A kind of high-gloss anti-friction varnish and its preparation method

A technology of varnish and tung oil, applied in the direction of coating, wax coating, etc., can solve the problems of poor surface adhesion of printed matter, hinder the development of water-based varnish, poor wear resistance, etc., achieve enhanced friction resistance and gloss, reduce Cleaning and maintenance costs, the smooth effect of ink conjunctiva

Inactive Publication Date: 2020-01-14
ZHEJIANG KEXIN INK
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since water-based varnish uses water as a solvent, it will not have a swelling effect on the ink on the surface of the printed matter, so it generally has the defect of poor adhesion to the surface of the printed matter, and the film formed by the water-based varnish is still wear-resistant. The problem of poor performance and difficult drying has become a technical bottleneck hindering the further development of water-based varnishes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-gloss anti-friction varnish and its preparation method
  • A kind of high-gloss anti-friction varnish and its preparation method
  • A kind of high-gloss anti-friction varnish and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A kind of glazing oil, it is made up of the raw material of following weight part:

[0033]

[0034] Among them: rosin modified phenolic resin is 8376# resin and 8102# resin, the weights of both are: 400g, 550g respectively; mineral oil is 280# white oil; antioxidant is 2,6-di-tert-butyl-4-methyl base phenol; desiccants are cobalt dry liquid and manganese dry liquid, the weights of which are respectively: 13.5g and 27g.

[0035] Above-mentioned glazing oil is prepared by following steps:

[0036] S1. Mix 405g tung oil and 135g linseed oil, heat up to 90-110°C, add 54g beeswax, and stir to obtain a wax paste;

[0037] S2, heat up the wax paste in step S1 to 160-170°C, keep it warm, add 400g8376# resin and 550g8102# resin in 5 times under constant stirring; then heat up to 230-240°C, add 432g linseed oil, 500g mineral oil; Then lower the temperature to 155-165°C, add 10.8g of liquid aluminum and 27g of mineral oil;

[0038] S3. The temperature of the mixture obtaine...

Embodiment 2

[0042] A kind of glazing oil, it is made up of the raw material of following weight part:

[0043]

[0044] Among them: rosin modified phenolic resin is 8376# resin and 8102# resin, the weights of both are: 380g and 570g respectively; mineral oil is 280# white oil; antioxidant is 2,6-di-tert-butyl-4-methyl base phenol; desiccant is cobalt dry liquid and manganese dry liquid, the weight of both is: 12.0g, 28.5g.

[0045] Above-mentioned glazing oil is prepared by following steps:

[0046] S1. Mix 392.2g tung oil and 109g linseed oil, heat up to 90-110°C, add 54g beeswax, and stir to obtain a wax paste;

[0047] S2, heat up the wax paste in step S1 to 160-170°C, keep warm, add 380g8376# resin and 570g 8102# resin in 5 times under constant stirring; then heat up to 230-240°C, add 436g linseed oil, 513g mineral oil ;Then lower the temperature to 155~165℃, add 10.8g liquid aluminum and 27g mineral oil;

[0048] S3. The temperature of the mixture obtained in step S2 is raised ...

Embodiment 3

[0052] A kind of glazing oil, it is made up of the raw material of following weight part:

[0053]

[0054]

[0055] Among them: rosin modified phenolic resin is 8376# resin and 8102# resin, the weights of both are: 500g and 500g respectively; mineral oil is 280# white oil; antioxidant is 2,6-di-tert-butyl-4-methyl base phenol; desiccants are cobalt dry liquid and manganese dry liquid, the weights of which are respectively: 15g and 30g.

[0056] Above-mentioned glazing oil is prepared by following steps:

[0057] S1. Mix 450g tung oil and 143g linseed oil, heat up to 90-110°C, add 50g beeswax, and stir to obtain a wax paste;

[0058] S2, heat up the wax paste in step S1 to 160-170°C, keep it warm, add 500g8376# resin and 500g8102# resin in 7 times under constant stirring; then heat up to 230-240°C, add 357g linseed oil, 522g mineral oil; Then lower the temperature to 155-165°C, add 15g of liquid aluminum and 27.45g of mineral oil;

[0059] S3. The temperature of the m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of coatings and discloses high-gloss and friction-resistant varnish and a preparation method thereof. The varnish is prepared from raw materials as follows: tung oil, linseed oil, cera alba, rosin modified phenolic resin, mineral oil, gel, a drying agent and an antioxidant. The varnish has the characteristics of good friction resistance, high gloss and proneness to drying, and the preparation process of the varnish has the advantages of being convenient to operate, low in cost and suitable for large-scale industrial production.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to a high-gloss, friction-resistant varnish and a preparation method thereof. Background technique [0002] Varnish is also called varnish or wear-resistant varnish. By coating it on the outer layer of ink, it can form a thin and uniform transparent bright layer on the surface of printed matter after leveling, drying, calendering and curing. , so that the gloss of the printed product can be increased, the visual beauty can be increased, and the printed product can be protected at the same time. To a certain extent, its wear resistance, chemical resistance, water resistance and corrosion resistance can be improved, so that the varnish Widely used in printing, packaging and other industries. [0003] At present, with people's emphasis on environmental protection, the research on water-based varnishes has been developed by leaps and bounds. For example, Chinese patent do...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D191/06C09D161/14C09D191/00C09D7/65C09D7/80
CPCC08L2205/025C08L2205/035C09D191/06C08L91/06C08L61/14C08L91/005C08K5/13
Inventor 黄时舫陈锋张保杰
Owner ZHEJIANG KEXIN INK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap