Composite tranquilizer composition and modified polymer material

A technology of polymer materials and stabilizers, applied in the field of stabilizer compositions and modified polymer materials, can solve the problems of easy oxidative degradation, coloration of organic polymers, decreased processing stability, yellowing mechanical properties, etc. problem, to achieve the effect of good color stability and processing stability

Inactive Publication Date: 2017-03-08
FDC LEES CHEM IND
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although organic polymers have the above advantages, commercially available organic polymers are easily oxidatively degraded under the action of heat energy, resulting in yellowing and degradation of mechanical properties
[0003] Therefore, in order to prevent the oxidative degradation of organic polymers, antioxidants are generally added in the extrusion process to reduce the degradation of organic polymers, so as to enhance the mechanical properties and heat resistance of organic polymers; however, antioxidants themselves may cause organic Polymer coloration and decreased processing stability
In addition, antacids are generally added during the extrusion process to inhibit the degradation of organic polymers caused by acidic substances; Decreased stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite tranquilizer composition and modified polymer material
  • Composite tranquilizer composition and modified polymer material
  • Composite tranquilizer composition and modified polymer material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1 to 15

[0053] According to the components and ratios (parts by weight) shown in Table 1, 100 parts by weight of polypropylene or 100 parts by weight of polyethylene and the composite stabilizer composition were uniformly mixed at 25°C to obtain the polymeric compounds of Examples 1 to 15. material (hereinafter referred to as E1' to E15').

Embodiment 16 to 30

[0061] According to the components and proportions (parts by weight) shown in Table 3, 100 parts by weight of polypropylene or 100 parts by weight of polyethylene and the compound stabilizer composition were uniformly mixed at 25°C to obtain the polymeric compounds of Examples 16 to 30. material (hereinafter referred to as E16' to E30').

Embodiment 31 to 45

[0069] According to the components and ratios (parts by weight) shown in Table 5, 100 parts by weight of polypropylene or 100 parts by weight of polyethylene and the composite stabilizer composition were uniformly mixed at 25° C. to obtain the polymers of Examples 31 to 45. materials (hereinafter referred to as E31' to E45').

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a composite tranquilizer composition, which contains a hydrotalcite compound represented by a chemical formula 1 and one selected from a sulfur-containing carboxylate represented by a chemical formula 2, a chemical formula 3, a chemical formula 4 and a combination thereof, wherein the chemical formula 1 is [M<II>1-xM<III>x(OH)2]<x+>(A<n->)x/n.mH2O, the chemical formula 2 is [R<1>-S-CHR<0>-(CH2)t-COO<->]qM<q+>, the chemical formula 3 is defined in the specification, the chemical formula 4 is defined in the specification, and each code is defined in the specification. The present invention further provides a modified polymer material, which comprises an organic polymer substrate and the composite tranquilizer composition, wherein the modified polymer material can have advantages of good color stability and good processing stability through the composite tranquilizer composition.

Description

technical field [0001] The invention relates to a stabilizer composition and a modified polymer material, in particular to a compound stabilizer composition comprising hydrotalcite compounds and sulfur-containing carboxylates, and a compound stabilizer composition comprising the compound formula A modified polymeric material of a stabilizer composition. Background technique [0002] Existing organic polymers (such as polyolefins) have good chemical stability, mechanical strength, electrical insulation and product dimensional stability, and have the advantages of non-toxicity and easy processing, so they are often widely used as thermoplastic engineering plastics. Although organic polymers have the above advantages, commercially available organic polymers are easily oxidatively degraded under the action of heat energy, resulting in yellowing and degradation of mechanical properties. [0003] Therefore, in order to prevent the oxidative degradation of organic polymers, antiox...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08K3/26C08K5/372C08L23/06C08L23/12
CPCC08K3/26C08K5/372C08K5/52C08K5/526C08K5/5313C08K5/5393C08L23/12C08L23/06
Inventor 薛友傑陈桢凯李昆昌
Owner FDC LEES CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products