Quick-setting type waterproof mortar having self-repairing function and secondary permeability resistance as well as preparation method thereof

A secondary anti-seepage and waterproof mortar technology, applied in the field of building waterproof materials, can solve the problems of no self-repair function and secondary anti-seepage

Inactive Publication Date: 2016-02-24
CHINA STATE CONSTRUCTION ENGINEERING CORPORATION +1
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The first purpose of the present invention is to provide a quick-setting waterproof mortar with self-repair function and secondary impermeability, so as to solve the problem that the existing quick-setting ordinary waterproof mortar and polymer modified waterproof mortar have no self-repair function and secondary impermeability technical issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Quick-setting type waterproof mortar having self-repairing function and secondary permeability resistance as well as preparation method thereof
  • Quick-setting type waterproof mortar having self-repairing function and secondary permeability resistance as well as preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] This example is an ordinary waterproof mortar: 43 kg of quick-setting sulphoaluminate cement, 45 kg of quartz sand, 2.2 kg of silica fume, 1.8 kg of heavy calcium, 1.5 kg of hemihydrate gypsum, 5 kg of osmotic crystal active masterbatch, naphthalene series 1 kg of water reducer, 0.4 kg of lithium carbonate coagulant, and 0.1 kg of cellulose ether.

[0033] Its preparation method is as follows: Weigh all the components according to the formula quantity, add them to the planetary mortar mixer and stir slowly for 23 seconds, then add the water required for the formula quantity (the water-cement ratio is 0.35), then slowly stir for 37 seconds, then transfer to Stir quickly, and stop stirring after 30 seconds to prepare quick-setting waterproof mortar.

Embodiment 2

[0035] This example is an ordinary waterproof mortar: 50 kg of quick-setting sulphoaluminate cement, 30 kg of quartz sand, 2 kg of silica fume, 3 kg of heavy calcium, 2.1 kg of hemihydrate gypsum, 8 kg of osmotic crystal active masterbatch, naphthalene series 1.2 kg of water reducer, 0.3 kg of lithium carbonate coagulant, and 0.05 kg of cellulose ether.

[0036] Its preparation method is as follows: Weigh all the components according to the formula quantity, add them to the planetary mortar mixer and stir slowly for 23 seconds, then add the water required for the formula quantity (the water-cement ratio is 0.35), then slowly stir for 37 seconds, then transfer to Stir quickly, and stop stirring after 30 seconds to prepare quick-setting waterproof mortar.

Embodiment 3

[0038] This example is an ordinary waterproof mortar: 45 kg of quick-setting sulphoaluminate cement, 40 kg of quartz sand, 1.5 kg of silica fume, 4.5 kg of heavy calcium, 1.8 kg of hemihydrate gypsum, 9 kg of osmotic crystal active masterbatch, naphthalene series 1.5 kg of water reducer, 0.2 kg of lithium carbonate coagulant, and 0.08 kg of cellulose ether.

[0039] Its preparation method is as follows: Weigh all the components according to the formula quantity, add them to the planetary mortar mixer and stir slowly for 23 seconds, then add the water required for the formula quantity (the water-cement ratio is 0.35), then slowly stir for 37 seconds, then transfer to Stir quickly, and stop stirring after 30 seconds to prepare quick-setting waterproof mortar.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Impermeability pressureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a quick-setting type waterproof mortar having self-repairing function and secondary permeability resistance as well as a preparation method thereof. The quick-setting type waterproof mortar having self-repairing function and secondary permeability resistance is prepared by using the following raw materials and water: a mixed cement, quartz sand, silica fume, heavy calcium, a capillary crystalline active master, a water reducer, an antifoaming agent, a coagulation accelerator and cellulose ether; and the mixed cement is composed of an ordinary portland cement and a quick-setting type sulphoaluminate cement. The quick-setting type waterproof mortar is used for repairing construction, if secondary leakage is happened, the capillary crystalline active master, the a repairing mortar and cement hydration product portlandite in concrete are continuously reacted for realizing self restoration, so that secondary anti-permeability effect can be reached, and secondary or multi-time restoration for regenerated cracks can be avoided.

Description

technical field [0001] The invention belongs to the technical field of building waterproof materials, in particular to quick-setting waterproof mortar with self-repair function and secondary impermeability. Background technique [0002] Roads, bridges, tunnels, basements of buildings, water conservancy facilities and other projects that use concrete as building materials usually suffer from structural defects (such as cracks, cracks and Micropores) infiltrate and corrode the steel bars inside the concrete, resulting in the degradation of the performance of the reinforced steel bars inside the concrete, seriously affecting the service life of the construction project. In order to prolong the service life of these construction projects, it is urgent to repair the defective parts in the concrete structure. And waterproof mortar is an effective repair and leak-proof material. [0003] Waterproof mortar can be divided into slow-setting quick-setting waterproof mortar and quick-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/14
Inventor 薛晓张卫东蒋立红李艳稳屈建秦杰张红强张荣普张子英
Owner CHINA STATE CONSTRUCTION ENGINEERING CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com