A New Method for Production of Medium Carbon Ferrochrome

A technology of medium-carbon ferrochrome and a new method, which is applied in ferrous metal smelting and production of medium-carbon ferrochrome, and can solve problems such as high power consumption, low utilization rate of chromium as the main element in chromium ore, and cumbersome process

Active Publication Date: 2018-08-17
五矿(湖南)铁合金有限责任公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The main disadvantages of this method for producing medium-carbon ferrochromium: 1. The process is cumbersome, and this product can only be produced through three electric furnaces; 2. The power consumption is high, and the utilization rate of the main element chromium in chrome ore is low.
3. The lining life is generally short (about 45-60 days)
But at the same time, its equipment investment is relatively large
[0016] In addition, in the existing method of producing medium carbon ferrochrome, its general energy consumption is 1000KWH / ton of product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] In the production of Cr60C2.0 chromium products, the composition wt% of various raw materials is shown in Table 1:

[0035] According to the proportion of 0.88 tons of high-carbon ferrochrome, 0.65 tons of Sudanese chrome ore, and 0.08 tons of silica, the raw materials are prepared, and the refining electric furnace is used as the smelting furnace to smelt at 1500-1800 ° C to obtain the product Cr60C2.0; the composition of the product Cr60C2.0 (wt%) see table 2

[0036] Table 1

[0037] raw material name

[0038] The chromium product composition in the produced Cr60C2.0 is: Table 2

[0039] product name

[0040] After batching 0.88 tons of high-carbon ferrochrome, 0.65 tons of Sudanese chrome ore, and 0.08 tons of silica, smelting according to the above-mentioned process to obtain 1 ton of Cr60C2.0. Unit smelting power consumption is 850KWH / ton of product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a new method for medium-carbon ferrochrome production, and belongs to the technical field of ferrous metal smelting. The new method disclosed by the invention comprises the following steps: preparing 350-360kg of Cr2O3 and 85-95kg of silica according to per ton of liquid high-carbon ferrochrome, wherein the Cr2O3 is supplied by chrome ores; and stacking the prepared material chrome ores and silica at the bottom of a furnace, and smelting at 1500-1800 DEG C in a manner of bottom heating to obtain medium-carbon ferrochrome. The new method disclosed by the invention is simple in process, low in energy consumption, low in requirement on equipment, and convenient for large-scale industrialized application.

Description

technical field [0001] The invention relates to a new method for producing medium-carbon ferrochrome, belonging to the technical field of black metal smelting technology. Background technique [0002] According to different carbon content, ferrochrome is divided into high carbon ferrochrome (C≦10%), medium carbon ferrochrome (C≦4.0%), low carbon ferrochrome (C≦0.5%), micro-carbon ferrochrome (C≦0.15%) %)Wait. At present, there are mainly two production methods of medium carbon ferrochrome: [0003] 1. Electric silicon thermal method; electric silicon thermal method is actually a desiliconization method. In the refining electric furnace, the oxide in the chromium ore is used to remove the silicon in the silicon-chromium alloy to achieve the purpose of producing medium-carbon ferrochromium. Medium-carbon chromium The C content in iron depends entirely on the C content of the chromium-silicon alloy. Its main reaction is as follows: [0004] 2Cr 2 o 3 +3Si=3SiO 2 +4Cr ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21B11/10
CPCC21B11/10
Inventor 晏文彪
Owner 五矿(湖南)铁合金有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More