Preparation method and application of NH2-MIL-125 modified carbon paste electrode

A kind of NH2-MIL-125, 1. NH2-MIL-125 technology, applied in the preparation and application field of NH2-MIL-125 modified carbon paste electrode

Active Publication Date: 2014-05-07
德尚智能科技(江苏)有限公司
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the determination of Mn2+ content by photoelectrochem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of NH2-MIL-125 modified carbon paste electrode
  • Preparation method and application of NH2-MIL-125 modified carbon paste electrode

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] 1. Preparation of NH 2 - MIL-125 (Ti) modified carbon paste electrode:

[0020] Weigh 0.5g graphite powder and 0.025gNH 2 - The solid powder of MIL-125 is fully ground in a mortar. After obtaining a uniformly mixed powder, add 0.18mL of liquid paraffin to the mixture and continue grinding until a uniform carbon paste is obtained.

[0021] Then fill the carbon paste into the cavity of the adjustable carbon paste electrode to get NH 2 - MIL-125 modified carbon paste electrodes.

[0022] Since the NH used for the electrode 2 -The working surface of the MIL-125 modified carbon paste electrode is only the bare lower end surface, so after each use, just pass the rotating shaft in the chamber of the adjustable carbon paste electrode, and the previously used enriched in NH 2 - The enrichment on the lower end surface of the MIL-125 modified carbon paste electrode is removed, and a new working surface is exposed again for subsequent use.

[0023] 2. NH 2 -Application of MI...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method and application of an NH2-MIL-125 modified carbon paste electrode, relating to the technical field of electrochemical detection. The method comprises the following steps: grinding graphite powder, NH2-MIL-125 (Ti) solid powder and liquid paraffin into uniform carbon paste, and filling the carbon paste in an adjustable carbon paste electrode cavity body to obtain the NH2-MIL-125 modified carbon paste electrode. Under the irradiation of visible light, the cathodic stripping voltammetry detection of an oxidative product after photocatalytic oxidation of NH2-MIL-125 (Ti) on Mn<2+> is performed, and relatively good sensitivity and selectivity can be realized as a standard curve method is adopted. The NH2-MIL-125 modified carbon paste electrode is applied to detection of the Mn<2+> content, the detection result of the method is nearly the same as that of atomic absorption spectrometry, and a novel method for detecting the manganese ion content is formed.

Description

technical field [0001] The present invention relates to NH 2 - The application of MIL-125 (Ti), which also involves the field of electrochemical detection technology, specifically belongs to NH 2 - Application of MIL-125 modified carbon paste electrodes. Background technique [0002] Metal-Organic Frameworks (MOFs) materials are a new type of porous materials developed in recent years. Due to its porosity, pore adjustability, easy functionalization, special optical and electrical characteristics, etc., it has shown good applications in the fields of gas adsorption and separation, gas storage, organic catalysis, photoelectromagnetic materials, and chemical sensors. Application prospect. [0003] NH 2 -MIL-125 (Ti) is a coordination polymer with a stable structure connected by Ti-O structural units and 2-aminoterephthalate. The presence of Ti-O structural units in the material makes it photocatalytic Properties (Dan-Hardi M., Serre C., Frot T., Rozes L., Maurin G., Sanche...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G01N27/30G01N27/48
Inventor 胡效亚王艳娟金根娣徐琴李可鑫金党琴
Owner 德尚智能科技(江苏)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap