Cold-recycling asphalt mixture

A technology for asphalt mixture and waste asphalt mixture, applied in sustainable waste treatment, solid waste management, climate sustainability, etc. The effect of good construction performance, high temperature stability and water stability, and high recycling rate

Inactive Publication Date: 2016-04-06
SOUTHEAST UNIV
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The existing technology cannot recycle the asphalt in the recycled asphalt pavement material (ie waste asphalt mixture) at room temperature, and the utilization of the asphalt in the recycled asphalt pavement material can only use the "hot melt" method
However, during the high-temperature heating process, a large amount of fuel is consumed, and the asphalt components in the mixture are further aged, which affects the technical performance of asphalt

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A kind of cold recycled asphalt mixture, which is composed of the following components (parts by weight): waste asphalt mixture: 88 parts; waste oil: 3.5 parts; diesel oil: 2.5 parts; slaked lime: 0.45 parts; lignin fiber: 0.68 parts; Aluminum: 2.4 parts; Fly ash: 3.6 parts; Benzophenone: 0.66 parts; p-toluenesulfonic acid: 0.26 parts; Ratio, add waste oil and diesel oil in the waste bituminous mixture that reclaims, stir 3.5 minutes, to dissolve the asphalt component wherein; (2) then follow the above-mentioned ratio sequentially slaked lime, lignin fiber, aniline and p-toluenesulfonic acid, stir 6 Minutes; (3) Finally, add aluminum chloride, fly ash and benzophenone according to the above ratio, and stir for 4 minutes to prepare cold recycled asphalt mixture.

Embodiment 2

[0041] A kind of cold recycled asphalt mixture, which is composed of the following components (parts by weight): waste asphalt mixture: 79 parts; waste oil: 1.35 parts; diesel oil: 3.65 parts; slaked lime: 0.46 parts; lignin fiber: 0.8 parts; Aluminum: 2.3 parts; Fly ash: 3.3 parts; Benzophenone: 0.7 parts; p-toluenesulfonic acid: 0.26 parts; Ratio, add waste oil and diesel oil in the waste bituminous mixture that reclaims, stir 4 minutes, to dissolve the asphalt component wherein; (2) then successively according to above-mentioned ratio slaked lime, lignin fiber, aniline and p-toluenesulfonic acid, stir 6 Minutes; (3) Finally, add aluminum chloride, fly ash and benzophenone according to the above ratio, and stir for 4 minutes to prepare cold recycled asphalt mixture.

Embodiment 3

[0043] A kind of cold recycled asphalt mixture, which is composed of the following components (parts by weight): waste asphalt mixture: 83 parts; waste oil: 4 parts; diesel oil: 3 parts; slaked lime: 0.45 parts; lignin fiber: 0.7 parts; Aluminum: 2.2 parts; Fly ash: 4.3 parts; Benzophenone: 0.85 parts; p-toluenesulfonic acid: 0.28 parts; Ratio, add waste oil and diesel oil to the recovered waste asphalt mixture, and stir for 4 minutes; (2) then follow the above ratios for slaked lime, lignin fiber, aniline and p-toluenesulfonic acid, and stir for 8 minutes; (3) Finally, Add aluminum chloride, fly ash and benzophenone according to the above ratio, and stir for 4 minutes to prepare cold recycled asphalt mixture.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a cold-recycling asphalt mixture, which is composed of the following ingredients (by weight): 75-95 parts of a waste asphalt mixture, 1-5 parts of gutter oil, 2-4 parts of diesel oil, 0.3-0.6 part of slaked lime, 0.5-1 part of lignin fiber, 2-3 parts of aluminium chloride, 3-5 parts of fly ash, 0.5-1 part of benzophenone, 0.2-0.3 part of p-toluenesulfonic acid and 0.3-0.6 part of aniline. By the use of a formula-improved cold-recycling mixture, a cold-recycling mixture having improved performance is obtained. A pavement milling material of the in-place cold-recycling mixture has high recycling rate and good construction performance. High-temperature stability and water stability of the in-place cold-recycling pavement are obviously enhanced. The technological flow is simplified. There is no need to consume fuel, and no exhaust gas is discharged. Thus, real cold-recycling of asphalt is realized, and mixture is beneficial to ''energy conservation and emission reduction'' and environmental protection.

Description

technical field [0001] The invention belongs to the field of road engineering materials, and in particular relates to a cold recycled asphalt mixture. Background technique [0002] With the rapid development of highway construction in my country, the total mileage of asphalt roads has increased year by year. At the same time, many asphalt roads built in the early stage have gradually entered the maintenance stage. The speed of construction and maintenance of asphalt roads has been basically the same. Traditional asphalt pavement maintenance adopts the method of excavating the surface layer and the base layer and then paving. Not only the cost of reconstruction is high and the construction period is long, but also the remaining value of the milled asphalt pavement materials cannot be fully utilized. [0003] Asphalt pavement regeneration technology enables the reuse of old asphalt pavement materials, reduces the use of new mineral materials, saves resources and energy, and i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/26C04B18/16
CPCC04B18/167C04B26/26C04B2111/0075C04B24/001C04B24/00C04B22/064C04B24/383C04B22/12C04B18/08C04B24/008C04B24/121Y02W30/91
Inventor 马涛张德育袁浩黄晓明赵永利叶勤
Owner SOUTHEAST UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap