Furnace-transmuted archaized brick and production method thereof

A production method and technology of antique bricks, applied in covering/lining, construction, building construction, etc., can solve the problems of singleness and insufficient layers, and achieve the effect of strong metal corrosion

Active Publication Date: 2015-03-11
HANGZHOU NABEL CERAMIC
View PDF14 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problem that the existing antique brick decoration methods are relatively single and the layers are not rich enough, the present invention provides a production method of kiln-transformed antique brick

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Furnace-transmuted archaized brick and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] 1) Preparing brick adobes: Prepare porcelain antique brick adobe powder according to conventional methods, and press molds to prepare adobes for use;

[0029] 2) Preparation of metal dry particles: according to the conventional glass frit preparation process, select lithium-containing minerals, quartz and chemical raw materials, and obtain The composition range is SiO2 25%, Al2O3 6%, Fe2O3 7%, Li2O 1%, B2O3 4%, ZnO 35%, PbO 15%, the rest is clarifying agent and impurities, and the particle size of moisture ≤ 0.5% is 100~200 Purpose frit, spare;

[0030] 3) Preparation of metal cloud: Based on the dry metal particles prepared in step 2), introduce an appropriate amount of suspending agent and debonding agent, add water and grind, control the fineness of the glaze slurry to be less than 0.05% on a 325 mesh sieve, and obtain a density of 1.3g / cm3 clouds of metal;

[0031] 4) Spreading clouds: spread metal clouds on the adobe prepared in step 1) by spraying glaze, and the...

Embodiment 2

[0038] 1) Preparing brick adobes: Prepare porcelain antique brick adobe powder according to conventional methods, and press molds to prepare adobes for use;

[0039]2) Preparation of metal dry particles: according to the conventional glass frit preparation process, select lithium-containing minerals, quartz and chemical raw materials, and obtain The composition range is SiO2 30%, Al2O3 3%, Fe2O3 5%, Li2O 2%, B2O3 5%, ZnO 28%, PbO 18%, the rest is clarifying agent and impurities, and the particle size of moisture ≤ 0.5% is 100~ 200 mesh frit, spare;

[0040] 3) Preparation of metal cloud: Based on the dry metal particles prepared in step 2), introduce an appropriate amount of suspending agent and debonding agent, add water and grind, control the fineness of the glaze slurry to be less than 0.05% on a 325 mesh sieve, and obtain a density of 1.4g / cm3 clouds of metal;

[0041] 4) Spreading clouds: spread metal clouds on the adobe prepared in step 1) by spraying glaze, and the am...

Embodiment 3

[0049] 1) Preparing brick adobes: Prepare porcelain antique brick adobe powder according to conventional methods, and press molds to prepare adobes for use;

[0050] 2) Preparation of metal dry particles: According to the conventional glass frit preparation process, select lithium-containing minerals, quartz and chemical raw materials, and obtain The composition range is SiO2 30%, Al2O3 6%, Fe2O3 9%, Li2O 1.5%, B2O3 2.5%, ZnO 26%, PbO 14%, the rest is clarifying agent and impurities, and the particle size of moisture <0.5% is 100~ 200 mesh frit, spare;

[0051] 3) Preparation of metal cloud: Based on the dry metal particles prepared in step 2), introduce an appropriate amount of suspending agent and debonding agent, add water and grind, control the fineness of the glaze slurry to be less than 0.05% on a 325 mesh sieve, and obtain a density of 1.1g / cm3 clouds of metal;

[0052] 4) Spreading clouds: spread metallic clouds on the adobe prepared in step 1) by throwing glaze, and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a furnace-transmuted archaized brick and a production method thereof. A furnace transmutation effect and an archaized brick are ingeniously combined in a decoration effect, matte glazes of multiple archaized color systems such as yellow, coffee and dark red are printed on the surface of a ceramic tile in a large scale to form the peculiar primitive charm and classical style of the archaized brick, dry metal particles matched with a mold pattern are printed on the surface of the ceramic tile, and a complex color developing effect is achieved by oxide in the dry metal particles under the influence of glaze bodies and a firing atmosphere at high temperature, so that the produced archaized brick is endowed with impressive metal corrosion appearance and bitterness, and is extremely decorative and artistic, the natural and imposing classical style caters to the mindset of admiring and returning to the nature of modern people, and the problems of undiversified decoration methods and undiversified layers of the archaized brick are solved.

Description

technical field [0001] The invention relates to the technical field of production methods of architectural ceramic antique bricks, in particular to a kiln-transformed antique brick and a production method thereof. Background technique [0002] Antique tiles belong to ordinary tiles, imitating the previous styles, using artificial methods such as acid leaching, high-pressure cooking, and printing antique glazes to make them old, and they are essentially glazed tiles. The body is mainly made of porcelain, and it can also be made of stoneware, fine stoneware and stoneware; the glaze is mainly matte, and the main colors are yellow, coffee, dark red, earthy, gray, gray and black. The cultural heritage and historical connotation contained in the antique brick make it the mainstream ceramic tile product in the European and American markets, and it has also developed rapidly in China. However, the decoration techniques of antique bricks are relatively single and the layers are not ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04F13/14C04B41/86C04B41/88
Inventor 徐海航朱爱余张晓芳田祖鸿王勇
Owner HANGZHOU NABEL CERAMIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com