Elastomer environment-friendly high-flame-resistance foaming material and preparation method thereof

A foaming material, high flame-retardant technology, applied in the field of composite materials and its preparation, can solve the problems of environmental impact and human body harm, safety reduction, and elastomer materials are not environmentally friendly, so as to ensure fire safety and personal safety , light weight, high flame retardant effect

Inactive Publication Date: 2016-11-23
YANGZHONG TIANZHENG SYNTHETIC MATERIAL RES CENT
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] As rice seedling trays are needed in the process of rice seedling raising, and the elastomer in the rice seedling tray is an important part of the rice seedling tray, its fire safety is very important. In addition to the fire safety of the existing elastomers, It is also necessary to have a lightweight requirement to meet the requirements of the overall weight of the vehicle. In order to achieve this purpose, people have tried various materials as elastomer materials, but the pursuit of lightweight also reduces safety, and often occurs In the event of failure or accident, it is easy to cause a fire situation. Therefore, how to meet the demand for lightweight and have flame-retardant properties to ensure safety is a difficult technical problem to solve. In addition, the existing elastomer materials are not environmentally friendly and have a negative impact on the environment. Great impact and human harm

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] An elastomer environment-friendly and highly flame-retardant foaming material, which is composed of the following mass ratio components, isocyanate: composite material = 1:0.8, said isocyanate is Mitsui MR300 in Japan, and the composition of the composite material is calculated according to the following parts by mass , the specific mass parts are as follows:

[0020] Polyether JTP330 68-75 parts

[0021] Polyether 982 30-35 parts

[0022] Polyether 210 8-10 parts

[0023] Polyether 1500 12-18 parts

[0024] Silicone oil AK8805 2.9-3.5 parts

[0025] Catalyst A33 0.8-1.3 parts

[0026] Catalyst A1 0.6-1 part

[0027] 3-3.8 parts of water

[0028] Flame retardant TCPP 35-40 parts.

Embodiment 2

[0030] A method for preparing the above-mentioned elastomer environment-friendly and high flame-retardant foaming material, comprising the following preparation steps: firstly, a composite material is prepared: 68 parts of polyether JTP330, 30 parts of polyether 982, 8 parts of polyether 210, 12 parts Polyether 1500, 2.9 parts of silicone oil AK8805, 0.8 parts of catalyst A33, 0.6 parts of catalyst A1, 35 parts of flame retardant TCPP and 3 parts of water were added to the reactor for mixing reaction, stirring speed 80r / min, stirring The combined material can be obtained after 6 hours, and then the isocyanate and the combined material are mixed uniformly at a mass ratio of 1:0.8 to obtain the foaming material.

Embodiment 3

[0032] A method for preparing the above-mentioned elastomer environment-friendly and high flame-retardant foaming material, comprising the following preparation steps: firstly, a composite material is prepared: 72 parts of polyether JTP330, 33 parts of polyether 982, 9 parts of polyether 210, 15 parts Polyether 1500, 3.2 parts of silicone oil AK8805, 1 part of catalyst A33, 0.8 parts of catalyst A1, 33 parts of flame retardant TCPP and 3.4 parts of water were added to the reactor for mixing reaction, stirring speed 100r / min, stirring The combined material can be obtained after 7 hours, and then the isocyanate and the combined material are mixed evenly at a mass ratio of 1:0.8 to obtain the foaming material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an elastomer environment-friendly high-flame-resistance foaming material in a rice seedling culture plate and a preparation method thereof. The elastomer environment-friendly high-flame-resistance foaming material is prepared from isocyanate and combined material at mass ratio of 1:0.8. The combined material is prepared from the following materials in parts by weight: 68-75 parts of polyether JTP 330, 30-35 parts of polyether 982, 8-10 parts of polyether 210, 12-18 parts of polyether 1500, 2.9-3.5 parts of silicone oil AK 8805, 0.8-1.3 parts of catalyst A33, 0.6-1 part of catalyst A1, 3-3.8 parts of water and 35-40 parts of flame retardant TCPP. After the material and the method are adopted, the formula component is reasonable in collocation and the preparation method is proper, so that the prepared foaming material is high in flame resistance and is difficult to burn once meeting fire and the waterproof safety and personal safety are further ensured. Besides, the prepared elastomer is light in weight and can meet the weight requirements of vehicles. The used raw materials of the foaming material are environment-friendly raw materials, so that the matters toxic and harmful to human body are not released and the environmental protection requirement can be met.

Description

technical field [0001] The invention relates to a composite material and a preparation method thereof, in particular to an elastomer environment-friendly high flame-retardant foaming material in a rice seedling raising tray and a preparation method thereof. Background technique [0002] As rice seedling trays are needed in the process of rice seedling raising, and the elastomer in the rice seedling tray is an important part of the rice seedling tray, its fire safety is very important. In addition to the fire safety of the existing elastomers, It is also necessary to have a lightweight requirement to meet the requirements of the overall weight of the vehicle. In order to achieve this purpose, people have tried various materials as elastomer materials, but the pursuit of lightweight also reduces safety, and often occurs In the event of failure or accident, it is easy to cause a fire situation. Therefore, how to meet the demand for lightweight and have flame-retardant propertie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/48C08J9/08C08K5/521C08G101/00
CPCC08G18/4804C08K5/521C08G2110/0083
Inventor 朱章娣朱凌宇
Owner YANGZHONG TIANZHENG SYNTHETIC MATERIAL RES CENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap