A kind of preparation method of humic acid coated urea

A technology of coating urea and humic acid, which is applied in the field of preparation of humic acid-coated urea, can solve the problems of complex coating agent production and coating process, large amount of coating agent, poor storage stability of urea particles, etc. Enhanced self-regulation ability, increased soil organic matter content, and beneficial to the sustainable development of agriculture

Active Publication Date: 2018-05-29
LIAONING PUTIAN TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing problems of commercial urea are as follows: (1) Urea granules have poor storage stability in humid and high-temperature environments, and are easy to melt and agglomerate. Therefore, urea manufacturers generally carry out oil immersion or coating treatment, such as sulfur coating Cloth urea, etc.
But the oil may pollute the soil, and the sulfur coating process is complicated and costly
(2) The application of urea in the soil is quickly converted into ammonium nitrogen by the action of soil urease, making most of it volatilize, and the utilization rate is very low
The current technical level and existing problems of coated urea are as follows: (1) The technology of sulfur-coated urea is mature, and national standards have been formulated; however, the process is complicated, the dosage of coating agent is large, and the nitrogen content is low, which limits the application
(2) The national standard of urea inhibitor-coated urea has also passed the review (stable fertilizer), but it is highly controversial, because urease inhibitor itself is highly toxic, although it has been applied, but no long-term positioning experiment has been carried out, which is harmful to soil, environment, It is still unknown how harmful water bodies and agricultural products are
(3) Humic acid-containing urea is currently being formulated. The problem is that the amount of humic acid-containing urea is too low, only 0.12%, which is of little significance, and the slow-release and anti-caking effects of humic acid-urea in the slurry mixing method are limited. At the same time, it is easy to Make the biuret exceed the standard
However, the production and coating process of the coating agent provided by this patent are very complicated, which is not conducive to large-scale production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0020] This embodiment provides a preparation method of humic acid-coated urea, which includes the following steps.

[0021] Step 1. Add humic acid raw powder and trisodium phosphate into sodium hydroxide or potassium hydroxide aqueous solution, that is, use sodium hydroxide or potassium hydroxide aqueous solution and trisodium phosphate to activate humic acid raw powder, and mix at 100°C React for 1 hour, centrifuge and collect the filtrate to obtain sodium humate or potassium humate solution.

[0022] The humic acid: sodium hydroxide (or potassium hydroxide): trisodium phosphate mass ratio is 10:0.6:0.4.

[0023] Step 2. Add 2% PVA-1788 to the sodium humate or potassium humate solution to make it fully miscible, and then dry the solution with a hot cylinder dryer until the water content is less than 10%, to obtain sodium humate or Potassium humate dry product.

[0024] Step 3, crush the dried product to 100-200 mesh, and use it as a coating agent for humic acid-coated urea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of humic acid coated urea. The preparation method comprises following steps: humic acid raw powder and trisodium phosphate are added into a sodium hydroxide or a potassium hydroxide aqueous solution for 1h of reaction at 100 DEG C so as to obtain a sodium humate or a potassium humate aqueous solution; polyvinyl alcohol is added for mixing, and an obtained mixed solution is dried until water content is lower than 10% so as to obtain a dry product; the dry product is smashed into particles with a particle size of 80 to 200 meshes, and is taken as a coating agent; at normal temperature, the coating agent is mixed with urea particles at a certain ratio; an obtained mixture is subjected to treatment in a roller for 10 to 30min, and is subjected to sieving and packaging so as to obtain humic acid coated urea. The preparation method is capable of realizing direct coating after pelleting in urea plants, and is suitable for coating processing in value-adding factories using commercial urea. Introduction of humic acid is capable of improving product functions, urea is provided with long-term stability, utilization ratio is increased greatly, the preparation method is beneficial for energy saving and environmental protection; long-term application is capable of restoring soil, increasing soil organic matter content, and improving soil self adjustment ability, and is beneficial for agricultural sustainable development.

Description

technical field [0001] The invention relates to the technical field of novel fertilizers, in particular to a preparation method of humic acid-coated urea. Background technique [0002] Humic acid (abbreviated as HA) widely exists in soil, peat, lignite, and weathered coal. It is an organic matter formed by the remains of organisms (mainly plants) through microbial decomposition and a series of geophysical and chemical processes. It is a type of complex composition. Natural organic polymer mixture. The molecular structure of humic acid is mainly composed of aromatic nucleus, and contains various functional groups such as carboxyl group, hydroxyl group, phenolic hydroxyl group, alcoholic hydroxyl group, and methoxyl group. [0003] Humic acid is a natural plant growth regulator. A certain concentration of humic acid can promote root growth and increase germination rate; enhance plant leaf respiration and photosynthesis intensity; improve physiological metabolism and enzyme ac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C05G3/08C05G3/04C05C9/00C05G3/80C05G3/90
Inventor 郭书利杨丽辉陶晓丹曹洪宇
Owner LIAONING PUTIAN TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products