Flame retardant and flame retardant polyurethane resin composition

一种阻燃剂、原料组合物的技术，应用在聚氨酯树脂组合物,阻燃性聚氨酯树脂组合物,阻燃剂领域，能够解决产生卤化氢等问题，达到变形特性优异、优异可回收性、焦烧特性优异的效果

Active Publication Date: 2016-06-15
DIAHACHI CHEMICAL INDUSTRY CO LTD
View PDF10 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, there is a problem that hydrogen halide is generated when the product of polyurethane foam containing such a flame retardant is discarded and incinerated.
However, the status quo is that there has been no flame retardant comprehensively satisfactory in terms of flame retardancy, anti-fog characteristics, deformation characteristics, and scorch characteristics so far, and development of such flame retardants has been widely desired.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame retardant and flame retardant polyurethane resin composition
  • Flame retardant and flame retardant polyurethane resin composition
  • Flame retardant and flame retardant polyurethane resin composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0228] Hereinafter, the present invention is described in further detail by showing synthesis examples, reference examples, examples, and comparative examples.

Synthetic example 1

[0231] Synthesis of formula (1) compound

[0232] [chemical formula 10A]

[0233]

[0234] As a first step reaction, 312.6 g of neopentyl glycol (3.00 mol) and 109.5 g of 1,4-dioxane were filled into a tank equipped with a stirrer, a thermometer, a return line connected to a hydrochloric acid recovery unit, an absorber, 1L four-necked flask with dropping funnel and heating device. The resulting liquid was heated to 50°C. Subsequently, 460.5 g (3.00 mol) of phosphorus oxychloride was added thereto over 2 hours while maintaining the reaction temperature at 45 to 55°C. After the addition was complete, the generated hydrochloric acid was collected while the mixture was further stirred at 80° C. for 1 hour, followed by dehydrochlorination at 80° C. and a low pressure of 80 kPa for 3 hours, thereby obtaining 662.8 g of a white slurry.

[0235] 100.6 g of the above white slurry obtained in the first reaction step of Synthesis Example 1 and 214.3 g of 1,4-dioxane were charged in...

Synthetic example 2

[0237] Synthesis of formula (4) compound

[0238] [chemical formula 10B]

[0239]

[0240] According to the same method as in Synthesis Example 1 except that 15.6 g (0.26 mol) of ethylenediamine was used instead of piperidine, 71.6 g (yield 77.4%) of a solid was obtained. Phosphorus content percentage: 17.3% by weight. Nitrogen content percentage: 7.8% by weight. The obtained flame retardant compounds were used in the following Reference Examples and Examples.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thermal degradation temperatureaaaaaaaaaa
thermal degradation temperatureaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
Login to view more

Abstract

The present invention provides a polyurethane which has excellent flame retardance and various excellent performances. A phosphoroamidate compound having a specific structure is used as a flame retardant for a polyurethane foam or a polyurethane elastomer. By mixing this flame retardant with a feedstock of polyurethane resin (polyol, polyisocyanate and various additives), a polyurethane reactive feedstock composition is obtained. By reacting the polyisocyanate and active hydrogen-containing compounds such as polyol in the polyurethane reactive feedstock composition, a hardening reaction takes place and a polyurethane foam composition or polyurethane elastomer composition is obtained. The obtained polyurethane resin composition has excellent flame retardance and other excellent performances as the polyurethane foam or polyurethane elastomer.

Description

technical field [0001] The present invention relates to a polyurethane resin composition (for example, a flame-retardant polyurethane foam composition and a flame-retardant elastomer composition) excellent in flame retardancy and various properties. The invention relates to a flame retardant, a flame retardant polyurethane resin composition, a raw material composition and a reactive raw material composition thereof. In one embodiment, it relates to a raw material composition of a flame-retardant polyurethane foam. The composition contains a phosphoramidate compound having a specific structure as a flame retardant. ), deformation characteristics and scorch characteristics are comprehensively excellent. Background technique [0002] Urethane resins are mainly used in various fields of daily life products such as automotive interiors, furniture, and electrical equipment materials due to their low cost, light weight, and easy formability. As for the embodiment used, most polyu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09K21/12C08G18/00C08G18/02C08K5/5357C08L75/04C08G101/00
CPCC08G18/4829C08G18/4845C08G2101/00C08J9/0038C08J2375/04C08K5/5357C08K5/5399C09K21/12C08L75/04C08J9/04C08L2201/02C08L2666/82C08L2666/84C08J9/145C08J2375/08
Inventor 小野悟平田学
Owner DIAHACHI CHEMICAL INDUSTRY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap