Spinning method of high-cotton-content, high-elasticity and abrasion-resistant fabric

A technology with cotton content and high elasticity, applied in textiles, textiles, papermaking, fabrics, etc., can solve the problems of poor elasticity, easy shrinkage and mildew of pure cotton fabrics, and achieve good wear resistance, good moisture absorption, and improved The effect of wrinkle resistance and abrasion resistance

Inactive Publication Date: 2017-07-21
相里海霞
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, pure cotton fabrics have disadvantages such as poor elasticity, easy shrinkage, and easy mildew. Based on the above problems, the present invention proposes a weaving method for high cotton content, high elasticity and wear-resistant fabrics.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The weaving method of a kind of high cotton content high elastic wear-resisting cloth that the present invention proposes, comprises the following steps:

[0019] S1, select combed cotton yarn and novel polyester PPT fiber monofilament, cotton yarn and novel polyester PPT fiber monofilament are respectively immersed in the slurry 5min that adds the nano-silver series inorganic antibacterial agent that consumption is 4% of slurry amount, Take out the pressure to remove the excess liquid, and dry at a high temperature of 60°C for 40 minutes;

[0020] S2. Plying 12 cotton yarns with a twist of 400 and a twist direction of Z to obtain cotton thread A, and 3 new polyester PPT fiber monofilaments with a twist of 500 and a twist direction of Z Joint stock in the same way to obtain polyester thread B;

[0021] S3. Plying 5 cotton threads A and 1 polyester thread B with a twist of 400 and a twisting direction of S to obtain a warp, 7 cotton threads A and 1 polyester thread B wi...

Embodiment 2

[0025] The weaving method of a kind of high cotton content high elastic wear-resisting cloth that the present invention proposes, comprises the following steps:

[0026] S1, select combed cotton yarn and novel polyester PPT fiber monofilament, cotton yarn and novel polyester PPT fiber monofilament are respectively immersed in the slurry 8min that adds the nano-silver series inorganic antibacterial agent that consumption is 2% of slurry amount, Take out the pressure to remove the excess liquid, and dry at a high temperature of 55°C for 45 minutes;

[0027] S2. Plying 10 cotton yarns with a twist of 350 and a twist direction of Z to obtain cotton thread A, and 1 piece of new polyester PPT fiber monofilament with a twist of 450 and a twist of Z Joint stock in the same way to obtain polyester thread B;

[0028] S3, 3 cotton threads A and 1 polyester thread B are plied with a twist of 350 and the twist direction is S to obtain a warp, and 5 cotton threads A and 1 polyester thread ...

Embodiment 3

[0032] The weaving method of a kind of high cotton content high elastic wear-resisting cloth that the present invention proposes, comprises the following steps:

[0033] S1, select combed cotton yarn and novel polyester PPT fiber monofilament, cotton yarn and novel polyester PPT fiber monofilament are respectively immersed in the slurry 4min that adds the nano-silver series inorganic antibacterial agent that consumption is 5% of slurry amount, Take out the pressure to remove the excess liquid, and dry at a high temperature of 70°C for 30 minutes;

[0034] S2. Plying 14 cotton yarns with a twist of 320 and a twist direction of Z to obtain cotton thread A, and 3 new polyester PPT fiber monofilaments with a twist of 600 and a twist direction of Z Joint stock in the same way to obtain polyester thread B;

[0035] S3, 5 cotton threads A and 1 polyester thread B are plied with a twist of 500 and the twist direction is S to obtain a warp, and 8 cotton threads A and 2 polyester threa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a weaving method of high cotton content, high elasticity and wear-resistant cloth, which comprises the following steps: respectively immersing cotton yarn and new-type polyester PPT fiber monofilament in slurry, taking out and drying; performing plying to obtain cotton thread A, and The new polyester PPT fiber monofilament is plied to obtain the polyester thread B; the cotton thread A and the polyester thread B are plied to obtain the warp and weft; the upper and lower parts are separated to form a shed, and the weft is introduced into the shed; Interweave the warp and weft threads to form a fabric, and roll it up after passing the inspection. The invention proposes a weaving method for a high-cotton-content, high-elasticity wear-resistant cloth, the weaving process is simple, the weaving efficiency is high, the wrinkle resistance and wear resistance of the cloth are improved, and the production cost is reduced. The cloth woven by the invention has the advantages of Good moisture absorption, moisture retention, heat resistance, alkali resistance, good air permeability, soft and comfortable, good elasticity, beautiful appearance, good antibacterial and wear-resistant effects, it is worth promoting.

Description

technical field [0001] The invention relates to the technical field of cloth weaving technology, in particular to a method for weaving a cloth with high cotton content and high elasticity and wear resistance. Background technique [0002] Pure cotton fabric refers to the fabric produced with cotton as raw material. Pure cotton fabric has excellent hygroscopicity and heat resistance, and is comfortable to wear, does not generate static electricity, has excellent air permeability, anti-sensitivity, and is easy to clean. Pure cotton fabrics are widely used in people's lives, especially some work clothes in industries that require relatively high moisture absorption of clothing can choose pure cotton fabrics for processing. However, pure cotton fabrics have disadvantages such as poor elasticity, easy shrinkage, and easy mildew. Based on the above problems, the present invention proposes a weaving method for high cotton content, high elasticity and wear-resistant fabrics. Conte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/00D03D13/00D06M11/00D06M101/06D06M101/32
CPCD03D15/00D03D13/008D06M11/00D06M16/00D06M2101/06D06M2101/32D10B2201/02D10B2331/04
Inventor 相里海霞
Owner 相里海霞
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap