Baby's physical sunscreen lotion and preparation method

A kind of sunscreen and physical technology, which is applied in the field of baby physical sunscreen and its preparation, can solve the problems of not dare to take babies, and babies are easy to be sunburned

Inactive Publication Date: 2018-02-09
郑生华
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the shortcomings of the prior art, provide a physical sunscreen for babies and its preparation method, and solve the problem that babies are easily sunburned and dare not take them out

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A kind of baby physical sunscreen, is made up of the following raw materials by weight:

[0038] A phase composition

[0039] 7.0 parts of water; 20.0 parts of glycerin; 1.0 parts of carbomer; 1.0 parts of arginine; 10.0 parts of titanium dioxide; 10.0 parts of zinc oxide;

[0040] Phase B component

[0041] C12-20 Alkyl Glucoside 50.0 parts; Cetearyl Alcohol 20.0 parts; Camellia Oil 1.0 parts; Jojoba Seed Oil 90.0 parts; Caprylic / Capric Triglyceride 20.0 parts;

[0042] C phase composition

[0043] 0.5 parts of caprylyl hydroxamic acid; 0.2 parts of ethylhexylglycerin; 1.0 parts of 1,2-hexanediol.

[0044] A preparation method of baby physical sunscreen, comprising the following steps:

[0045] S1. Grind titanium dioxide and zinc oxide finely respectively. The particle size of the ground titanium dioxide and zinc oxide is 1000 mesh. Then add the components of phase A into the emulsification pot in turn, and heat up to 85°C. The specific operation steps for heating ...

Embodiment 2

[0051] A kind of baby physical sunscreen, is made up of the following raw materials by weight:

[0052] A phase composition

[0053] 27.2 parts of water; 11.0 parts of glycerin; 0.6 parts of carbomer; 0.5 parts of arginine; 6.5 parts of titanium dioxide; 5.2 parts of zinc oxide;

[0054] Phase B component

[0055] C12-20 Alkyl Glucoside 20.0 parts; Cetearyl Alcohol 55.0 parts; Camellia Oil 25.5 parts; Jojoba Seed Oil 45.5 parts; Caprylic / Capric Triglyceride 12.5 parts;

[0056] C phase composition

[0057] 0.7 parts of caprylyl hydroxamic acid; 0.15 parts of ethylhexylglycerin; 1.5 parts of 1,2-hexanediol.

[0058] A preparation method of baby physical sunscreen, comprising the following steps:

[0059] S1. Grind titanium dioxide and zinc oxide finely respectively. The particle size of the ground titanium dioxide and zinc oxide is 900 mesh. Then add the components of phase A into the emulsification pot in turn, and heat up to 82°C. The specific operation steps for heating ...

Embodiment 3

[0065] A kind of baby physical sunscreen, is made up of the following raw materials by weight:

[0066] A phase composition

[0067] 14.9 parts of water; 20.0 parts of glycerin; 0.5 parts of carbomer; 0.5 parts of arginine; 7.0 parts of titanium dioxide; 10.0 parts of zinc oxide;

[0068] Phase B component

[0069] C12-20 Alkyl Glucoside 1.0 parts; Cetearyl Alcohol 50.0 parts; Camellia Oil 15.0 parts; Jojoba Seed Oil 5.0 parts; Caprylic / Capric Triglyceride 5.0 parts;

[0070] C phase composition

[0071] 1.0 parts of caprylyl hydroxamic acid; 0.1 parts of ethylhexylglycerin; 1.0 parts of 1,2-hexanediol.

[0072] A preparation method of baby physical sunscreen, comprising the following steps:

[0073] S1. Grind titanium dioxide and zinc oxide finely respectively. The particle size of the ground titanium dioxide and zinc oxide is 880 mesh. Then add the components of phase A into the emulsification pot in turn, and heat up to 81°C. The specific operation steps for heating are...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Login to View More

Abstract

The invention relates to baby's physical sunscreen lotion. The baby's physical sunscreen lotion is prepared from raw materials in parts by weight as follows: a phase A component, a phase B component and a phase C component, wherein the phase A component contains 7.0-70.0 parts of water, 1.0-20.2 parts of glycerin, 0.1-1.0 part of carbomer, 0.1-1.0 part of arginine, 1.0-10.0 parts of titanium dioxide and 0.5-10.0 parts of zinc oxide; the phase B component contains 1.0-50.0 parts of C12-20 alkyl glucoside, 20.0-90.0 parts of cetostearyl alcohol, 1.0-50.0 parts of camellia oil, 1.0-90.0 parts ofsimmondsia chinensis seed oil and 5.0-20.0 parts of caprylic / capric triglyceride; the phase C component contains 0.5-1.0 part of capryloyl hydroximic acid, 0.1-0.2 parts of ethylhexylglycerin and 1.0-2.0 parts of 1,2-hexanediol. The invention also provides a preparation method of the baby's physical sunscreen lotion. The baby's physical sunscreen lotion has the advantages that the problem that babies are easily sunburnt when playing outside is solved; the physical sunscreen lotion has a sun protection function on skin of babies and children and also has certain moisturizing efficacy; the baby's physical sunscreen lotion with the sun protection function is prepared by use of the physical characteristics that inorganic particles have reflection and scattering functions on ultraviolet, visible light and infrared radiation.

Description

technical field [0001] The invention relates to the technical field of baby products, in particular to a baby physical sunscreen and a preparation method. Background technique [0002] The outside world is beautiful and colorful, but because the baby's skin is delicate and vulnerable to external damage, if it is energetic and hot, it will directly sunburn the baby's skin, which is hard to guard against. The present invention is a kind of physical sunscreen lotion used by infants, which utilizes titanium dioxide, zinc oxide and other inorganic particles to reflect or scatter most of the ultraviolet, visible and infrared radiation, which is non-irritating to infants, moistens and moisturizes, and can utilize physical reflection or scattering to Partial UV, visible and infrared radiation reduces skin damage. Therefore a kind of baby physical sunscreen lotion of the present invention meets the demand of market. [0003] Zinc oxide: It is an inorganic particle, white powder, od...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61K8/29A61K8/27A61K8/92A61Q17/04A61Q19/00
CPCA61K8/27A61K8/29A61K8/922A61K2800/30A61K2800/412A61Q17/04A61Q19/00
Inventor 郑生华陈家绍邓银丽唐国俊罗金
Owner 郑生华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com