluminum alloy conductor and a preparation method thereof. The rare earth aluminum alloy conductor comprises the following components in percentage by weight: 0.5-1% of Fe, 0.07-0.1% of Zn, 0.05-0.1% of Si, 0.02-0.04% of Sb, 0.02-0.05% of Sn, 0.15-0.30% of Cu, 0.01-0.02% of Sr, 0.01-0.03% of Te, 0.03-0.05% of rare earth and the balance of aluminum and inevitable impurities. The rare earth aluminum alloy conductor provided by the invention is excellent in electric property and can be used for producing a cable.

Description

technical field [0001] The invention relates to the field of aluminum alloy conductors, in particular to a rare earth aluminum alloy conductor and a preparation method thereof. Background technique [0002] In the 1970s, the global copper price rose rapidly, and "replacing copper with aluminum" became a technical policy generally followed by the electrical industry. Therefore, the trunk lines and branch lines of civil buildings all use pure aluminum cables. The disadvantages of pure aluminum conductors are mainly reflected in the following aspects: [0003] (1) Poor mechanical strength and easy to break; [0004] (2) It is easy to creep and needs to be tightened frequently; [0005] (3) It is easy to overload and generate heat; there are potential safety hazards; [0006] (4) The problem of copper-aluminum transition connection is not well solved. [0007] Alloy conductor is a new conductor material formed by adding rare earth, magnesium, copper, iron and other elements ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C21/00H01B1/02H01B13/00
Inventor 黄诚王业山王永海
Owner ANHUI PACIFIC CABLE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap