A kind of polydopamine-based core-shell material and its preparation method and application

A dopamine, core-shell technology, applied in the field of nanomaterial synthesis, can solve problems such as high SERS activity, and achieve the effects of high SERS enhancement factor, stable Raman signal, and maintaining stability

Active Publication Date: 2021-05-11
QILU UNIV OF TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, so far, how to modify AgNWs to have high SERS activity has not been reported.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polydopamine-based core-shell material and its preparation method and application
  • A kind of polydopamine-based core-shell material and its preparation method and application
  • A kind of polydopamine-based core-shell material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] Put 50mL EG into a three-necked flask, heat to 150°C in an oil bath and react for 1h. Prepare 4mM CuCl 2 +2H 2 EG solution of O; 1g PVP (Mw=30000) and 0.5g AgNO 3 Dissolve in 10mL of EG respectively, add 200μL of CuCl dissolved in EG dropwise after reacting for 1h 2 +2H 2 O solution; after continuing to react for 15 minutes, add the prepared PVP and AgNO respectively 3 solution, PVP and AgNO 3 The mass ratio is 2:1; after the final reaction for 1 h, cool down to room temperature and wash with acetone. The obtained precipitate is AgNWs. The diameter of the prepared AgNWs is about 100 nm and the length is about 10 μm. The obtained precipitate is dispersed in 10 mL of ethanol ready in solution.

[0047] Sonicate the above-mentioned ethanol solution of AgNWs until it is evenly mixed; prepare a 10mM Tris-HCl buffer solution with pH=8.5; take 100mL of the buffer solution to prepare 2g·L –1 Then take the above AgNWs solution and disperse it in the DA solution, wherein t...

Embodiment 2

[0050] Put 50mL EG into a three-necked flask, heat to 150°C in an oil bath and react for 1h. Prepare 4mM CuCl 2 +2H 2 EG solution of O; 1g PVP (Mw=30000) and 0.5g AgNO 3 Dissolve in 10mL of EG respectively, add 200μL of CuCl dissolved in EG dropwise after reacting for 1h 2 +2H 2 O solution; after continuing to react for 15 minutes, add the prepared PVP and AgNO respectively 3 solution, PVP and AgNO 3 The mass ratio is 2:1; after the final reaction for 1h, it is cooled to room temperature and washed with acetone. The obtained precipitate is AgNWs, and the morphology is as follows figure 1 As shown, the diameter of the prepared AgNWs is about 100 nm, and the length is about 10 μm, and the obtained precipitate is dispersed in 10 mL ethanol solution for later use.

[0051] Sonicate the above-mentioned ethanol solution of AgNWs until it is evenly mixed; prepare a 10mM Tris-HCl buffer solution with pH=8.5; take 100mL of the buffer solution to prepare 2g·L –1 DA solution, and ...

Embodiment 3

[0054] Put 50mL EG into a three-necked flask, heat to 150°C in an oil bath and react for 1h. Prepare 4mM CuCl 2 +2H 2 EG solution of O; 1g PVP (Mw=30000) and 0.5g AgNO 3 Dissolve in 10mL of EG respectively, add 200μL of CuCl dissolved in EG dropwise after reacting for 1h 2 +2H 2 O solution; after continuing to react for 15 minutes, add the prepared PVP and AgNO respectively 3 solution, PVP and AgNO 3 The mass ratio is 2:1; after the final reaction for 1 h, cool down to room temperature and wash with acetone. The obtained precipitate is AgNWs. The diameter of the prepared AgNWs is about 100 nm and the length is about 10 μm. The obtained precipitate is dispersed in 10 mL of ethanol ready in solution.

[0055] Sonicate the above-mentioned ethanol solution of AgNWs until it is evenly mixed; prepare a 10mM Tris-HCl buffer solution with pH=8.5; take 100mL of the buffer solution to prepare 2g·L –1 Then take the above AgNWs solution and disperse it in the DA solution, wherein t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a core-shell material based on polydopamine, its preparation method and application. Using AgNWs and dopamine as raw materials, the AgNWs@PDA core-shell material with AgNWs as the core and polydopamine as the shell was prepared by in-situ polymerization. The AgNWs@PDA core-shell material was put into the silver ammonia solution for reaction, so that the reaction The final AgNPs are attached to the surface of the AgNWs@PDA core-shell material, thus forming the AgNWs@PDA@AgNPs core-shell material. The AgNWs obtained by this method not only have good electrical conductivity, bending properties, and huge specific surface area, which can be used to prepare flexible conductive electrodes, but also have high SERS activity and can be used as SERS substrates. The preparation method of the invention is simple, the preparation process is safe, the energy consumption is low, and the operability is strong.

Description

technical field [0001] The invention relates to a preparation method of a silver nanowire / polydopamine / silver nanoparticle (AgNWs@PDA@AgNPs) core-shell material and its application to a highly sensitive surface-enhanced Raman substrate, belonging to the technical field of nanomaterial synthesis. Background technique [0002] Surface-enhanced Raman scattering (SERS) can obtain a signal that is stronger than ordinary Raman scattering by adsorbing molecules on the surface of rough metal or metal sol particles, and its intensity can increase by several orders of magnitude. This advantage makes the surface enhanced Raman scattering has been widely used in physics, chemistry, biology, medicine, environment and other fields. [0003] Under visible light excitation, nanomaterials based on noble metals gold, silver, and copper have high enhancement effects, and are currently commonly used SERS substrate materials, among which silver has the strongest enhancement ability. As a one-di...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): G01N21/65
CPCG01N21/658
Inventor 张志良司甜甜周国伟韩可慧
Owner QILU UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products