A processing method of high-performance cemented carbide new material slitting and cutting knife

A technology of cemented carbide and processing methods, applied in other manufacturing equipment/tools, engine components, mechanical equipment, etc., can solve the problem that the performance of cemented carbide slitting knives cannot be fully satisfied, the service life of the blade needs to be further improved, and the processing efficiency and low machining accuracy, to achieve the effect of ensuring compactness and uniformity, reducing pores, and fine grain size

Active Publication Date: 2017-11-24
MAANSHAN HENGLIDA MACHINE BLADE
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In my country, according to data, the current annual sales of domestic cutting tools is about 14.5 billion yuan, most of which are low-end products, and are still standard high-speed steel cutting tools, with low processing efficiency and precision, and are often used in traditional machine tools. and low-precision machine tools, while the proportion of high-quality carbide tools is less than 25%, which is far behind foreign countries.
However, the inventor found in the process of use that the performance of the final cemented carbide slitting knife in this application still cannot fully meet the requirements of our country for the slitting blade, and cannot effectively solve the problem of processing some products with higher quality requirements. When it is necessary to import foreign knives, and the service life of the blades needs to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A processing method of high-performance cemented carbide new material slitting and cutting knife
  • A processing method of high-performance cemented carbide new material slitting and cutting knife
  • A processing method of high-performance cemented carbide new material slitting and cutting knife

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A kind of high-performance cemented carbide new material slitting and cutting knife of this embodiment, the slitting and slitting knife is made by powder metallurgy process, and each component of its raw material is composed according to the following mass percentage:

[0048]

[0049] The above-mentioned inhibitor is a multi-component compound inhibitor, which is composed of the following components in mass percentage: 0.7% VC, 0.6% Cr 3 C 2 and 0.3% TaC. Wherein, Co of the present embodiment refers to cobalt powder, VC refers to vanadium carbide, Cr 3 C 2 refers to chromium carbide, TaC refers to tantalum carbide, CT refers to catechol, and WC refers to tungsten carbide powder. In this example, according to the powder metallurgy process, ultra-fine grain hard carbide WC and bonding metal Co powder are selected, trace elements are added as inhibitors (carbides) according to conditions, and octadecanoic acid is added as activation according to the grinding mechani...

Embodiment 2

[0078] A kind of high-performance cemented carbide new material slitting and cutting knife of this embodiment, the slitting and slitting knife is made by powder metallurgy process, and each component of its raw material is composed according to the following mass percentage:

[0079]

[0080] The above-mentioned inhibitor is a multi-component compound inhibitor, which is composed of the following components in mass percentage: 0.5% VC, 0.8% Cr 3 C 2 and 0.5% TaC.

[0081] The processing method of the above-mentioned high-performance cemented carbide new material slitting and cutting knife of the present embodiment is characterized in that: the processing of the slitting and slitting knife comprises the following steps:

[0082] Step 1. Ingredients: Weigh and mix the components of the slitting knife according to the mass percentage;

[0083] Step 2, wet grinding and pressing: mix the components weighed in step 1 and put them into a wet mill for wet grinding. The wet grindi...

Embodiment 3

[0095] A kind of high-performance cemented carbide new material slitting and cutting knife of this embodiment, the slitting and slitting knife is made by powder metallurgy process, and each component of its raw material is composed according to the following mass percentage:

[0096]

[0097] The above-mentioned inhibitor is a multi-component compound inhibitor, which consists of the following components in mass percentage: 0.6% VC, 1.0% Cr 3 C 2 and 0.4% TaC.

[0098] The processing method of the above-mentioned high-performance cemented carbide new material slitting and cutting knife of the present embodiment is characterized in that: the processing of the slitting and slitting knife comprises the following steps:

[0099] Step 1. Ingredients: Weigh and mix the components of the slitting knife according to the mass percentage;

[0100] Step 2. Wet grinding and pressing: Mix the components weighed in step 1 and put them into a wet mill for wet grinding. The wet grinding me...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-performance stripping and slitting knife adopting a new hard alloy material and a manufacturing method of the stripping and slitting knife and belongs to the technical field of hard alloy cutters. The high-performance stripping and slitting knife adopting the new hard alloy material is manufactured with a powder metallurgy technology, and raw materials comprise components in percentage by mass as follows: 0.40%-0.50% of CT, 80.0%-80.5% of WC, 17.0%-17.5% of Co, 1.6%-2.2% of an inhibitor and 0.05%-0.08% of stearic acid. The manufacturing method of the stripping and slitting knife comprises steps as follows: blending; wet grinding; pressing; sintering; machining. On the basis that higher hardness and higher wear resistant property of a blade are guaranteed, the stripping and slitting knife can still keep excellent impact toughness and breakage resistance and can meet the slitting requirement of various metal sheets on the stripping and slitting knife, and the service life of the blade is remarkably prolonged.

Description

technical field [0001] The invention belongs to the technical field of cemented carbide cutting tools, and more specifically relates to a high-performance cemented carbide new material slitting and cutting knife and a processing method thereof. Background technique [0002] Since the new century, with the rapid development of my country's manufacturing industry, a large number of domestic CNC equipment and assembly lines have entered various fields, and a sharp contradiction soon surfaced-advanced equipment cannot be equipped with advanced domestic mechanical tools. foreign knife. Luo Baihui, secretary-general of the International Mold and Metal Plastic Industry Suppliers Association, said that high-quality cemented carbide cutting tools have become the main tools required by processing enterprises in my country, and are widely used in heavy industries such as automobile and parts production, mold manufacturing, and aerospace. field, but my country's cutting tool companies ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C29/08B22F5/00B22F1/00B22F3/10
CPCB22F1/0003B22F3/1007B22F3/1025B22F5/00B22F2005/001B22F2999/00C22C29/08B22F2201/11
Inventor 张增明杨威谢敏徐本富张荣强
Owner MAANSHAN HENGLIDA MACHINE BLADE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com