Preparation method of modified hypoeutectic aluminium alloy material used for automobile safety parts

An aluminum alloy material and automobile safety technology, which is applied in the field of preparation of metamorphic hypoeutectic aluminum alloy materials for automobile safety parts, can solve problems such as bonding, and achieve the effect of improving service life and safety factor

Inactive Publication Date: 2015-06-10
TIANJIN LIZHONG ALLOY GROUP
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The invention overcomes the problems of the prior art that it will bond with the aluminum alloy liquid at high temperature and release impurities such as silicon and iron in the refractory material into the aluminum alloy liquid

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of modified hypoeutectic aluminium alloy material used for automobile safety parts
  • Preparation method of modified hypoeutectic aluminium alloy material used for automobile safety parts
  • Preparation method of modified hypoeutectic aluminium alloy material used for automobile safety parts

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0036] The present invention will be further described in detail below through the specific examples, the following examples are only descriptive, not restrictive, and cannot limit the protection scope of the present invention with this.

[0037] A method for preparing a metamorphic hypoeutectic aluminum alloy material for automotive safety parts, described below:

[0038] One, the preparation steps of Al+Sb+Ti refining and modifying parent aluminum alloy liquid are as follows:

[0039] Prepare master aluminum alloy liquid according to Ti: 5-6%, Sb: 5-6%, Al: 88-90%

[0040] ⑴Weigh 147Kg of titanium agent (75% Ti content) and 110Kg of metal antimony according to the mass percentage of elements in the parent aluminum alloy liquid: Ti: 5-6%, Sb: 5-6%, Al: 88-90%, and remelt Aluminum ingot 1743Kg; =

[0041] (2) Weigh ST-1 flux according to 0.3-0.5% of the total feed, weigh ST-1S covering agent according to 0.3-0.5% of the total feed, and weigh ST-sodium-free refining agent acc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a modified hypoeutectic aluminium alloy material used for automobile safety parts. The preparation method comprises the steps of preparation of a refined and modified master aluminium alloy liquid and preparation of a novel refined and modified hypoeutectic aluminium alloy material. The alloy material has the advantages of high-temperature wear resistance, high-temperature fatigue resistance, high strength, high toughness, and the like, is used for manufacturing automobile safety parts, such as rear brake calipers, brake master cylinders and steering cases, and has the effects of greatly prolonging the service lives of the automobile parts and improving the safety factors of automobiles; the mechanical properties of the novel refined and modified hypoeutectic aluminium alloy material are detected after thermal treatment of the novel refined and modified hypoeutectic aluminium alloy material and are close to the standards (the tensile strength is not less than 400MPa) of the mechanical properties of high-strength aluminium alloys while the elongation and yield strength of the novel refined and modified hypoeutectic aluminium alloy material are far higher than those of high-strength hard aluminium alloys.

Description

technical field [0001] The invention belongs to the field of non-ferrous metal material preparation technology and metamorphic treatment process, and in particular relates to a preparation method of metamorphic hypoeutectic aluminum alloy material for automobile safety parts. Background technique [0002] Metal structure refinement is one of the ways to improve the mechanical properties of metal materials, and it is also the only way to improve the plasticity index of materials without sacrificing the strength index of the material. , [0003] By searching, only the following two published patent documents related to this patent application were found: [0004] 1. A large-diameter casting aluminum alloy hydraulic coupling impeller heat treatment process (CN101148744), which is characterized in that it consists of the following steps: preparing the large-diameter casting aluminum alloy hydraulic coupling impeller before heat treatment, and large-diameter casting aluminum all...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C1/03C22C1/06C22C21/00
Inventor 王如芬李志琴郭强冯啸姜淑珍霍会娟
Owner TIANJIN LIZHONG ALLOY GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap