Odorless anti-formaldehyde environment-friendly internal wall latex paint and preparation method thereof

A latex paint and anti-formaldehyde technology, applied in latex paint, coatings, etc., can solve the problems of low visible light response, restrictions on popularization, low photon quantum efficiency, etc., and achieve the effect of purifying room air, improving living environment, and low VOC content

Active Publication Date: 2013-04-24
CHINA UNIV OF GEOSCIENCES (WUHAN) +1
View PDF4 Cites 115 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because titanium dioxide only absorbs ultraviolet light, it has a low response to visible light, and due to the recombination of photogenerated electrons and holes, the photon quantum efficiency is very low, which seriously restricts its large-scale promotion and use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Odorless anti-formaldehyde environment-friendly internal wall latex paint and preparation method thereof
  • Odorless anti-formaldehyde environment-friendly internal wall latex paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A formaldehyde-free environment-friendly interior latex paint, its components and contents (by weight percentage) are as follows: visible light-induced nano-titanium dioxide photocatalyst slurry 1%, odor-cleaning emulsion 20%, formaldehyde absorbent 1%, dispersant Dispersant 5027 2%, thickener Natrosol 250HBR 0.2%, wetting agent Wet 996 0.9%, defoamer Defoamer 154S 0.8%, film-forming aid Texanol 1.5%, antifreeze agent propylene glycol 1%, pigment and filler 40%, pH Value regulator AMP-95 0.17%, antiseptic and fungicide Kathon-LXE 0.08%, deionized water 31.35%.

[0028] The components and contents (by weight percentage) of the visible light-induced nano-titanium dioxide photocatalyst slurry are as follows: visible light-induced nano-titanium dioxide photocatalyst 30%, thickener Natrosol 250HBR 0.2%, dispersant Dispersant 5027 1%, wetting agent Wet 996 0.6%, deodorant styrene-acrylic emulsion RS-9981 15%, defoamer Defoamer 154S 0.2%, deionized water 53%.

[0029] The par...

Embodiment 2

[0040] A formaldehyde-free environment-friendly interior latex paint, its components and contents (by weight percentage) are as follows: visible light-induced nano-titanium dioxide photocatalyst slurry 15%, odor-cleaning emulsion 20%, formaldehyde absorbent 2%, dispersant Dispersant 5027 1%, thickener Natrosol 250HBR 0.2%, wetting agent Wet 996 0.7%, defoamer Defoamer 154S 0.4%, film-forming aid Texanol 1.5%, antifreeze agent propylene glycol 1%, pigment and filler 33%, pH Value regulator AMP-95 0.17%, antiseptic and fungicide Kathon-LXE 0.02%, deionized water 26.57%.

[0041] The components and contents (by weight percentage) of the visible light-induced nano-titanium dioxide photocatalyst slurry are as follows: visible light-induced nano-titanium dioxide photocatalyst 10%, thickener Natrosol 250HBR 0.2%, dispersant Dispersant 5027 1%, wetting agent Wet 996 0.6%, deodorant styrene-acrylic emulsion RS-9981 15%, defoamer Defoamer 154S 0.2%, deionized water 73%.

[0042] The pa...

Embodiment 3

[0053] A formaldehyde-free environment-friendly interior latex paint, its components and contents (by weight percentage) are as follows: visible light-induced nano-titanium dioxide photocatalyst slurry 3%, odor-cleaning emulsion 30%, formaldehyde absorbent 5%, dispersant Dispersant 5027 1%, thickener Natrosol 250HBR 0.4%, wetting agent Wet 996 0.5%, defoamer Defoamer 154S 0.4%, film-forming aid Texanol 1.5%, antifreeze agent propylene glycol 1%, pigment and filler 32%, pH Value regulator AMP-95 0.17%, antiseptic and fungicide Kathon-LXE 0.03%, deionized water 25%.

[0054] The components and contents (by weight percentage) of the visible light-induced nano-titanium dioxide photocatalyst slurry are as follows: visible light-induced nano-titanium dioxide photocatalyst 30%, thickener Natrosol 250HBR 0.2%, dispersant Dispersant 5027 1%, wetting agent Wet 996 0.6%, deodorant styrene-acrylic emulsion RS-9981 15%, defoamer Defoamer 154S 0.2%, deionized water 53%.

[0055] The partic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses an odorless anti-formaldehyde environment-friendly internal wall latex paint and a preparation method thereof. The odorless anti-formaldehyde environment-friendly internal wall latex paint is prepared from the following components in percentage by weight: 1-15% of visible light induced nano titanium dioxide photocatalyst slurry, 15-35% of odorless emulsion, 1-15% of formaldehyde absorbent, 0.5-2% of dispersing agent, 0.2-3% of thickening agent, 0.2-1% of wetting agent, 0.1-1% of defoaming agent, 0.5-5% of film-forming assistant, 0.2-3% of anti-freeze agent, 20-40% of pigment and filler, 0.1-1% of pH regulator, 0.01-0.1% of anticorrosive bactericide and 15-40% of deionized water. The invention adopts an IPS+odorless technique, and the visible light induced nano titanium dioxide photocatalyst and the formaldehyde absorbent are added, thereby achieving the optimal effect of removing formaldehyde and other harmful substances through physical adsorption and chemical decomposition. The invention can be widely used for decorative spraying of various internal walls and other constructions.

Description

technical field [0001] The invention relates to a paint and a preparation method thereof, in particular to a clean-odour, formaldehyde-resistant and environment-friendly interior wall latex paint and a preparation method thereof. Background technique [0002] With the development of the economy and the improvement of people's living standards, a variety of building decoration materials have entered homes and offices, and VOC (volatile organic compounds) has become an important substance that pollutes the indoor air environment. Among VOCs, formaldehyde is the most common pollutant. It is mainly released through the degradation of wood adhesives and plastics used in interior decoration, decorative materials, and furniture. It poses a huge threat to human health and has become the number one killer of human health. How to remove formaldehyde and other volatile organic compounds in indoor air has become the focus of attention. [0003] Interior wall latex paint is widely used ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D125/14C09D123/08C09D5/02C09D7/12
Inventor 程国娥柯汉忠孔维俊皮振邦周伟建谭俊峰李君荣李淑燕李腾飞郭全坚梁振霖
Owner CHINA UNIV OF GEOSCIENCES (WUHAN)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka