A kind of polystyrene acrylic acid-2-hydroxypropyl ester and its synthesis method and application
A technology of hydroxypropyl ester and acrylic acid, which is applied in construction and other fields, can solve the problem that there is no effective monitoring method for oil production, and achieve the effect of less dosage
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0031] Dissolve 0.1g of polyethylene glycol (PEG4000 average molecular weight 3600-4400) into 55g of hot water, raise the temperature to 75°C for 30min, slowly add 40g of 2-hydroxypropyl acrylate, 4g of styrene and 0.9g of azo The mixed solution of diisobutyronitrile was reacted for 8 hours after the dropwise addition, cooled to room temperature and discharged. Particles with a particle diameter of 0.425 mm-0.850 mm (20 mesh-40 mesh) were obtained.
Embodiment 2
[0033] Dissolve 0.15g of polyethylene glycol (PEG4000 average molecular weight 3600-4400) into 60g of hot water, raise the temperature to 75°C for 30min, slowly add 35g of 2-hydroxypropyl acrylate, 3.5g of styrene and 0.8g of The mixed solution of azodiisobutyronitrile was reacted for 8 hours after the dropwise addition was completed, cooled to room temperature and discharged. Particles with a particle diameter of 0.425 mm-0.212 mm (40 mesh-70 mesh) were obtained.
Embodiment 3
[0035] Dissolve 0.2g of polyethylene glycol (PEG4000 average molecular weight 3600-4400) into 65g of hot water, raise the temperature to 75°C for 30min, slowly add 30g of 2-hydroxypropyl acrylate, 3g of styrene and 0.6g of azo The mixed solution of diisobutyronitrile was reacted for 8 hours after the dropwise addition, cooled to room temperature and discharged. Particles with a particle diameter of 0.212 mm-0.090 mm (70 mesh-170 mesh) were obtained.
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com