A high blowing rate ventilation brick and its manufacturing method

A manufacturing method and high blowing rate technology, applied in the field of refractory materials, can solve problems such as difficult distribution of micro-pore forming agents, difficulty in uniform dispersion of micro-pores, and reduction of material strength, etc., to achieve excellent volume stability and good ventilation effect Effect

Active Publication Date: 2016-03-02
PUYANG REFRACTORIES GRP CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the micropore forming agent is often difficult to distribute evenly, which makes it difficult to disperse the micropores evenly; on the other hand, the formed micropores have a low connectivity rate and are closed to each other, making it difficult to achieve a practical level of air permeability
If too much micropore forming agent is added, although the ventilation effect will be improved to a certain extent, the material strength will also be significantly reduced at the same time, and it is difficult to meet the use requirements of ventilation brick products.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high blowing rate ventilation brick and its manufacturing method
  • A high blowing rate ventilation brick and its manufacturing method
  • A high blowing rate ventilation brick and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0066] The present invention will be described in further detail below in conjunction with specific examples, but not as a limitation of the present invention.

[0067] The first group of embodiments (see table 1):

[0068] Table 1

[0069]

[0070] The manufacture method of air-permeable brick in embodiment 1 to embodiment 7, comprises the following steps:

[0071] The first step: prepare raw materials according to the high blowing rate permeable brick formula (Al in the rough corundum or the fine corundum in embodiment 1-embodiment 7 2 o 3 ≥95wt%, the rough corundum and the fine corundum are both tabular corundum, and in other embodiments can also be one or more of dense corundum, white corundum and brown corundum), and the raw materials are processed according to the national standard test;

[0072] The second step: batching and mixing process;

[0073] The third step: trapped material process;

[0074] The fourth step: mold assembly process;

[0075] The fifth s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to an air brick with a high blowing through rate and a manufacturing method thereof. The air brick is composed of the following components: coarse corundum with granularity greater than 0.5mm and smaller than or equal to 1 mm and mass fraction of 35-50%; fine corundum with granularity greater than 0 and smaller than or equal to 0.5 mm and mass fraction of 25-40%; alumina fine powder with granularity greater than 0.020 mm and smaller than or equal to 0.044 mm and mass fraction of 8-15%; alumina micro powder with granularity greater than 0 and smaller than or equal to 0.020 mm and mass fraction of 5-10%. The manufacturing method comprises the procedures of mixed milling, material kneading and press forming, and further comprises the procedures of roasting, high temperature sintering, flow detecting, steel shell packaging and the like. According to the air brick provided by the invention, the particle size distribution and the machine pressing pressure are controlled, and uniformly distributed and mutually communicated micropores are formed in a brick body after high temperature sintering so as to achieve the permeability of an air brick body material.

Description

technical field [0001] The invention relates to a ventilating brick for metallurgical refining, in particular to a ventilating brick with a high blowing rate and a manufacturing method thereof, belonging to the field of refractory materials. Background technique [0002] With the development of industrial technology, social demand puts forward higher requirements on steel quality and quality, forcing steel companies to continuously upgrade smelting technology. Therefore, the refining ratio and difficulty of steel smelting are constantly increasing, which affects the stability and smoothness of the smelting process. Higher requirements have also been raised. Moreover, since 2008, iron and steel enterprises have entered the era of meager profits as a whole. In 2011, the profit margin was only 2.4%. This efficiency enhancement project has put a heavy pressure on the price of refractory materials. In this context, customers put forward higher requirements for functional refrac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/66
Inventor 吴晓童则明刘国涛李伟李彦明郑日徐张厚兴刘百宽孙荣海刘国威
Owner PUYANG REFRACTORIES GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products