Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A cooling method for high temperature blast holes

A technology of high-temperature blastholes and blastholes, which is applied in the field of high-temperature blasthole cooling, can solve the problems of restricting the progress of blasting operations in high-temperature fire areas, high potential safety hazards, and waste of water resources, so as to prevent high-temperature gas from escaping and water leakage, and ensure safety High performance, the effect of increasing the scale of work

Active Publication Date: 2016-06-08
CHINA GEZHOUBA GRP YIPULI CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above problems seriously restrict the progress of blasting operations in high-temperature fire areas, especially in areas with severe water shortages in the north, where water resources are extremely wasted and safety hazards are high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A cooling method for high temperature blast holes

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1: a kind of high-temperature blast hole cooling method, such as figure 1 shown, including the following steps:

[0023] (1) Water 1 and cement slurry 3 are respectively injected into the two boxes of the jetting machine 1. The jetting machine 1 is an ordinary concrete jetting machine commonly used in the construction field. The water spray spray bar 4 and the spray spray bar 5 are scalable spray bars, and the water spray spray bar 4 and the spray spray bar 5 are L-shaped, and its free end, that is, the shaft extending in the vertical direction can be telescopic, and the shaft of the shaft The lower end is respectively provided with a water spray nozzle 8 and a spray nozzle 7. The nozzle can descend and rise in the blast hole 6 along with the expansion and contraction of the shaft. The water nozzle 8 and the spray nozzle 7 are respectively provided with horizontally oriented nozzles. The nozzle can spray liquid 360° horizontally, and the spray nozzle 7 is al...

Embodiment 2

[0029] Embodiment 2: in the present embodiment, the cooling method is basically the same as in embodiment 1, except that the high temperature-resistant and anti-gas channeling latex cement slurry poured in the jet machine 1 is made of 88-90wt.% ordinary cement slurry and It is prepared by mixing 12-10wt.% high-temperature anti-channeling latex cement admixture. In step (4), when the spraying boom 5 rises, the spraying nozzle 7 stops spraying downwards, and only the spraying holes 6 The walls are sprayed horizontally.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a high-temperature blast hole cooling method. The high-temperature blast hole cooling method comprises the following steps that (1) water and cement grout are injected into an injection machine which is provided with a water spraying rod and a grout spraying rod; (2) the injection machine is installed at a blast hole position, the water spraying rod and the grout spraying rod are made to stretch into a blast hole and be aligned with the center of the blast hole position; (3) the water spraying rod descends, and a water spraying nozzle is used for spraying water on the wall of the blast hole; (4) the water spraying rod ascends, the grout spraying rod descends at the same time, a grout spraying nozzle of the grout spraying rod begins to spray the cement grout in the lower direction and the horizontal direction at the same time when the grout spraying rod descends to the bottom of the blast hole, then the grout spraying rod ascends, and the grout spraying nozzle conducts grout spraying process continuously in the ascending process of the grout spraying rod and stops spraying grout when ascending to the opening of the blast hole; (5) after the grout in the blast hole is solidified, water is injected into the blast hole for cooling. By means of the high-temperature blast hole cooling method, the safety and the operation scale of blasting operation in a high-temperature burning area can be improved, safety is high, water resources are saved, and very high application and popularization value is achieved.

Description

technical field [0001] The invention relates to the field of high-temperature fire zone blasting, in particular to a method for cooling a high-temperature blast hole. Background technique [0002] In my country's Xinjiang, Inner Mongolia, Ningxia, Shanxi and other areas where the coal seams are buried shallowly, due to the coal seam outcropping in open-pit coal mines, the coal seam spontaneous combustion zone and the airtightness of the gob area are not strictly sealed, and the air enters to form a spontaneous combustion zone, forming a large high-temperature fire zone. . The "Blasting Safety Regulations" stipulates that blasting operations with a blasthole bottom temperature higher than 60°C are high-temperature blasting. When the blasthole temperature exceeds 60°C, special blasting safety measures must be taken, including cooling down the blasthole, using high-temperature-resistant blasting equipment and thermal insulation protection for explosives, etc. [0003] At prese...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): F42D5/00F42D3/04
Inventor 郝亚飞朱根华周桂松
Owner CHINA GEZHOUBA GRP YIPULI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com