A method for detecting particle size and surface characteristics of diamond micropowder by flow cytometer

A technology of diamond micropowder and surface characteristics, applied in particle size analysis, preparation of test samples, instruments, etc., to improve detection accuracy, improve detection accuracy and detection efficiency, and reduce agglomeration

Active Publication Date: 2020-08-21
ZHECHENG HUIFENG DIAMOND TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is: aiming at the deficiencies in the existing diamond powder detection technology, the present invention provides a method for detecting the particle size and surface characteristics of diamond powder by using a flow cytometer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The present invention utilizes flow cytometer to detect the method for diamond micropowder particle size and surface characteristic, it is characterized in that, described detection method comprises the following steps:

[0037] a, at room temperature, take by weighing 0.2 g of the prepared diamond micropowder as a test sample;

[0038] B, sodium chloride is added in water and is mixed with the sodium chloride solution that mass concentration is 0.9%, the gained sodium chloride solution is adopted filter bottle to filter, obtains sodium chloride solution for subsequent use;

[0039] C, the detection sample diamond micropowder 0.2g that step a takes by weighing is placed in container, adds in the sodium chloride solution that 40mL step b prepares and stirs 3 minutes, obtains diamond micropowder solution for subsequent use;

[0040] d. Put the container containing the stirred diamond micropowder solution in step c on the lifting platform in the ultrasonic cell pulverizer,...

Embodiment 2

[0052] The present invention utilizes flow cytometer to detect the method for diamond micropowder particle size and surface characteristic, it is characterized in that, described detection method comprises the following steps:

[0053] a, at room temperature, take by weighing 0.2 g of the prepared diamond micropowder as a test sample;

[0054] B, sodium chloride is added in water and is mixed with the sodium chloride solution that mass concentration is 0.6%, the gained sodium chloride solution is adopted filter bottle to filter, obtains sodium chloride solution for subsequent use;

[0055] C, the detection sample diamond micropowder 0.2g that step a takes by weighing is placed in container, adds in the sodium chloride solution that 50mL step b prepares and stirs 4 minutes, obtains diamond micropowder solution for subsequent use;

[0056] d. Put the container containing the stirred diamond micropowder solution in step c on the lifting platform in the ultrasonic cell pulverizer,...

Embodiment 3

[0065] The present invention utilizes flow cytometer to detect the method for diamond micropowder particle size and surface characteristic, it is characterized in that, described detection method comprises the following steps:

[0066] a, at room temperature, take by weighing 0.2 g of the prepared diamond micropowder as a test sample;

[0067] B, sodium chloride is added in water and is mixed with the sodium chloride solution that mass concentration is 0.8%, the gained sodium chloride solution is adopted filter bottle to filter, obtains sodium chloride solution for subsequent use;

[0068] C, place 0.2 g of the test sample diamond micropowder weighed in step a in the container, add 60 mL of the sodium chloride solution prepared in step b and stir for 4 minutes to obtain the diamond micropowder solution for subsequent use;

[0069] d. Put the container containing the stirred diamond micropowder solution in step c on the lifting platform in the ultrasonic cell pulverizer, lift t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for detecting the granularity and surface feature of diamond micro-powder by using a flow cytometer. The method comprises the steps of putting a detecting sample diamond micro-powder into a container, adding a prepared sodium chloride solution, stirring to obtain a diamond micro-powder solution; putting the container containing the diamond micro-powder solution into an ultrasonic cell pulverizer for ultrasonic dispersion, so as to obtain a primarily dispersed diamond micro-powder solution; standing the obtained solution, then adding a prepared octylphenoxypolyethoxyethanol solution and evenly shaking; then putting the solution into the ultrasonic cell pulverizer for ultrasonic dispersion again, so as to obtain a to-be-detected diamond powder solution; finally, automatically detecting the to-be-detected diamond powder solution by adopting the flow cytometer and automatically storing data; finally calling out data of diameter, circularity, breadth length ratio, strip ratio and granularity distribution, and analyzing a result. The detection method provided by the invention can reduce agglomeration to a large extent; the operation is simple, and the effect is obvious.

Description

[0001] 1. Technical field: [0002] The invention relates to a method for detecting the particle size and surface characteristics of diamond micropowder, which belongs to the technical field of superhard material micropowder, and in particular relates to a method for detecting the particle size and surface characteristics of diamond micropowder by using a flow cytometer. [0003] 2. Background technology: [0004] Diamond micropowder refers to diamond particles with a particle size finer than 36 / 54 microns. In the production of diamond micropowder, the particle size distribution and surface characteristics of diamond (crystal form of diamond micropowder) have a great influence on the use of diamond micropowder, especially In the field of diamond wire saw applications. Different particle size distributions and different crystal forms will have a serious impact on diamond wire cutting. In the production of diamond, because the powder particles absorb a large amount of mechanical...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N1/38G01N15/02G01N15/14
CPCG01N1/38G01N15/0205G01N15/1404
Inventor 王再福李飞
Owner ZHECHENG HUIFENG DIAMOND TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com