Pumice bronze-imitating sculpture powder

A technology of imitation of pumice stone and bronze, applied in the field of sculpture, can solve the problems that the color and strength are difficult to imitate bronze and not suitable, and achieve the effect of high artistic appreciation and collection value.

Inactive Publication Date: 2016-09-21
蒋文兰
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The shortcomings of the above patents: the color and strength of the sculpture made of "bronze-imitation sculpture raw material formula" are difficult to achieve the effect of imitation bronze, and it is not suitable for placing in an outdoor environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0036] Below in conjunction with embodiment the present invention will be further described:

[0037] 1. The ingredients of pumice imitation bronze sculpture powder are composed of the following components by weight percentage: pumice imitation bronze sculpture powder semi-finished product 52%, white cement 30%, acidified zeolite particles 8%, rock wool 5%, bronze pearl powder 3 % and Glitter Powder 2%.

[0038] 2. The ingredients of the semi-finished pumice imitation bronze sculpture powder are composed of the following components by weight percentage: 56% of pumice, 28% of natural weathered attapulgite clay, 5% of white carbon black, 8% of bronze powder, and 2% of iron oxide yellow and Tartrazine 1%.

[0039]3. The production method of pumice imitation bronze sculpture powder: (1) Input the ingredients of pumice imitation bronze sculpture powder semi-finished product into the mixer for mixing and stirring, after stirring evenly, input it into the mill to grind the pumice im...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a pumice bronze-imitating sculpture powder. The main points of a technical scheme of the invention are as follows: the pumice bronze-imitating sculpture powder is composed of pumice, acidized zeolite particles, naturally-weathered attapulgite clay, white cement, white carbon black, bronze powder, iron oxide yellow, lemon yellow, rock wool, bronze pearlescent powder and glitter powder. The pumice bronze-imitating sculpture powder is prepared through the following steps: subjecting ingredients of a semi-finished pumice bronze-imitating sculpture powder to stirring and carrying out milling, then carrying out co-mixing with the ingredients of the pumice bronze-imitating sculpture powder under stirring, and carrying out packaging so as to obtain the pumice bronze-imitating sculpture powder. By adopting the pumice bronze-imitating sculpture powder to manufacture a bronze-imitating sculpture, a bronze-imitating sculpture craft with pure color is obtained after maintenance and hardening; the obtained bronze-imitating sculpture craft has the characteristics of good smooth finish, brightness, high strength, small shrinkage rate, wear resistance and corrosion resistance, can be placed at a variety of places like outdoors, squares, gardens or indoors, is adaptable to weather exposure, and does not deform under exposure to wind and rain; meanwhile, the pumice bronze-imitating sculpture powder is applicable to manufacturing of a variety of bronze-imitating sculpture crafts.

Description

technical field [0001] The invention relates to sculpture, in particular to pumice imitation bronze sculpture powder. Background technique [0002] In many parks, there are imitation bronze sculptures of various ancient and modern figures, children or animals, which are very popular among tourists. Color to shape will be more seriously damaged. [0003] Chinese Patent Publication No.: CN 104446286A, Publication Date: March 25, 2015, titled "A Raw Material Formula for Imitation Bronze Sculpture", discloses "A Raw Material Formula for Imitation Bronze Sculpture, wherein the following components by weight Composition of materials: 40-50 parts of paraffin; 20-30 parts of talcum powder; 15-20 parts of copper gold powder; 5-8 parts of rosin; 10-15 parts of magnesium oxide; 2-5 parts of toughening agent; Part.Wherein, the catalyst is selected from phosphate, sulfate and oxalic acid.Described toughening agent is selected from plant orange stalk fine powder, glass fiber and organic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B111/20
CPCC04B28/04C04B2111/00017C04B2111/00956C04B2111/20C04B2111/2038
Inventor 许庆华袁欣金白云吴一清蒋文兰沈向东许盛英袁长兵
Owner 蒋文兰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com